Ternary erbium chromium sulfides : structural relationships and magnetic properties

Single crystals of four erbium-chromium sulfides have been grown by chemical vapor transport using iodine as the transporting agent. Single-crystal X-ray diffraction reveals that in Er(3)CrS(6) octahedral sites are occupied exclusively by Cr(3+) cations, leading to one-dimensional CrS(4)(5-) chains of edge-sharing octahedra, while in Er(2)CrS(4), Er(3+), and Cr(2+) cations occupy the available octahedral sites in an ordered manner. By contrast, in Er(6)Cr(2)S(11) and Er(4)CrS(7), Er(3+) and Cr(2+) ions are disordered over the octahedral sites. In Er(2)CrS(4), Er(6)Cr(2)S(11), and Er(4)CrS(7), the network of octahedra generates an anionic framework constructed from M(2)S(5) slabs of varying thickness, linked by one-dimensional octahedral chains. This suggests that these three phases belong to a series in which the anionic framework may be described by the general formula [M(2n+1)S(4n+3)](x-), with charge balancing provided by Er(3+) cations located in sites of high-coordination number within one-dimensional channels defined by the framework. Er(4)CrS(7), Er(6)Cr(2)S(11), and Er(2)CrS(4) may thus be considered as the n = 1, 2, and infinity members of this series. While Er(4)CrS(7) is paramagnetic, successive magnetic transitions associated with ordering of the chromium and erbium sub-lattices are observed on cooling Er(3)CrS(6) (T(C)(Cr) = 30 K; T(C)(Er) = 11 K) and Er(2)CrS(4) (T(N)(Cr) = 42 K, T(N)(Er) = 10 K) whereas Er(6)Cr(2)S(11) exhibits ordering of the chromium sub-lattice only (T(N) = 11.4 K).

Co3(SO4)3(OH)2[enH2]: a newS= 3/2 Kagome-type layered sulfate with a unique connectivity

The Kagome lattice, comprising a two-dimensional array of corner-sharing equilateral triangles, is central to the exploration of magnetic frustration. In such a lattice, antiferromagnetic coupling between ions in triangular plaquettes prevents all of the exchange interactions being simultaneously satisfied and a variety of novel magnetic ground states may result at low temperature. Experimental realization of a Kagome lattice remains difficult. The jarosite family of materials of nominal composition AM3(SO4)2(OH)6 (A = monovalent cation; M= Fe3+, Cr3+), offers perhaps one of the most promising manifestations of the phenomenon of magnetic frustration in two dimensions. The magnetic properties of jarosites are however extremely sensitive to the degree of coverage of magnetic sites. Consequently, there is considerable interest in the use of soft chemical techniques for the design and synthesis of novel materials in which to explore the effects of spin, degree of site coverage and connectivity on magnetic frustration.