Efficiency and purity control in the preparation of pure and/or aluminum-doped barium ferrites by hydrothermal methods using ferrous ions as reactants

The synthesis of hexagonal barium ferrite (BaFe12O19) was studied under hydrothermal conditions by a method in which a significant amount of ferrous chloride was introduced along side ferric chloride among the starting materials. Though all of the Fe2+ ions in the starting material were converted to Fe3+ ions in the final product, Fe2+ was confirmed to participate differently from the Fe3+ used in the conventional method in the mechanism of forming barium ferrite. Indeed the efficiency of the synthesis and the quality of the product and the lack of impurities such as Fe2O3 and BaFe2O4 were improved when Fe2+ was included. However, the amount of ferrous ions that could be included to obtain the desired product was limited with an optimum ratio of 2:8 for FeCl2/FeCl3 when only 2h of reaction time were needed. It was also found that the role of trivalent Fe3+ could be successfully replaced by Al3+. Up to 50% of their on could be replaced by Al3+ in the reactants to produce Al- doped products. It was also found that the ratio of Fe2+/M3+ could be increased in the presence of Al3+ to produce high quality barium ferrite.

Preparation and magnetic properties of barium ferrites substituted with manganese, cobalt, and tin

Barium ferrites substituted by Mn–Sn, Co–Sn, and Mn–Co–Sn with general formulae BaFe12−2xMnxSnxO19 (x=0.2–1.0), BaFe12−2xCoxSnxO19 (x=0.2–0.8), and BaFe12−2xCox/2Mnx/2SnxO19 (x=0.1–0.6), respectively, have been prepared by a previously reported co-precipitation method. The efficiency of the method was refined by lowering the reaction temperature and shortening the required reaction time, due to which crystallinity improved and the value of saturated magnetization increased as well. Low coercivity temperature coefficients, which are adjustable by doping, were achieved by Mn–Sn and Mn–Co–Sn doping. Synthesis efficiency and the effect of doping are discussed taking into account accumulated data concerning the synthesis and crystal structure of ferrites.

Hybrid polystyrene based electrospun fibers with spin-crossover properties

We have succeeded in the preparation of electrospun fibers of polystyrene incorporating a metallo-organic polymer of [Fe (II) (4-octadecyl-1,2,4-triazole)3(ClO4)2]n. The obtained fibers have diameters in the range 2–4 µm and show the characteristic spin-crossover transition associated with the metallo-organic polymer. The structure of both, polystyrene and the metallo-organic polymer, in the fibers was also studied.