Electrochemical characterisation and anodic stripping voltammetry at mesoporous platinum rotating disc electrodes

Using the technique of liquid crystal templating a rotating disc electrode (RDE) was modified with a high surface area mesoporous platinum film. The surface area of the electrode was characterised by acid voltammetry, and found to be very high (ca. 86 cm(2)). Acid characterisation of the electrode produced distorted voltammograms was interpreted as being due to the extremely large surface area which produced a combination of effects such as localised pH change within the pore environment and also ohmic drop effects. Acid voltammetry in the presence of two different types of surfactant, namely Tween 20 and Triton X-100, suggested antifouling properties associated with the mesoporous deposit. Further analysis of the modified electrode using a redox couple in solution showed typical RDE behaviour although extra capacitive currents were observed due to the large surface area of the electrode. The phenomenon of underpotential deposition was exploited for the purpose of anodic stripping voltammetry and results were compared with data collected for microelectrodes. Underpotential deposition of metal ions at the mesoporous RDE was found to be similar to that at conventional platinum electrodes and mesoporous microelectrodes although the rate of surface coverage was found to be slower at a mesoporous RDE. It was found that a mesoporous RDE forms a suitable system for quantification of silver ions in solution.

Evaluation of negative photo-patternable PDMS for the encapsulation of neural electrodes

This communication examines the suitability of a photo-patternable polydimethylsiloxane (PP-PDMS) elastomer as an insulating material for implantable microelectrodes. PP-PDMS is produced by mixing a photoinitiator (2-hydroxy-2-methylpropiophenone) with the PDMS base and curing agent. Subsequent exposure to UV radiation and development of the elastomeric “photo-resist” allows for the definition of well-defined openings within the PP-PDMS film. The dielectric constants of PP-PDMS and PDMS are similar (ε ≈ 2.6, f <;1MHz). Gold film microelectrodes patterned on glass or a PDMS substrate are encapsulated with PP-PDMS, while recording sites as small as 104 μm2 can be obtained in the PP-PDMS layer. The cytotoxicity of the PP-PDMS was preliminary tested in vitro by culturing 3T3 fibroblasts in PP-PDMS extracts. No adverse effects were observed in cultures exposed to PP-PDMS films initially leached in isopropanol solvent for 48h.