Synergetic effects of the Cu/Pt{110} surface alloy: enhanced reactivity of water and carbon monoxide

We have used synchrotron-based high-resolution X-ray photoelectron spectroscopy in combination with ab initio density functional theory calculations to investigate the characteristics of water and CO adsorption on the bimetallic Cu/Pt{110}-(2 x 1) surface at a Cu coverage near 0.5 ML. Cu fills the troughs of the reconstructed clean surface forming nanowires, which are stable up to 830 K. Their presence dramatically influences the adsorption of water and CO. Water adsorption changes from intact to partially dissociated while the desorption temperature of CO on this surface increases by up to 27 K with respect to the clean Pt{110} surface. Ab initio calculations and experimental valence band spectra reveal that the Cu 3d-band is narrowed and shifted upward with respect to bulk Cu surfaces. This and electron donation to surface Pt atoms cause the increase in the bond strength between CO and the Pt surface atoms. The pathway for water dissociation occurs via Cu surface atoms. The heat of adsorption of water bonding to Cu surface atoms was calculated to be 0.82 eV, which is significantly higher than on the clean Pt{110} surface; the activation energy for partial dissociation is 0.53 eV (not corrected for zero point energy).

Ultra-thin porous silica coated silver-platinum alloy nano-particle as a new catalyst precursor

Templated sol-gel encapsulation of surfactant-stabilised micelles containing metal precursor(s) with ultra-thin porous silica coating allows solvent extraction of organic based stabiliser from the composites in colloidal state hence a new method of preparing supported alloy catalysts using the inorganic silica-stabilised nano-sized, homogenously mixed, silver - platinum (Ag-Pt) colloidal particles is reported.

Hollow structures with bilayer graphene walls

The formation of three-dimensional shell-like structures with bilayer graphene walls is described. The structures are produced by the passage of an electric current through graphite in an arc-discharge apparatus. High resolution transmission electron microscopy is used to characterize the carbon, and provides evidence that the structures are three-dimensional rather than flat. A striking feature of the material is that it contains bilayer nanotubes seamlessly joined to larger shell-like regions. The possible growth mechanism of the carbon is discussed, and potential applications considered.

Hollow capsules formed in a single stage via interfacial hydrogen-bonded complexation of methylcellulose with poly(acrylic acid) and tannic acid

Hollow capsules can be prepared in a single stage by the interfacial complexation of methylcellulose (MC) with poly(acrylic acid) (PAA) or tannic acid (TA) via hydrogen bonding in aqueous solutions. The formation of capsules is observed when viscous solution of methylcellulose is added drop-wise to diluted solutions of polyacids under acidic conditions. The optimal parameters such as polymer concentration and solution pH for the formation of these capsules were established in this work. It was found that tannic acid forms capsules in a broader range of concentrations and pHs compared to poly(acrylic acid). The TA/MC capsules exhibited better stability compared to PAA/MC in response to increase in pH: the dissolution of TA/MC capsules observed at pH > 9.5; whereas PAA/MC capsules dissolved at pH > 3.8. The interfacial complexation can be considered as a potential single stage alternative to the formation of capsules using multistage layer-by-layer deposition method.