Influence of molecular composition on the development of microstructure from sheared polyethylene melts: Molecular and lamellar templating

A combination of in situ and ex situ X-ray scattering techniques and transmission electron microscopy has been used to study the crystallization behaviour of polyethylene, following the imposition of melt shear. In the case of a branched material, the imposition of shear flow up to a rate of 30 s(-1) was found to induce no anisotropy. Although shearing the linear material only ever induced a very small degree of anisotropy in the melt, for shear rates > 0.15 s(-1), subsequent crystallization resulted in increasing anisotropy. Blends of the above two polyethylenes were produced, in which the linear material constituted the minority fraction (similar to 10%). Isothermal crystallization at temperatures where extensive crystallization of the branched material does not occur demonstrated that the behaviour of the linear component of the sheared blend mirrored that of the linear polyethylene alone. However, in addition, it was found that when crystallized in the presence of an oriented morphology, the branched polymer also formed anisotropic structures. We have termed the process templating, in which the crystallization behaviour of the bulk of the system (similar to 90% branched material) is completely altered (spherulitic to oriented lamellar) by mapping it onto a pre-existing minority structure (similar to 10% linear polymer). (c) 2006 Elsevier Ltd. All rights reserved.

On the time for fold surfaces to order during the crystallization of polyethylene from the melt and its dependence on molecular parameters

New experiments underpin the interpretation of the basic division in crystallization behaviour of polyethylene in terms of whether or not there is time for the fold surface to order before the next molecular layer is added at the growth front. For typical growth rates, in Regime 11, polyethylene lamellae form with disordered {001} fold surfaces then transform, with lamellar thickening and twisting, towards the more-ordered condition found for slower crystallization in Regime 1, in which lamellae form with and retain {201} fold surfaces. Several linear and linear-low-density polyethylenes have been used to show that, for the same polymer crystallized alone or in a blend, the growth rate at which the change in initial lamellar condition occurs is reasonably constant thereby supporting the concept of a specific time for surfaces to attain the ordered {201}) state. This specific time, in the range from milliseconds to seconds, increases with molecular length, and in linear-low-density polymer, for higher branch contents. (c) 2006 Elsevier Ltd. All rights reserved.