Photopolymerization of Pluronic F127 diacrylate: a colloid-templated polymerization

Pluronic F127 diacrylate (F127DA) is a bifunctional acrylate and as such it should in principle produce macroscopically cross-linked materials; however, its photopolymerization in water does not lead to 3D-extended hydrogels. The main species present after photopolymerization appear to be cross-linked micelles, which indicates that the micellar morphology of F127DA has a template effect on the polymerization. The structural analogy causes the physical state of precursor and polymerized materials to be very similar for a wide range of concentrations (5–25% wt) and temperatures (10–37 °C). Also the long-range morphology of F127DA appears to have a template effect: samples photopolymerized in a micellar gel state and redispersed at high concentration (25% wt) show a long-range organization that depended on the concentration and therefore on the order of the precursor.

A transmission electron microscopy study of polymer-stabilised liquid crystal structure

A method has been established for observing the internal structure of the network component of polymer-stabilised liquid crystals. In situ photopolymerisation of a mesogenic diacrylate monomer using ultraviolet light leads to a sparse network (∼1 wt%) within a nematic host. Following polymerisation, the host was removed through dissolution in heptane, revealing the network. In order to observe a cross-section through the network, it was embedded in a resin and then sectioned using an ultramicrotome. However, imaging of the network was not possible due to poor contrast. To improve this, several reagents were used for network staining, but only one was successful: bromine. The use of a Melinex-resin composite for sectioning was also found to be advantageous. Imaging of the network using transmission electron microscopy revealed solid “droplets” of width 0.07–0.20 μm, possessing an open, yet homogeneous structure, with no evidence for any large-scale internal structures.