Effects of calcium chloride and sodium hexametaphosphate on certain chemical and physical properties of soymilk

Soymilks with sodium hexametaphosphate (SHMP) (0% to 1.2%) and calcium chloride (12.50, 18.75, and 25.00 mM Ca),were analyzed for total Ca, Ca ion concentration, pH, kinematic viscosity, particle diameter, and sediment after pasteurization. Higher added Ca led to significant (P <= 0.05) increases in Ca ion concentration and significant (P <= 0.05) decreases in pH. At certain levels of SHMP, higher concentrations of added Ca significantly increased (P <= 0.05) kinematic viscosity, particle diameter, and sediment. Increasing SHMP concentration reduced Ca ion concentration, particle diameter, and dry sediment content, but reduced kinematic viscosity of samples (P <= 0.05). Adding SHMP up to 0.7% influenced pH of soymilk in different ways, depending on the level of Ca addition. When the pH of Ca-fortified soymilk was adjusted to a higher level, ionic Ca decreased as pH increased. Ihere was a negative linear relationship between the logarithm of ionic Ca concentration and the adjusted pH of the soymilk. Ionic Ca appeared to be a good indicator of thermally induced sediment formation, with little sediment being produced if ionic Ca was maintained below 0.4 mM.

Feasibility of using dialysis for determining calcium ion concentration and pH in calcium-fortified soymilk at high temperature

Dialysis was performed to examine some of the properties of the soluble phase of calcium (Ca) fortified soymilk at high temperatures. Dialysates were obtained while heating soymilk at temperatures of 80 and 100 °C for 1 h and 121 °C for 15 min. It was found that the pH, total Ca, and ionic Ca of dialysates obtained at high temperature were all lower than in their corresponding nonheated Ca-fortified soymilk. Increasing temperature from 80 to 100 °C hardly affected Ca ion concentration ([Ca2+]) of dialysate obtained from Ca chloride-fortified soymilk, but it increased [Ca2+] in dialysates of Ca gluconate-fortified soymilk and Ca lactate-fortified soymilk fortified with 5 to 6 mM Ca. Dialysates obtained at 100 °C had lower pH than dialysate prepared at 80 °C. Higher Ca additions to soymilk caused a significant (P≤ 0.05) reduction in pH and an increase in [Ca2+] of these dialysates. When soymilk was dialyzed at 121 °C, pH, total Ca, and ionic Ca were further reduced. Freezing point depression (FPD) of dialysates increased as temperature increased but were lower than corresponding soymilk samples. This approach provides a means of estimating pH and ionic Ca in soymilks at high temperatures, in order to better understand their combined role on soymilk coagulation.

Viscoelastic properties of high pressure and heat induced tofu gels

Tofu gels were rheologically examined to determine their storage or elastic (G′) and loss or viscous (G″) moduli as a function of frequency within their linear viscoelastic limits. The tofu gels were made using either glucono-δ-lactone (GDL) or calcium sulphate (CaSO4·2H2O), followed by either heat treatment (heated soymilk at 97 °C prior to coagulation and subsequently held at 70 °C for 60 min, HT) or high pressure treatment (400 MPa at 20 °C for 10 min, HP). The overall moduli values of the GDL gels and CaSO4·2H2O gels of both physical treatments were similar, each gave frequency profiles expected for weak viscoelastic materials. However, although both temperature and high pressure treatments could be used to produce tofu gels, the final products were not the same. Pressure formed gels, despite having a higher overall “consistency” (increasing values of their moduli), had a proportionately higher contribution from the loss modulus (increased tan δ). Differences could also be observed using confocal scanning laser microscopy. While such treatment may give rise to differing systems/structures, with new or modified organoleptic properties, the more “open” structures obtained by pressure treatment may well cause processing difficulties if subsequent reworking or moulding is required.

Viscoelastic properties of high pressure and heat induced tofu gels

Tofu gels were rheologically examined to determine their storage or elastic (G') and loss or viscous (G '') moduli as a function of frequency within their linear viscoelastic limits. The tofu gels were made using either glucono-delta-lactone (GDL) or calcium sulphate (CaSO4 center dot 2H(2)O), followed by either heat treatment (heated soymilk at >= 97 degrees C prior to coagulation and subsequently held at 70 degrees C for 60 min, HT) or high pressure treatment (400 MPa at 20 degrees C for 10 min, HP). The overall moduli values of the GDL gels and CaSO4 center dot 2H(2)O gels of both physical treatments were similar, each gave frequency profiles expected for weak viscoelastic materials. However, although both temperature and high pressure treatments could be used to produce tofu gels, the final products were not the same. Pressure formed gels, despite having a higher overall "consistency" (increasing values of their moduli), had a proportionately higher contribution from the loss modulus (increased tan delta). Differences could also be observed using confocal scanning laser microscopy. While such treatment may give rise to differing systems/structures, with new or modified organoleptic properties, the more "open" structures obtained by pressure treatment may well cause processing difficulties if subsequent reworking or moulding is required. (c) 2007 Elsevier Ltd. All rights reserved.