A surface and catalytic study of heterogenised Os-3(CO)(12) species in MCM-41 structures

Immobilised Os species prepared via chemical vapour deposition (CVD) of Os-3(CO)(12) onto MCM-41 are active and selective catalysts for the dihydroxylation of trans-stilbene in acetone and water, using N-methylmorpholine N-oxide as the oxidant. A detailed temperature programmed decomposition study of the solids enables to identify the active sites as Os-x(CO)(y) surface species. The initial loading of the MCM-41 with the trinuclear precursor, as well as the temperature of the post-synthesis oxidising treatment, are found to have a significant impact on the structure/geometry of the resulting surface species, and thus their catalytic properties. We show how it is also affected by the confined environment of the MCM-41 mesopores and especially the curvature of the 30 Angstrom diameter channels. Finally, a careful study of the catalytic properties of the materials together with a study of the reactivity of the reaction products under similar conditions enable to suggest a mechanism involving the reaction of the oxidant with the osmium carbonyl surface species to form the catalytically active Os-oxo sites, and the formation of an osmoate-type species (through adsorption of the alkene onto the Os-oxo site) which subsequently reacts with the solvent to produce the diol. (C) 2003 Elsevier B.V. All rights reserved.

The trapping and decomposition of toxic gases such as hydrogen cyanide using modified mesoporous silicates

Selected silicas were modified with the covalently bound ligand 2,6-bis(benzoxazoyl)pyridine (BBOP), equilibrated with copper(II) nitrate, then challenged with toxic vapour containing HCN (8000 mg m(-3) at 80% relative humidity). The modified SBA-15 material (Cu-BBOP-SBA-15) had an improved breakthrough time for HCN (36 min at a flow rate of 30 cm(3) min(-1)) when compared to the other siliceous materials prepared in this study, equating to a hydrogen cyanide capacity of 58 mg g(-1), which is close to a reference activated carbon adsorbent (24 min at 50 cm(3) min(-1)) that can trap 64 mg g(-1). The enhanced performance observed with Cu-BBOP-SBA-15 has been related to the greater accessibility of the functional groups, arising from the ordered nature of the interconnected porous network and large mesopores of 5.5 nm within the material modified with the Cu(II)-BBOP complex. Modified MCM-41 and MCM-48 materials (Cu-BBOP-MCM-41 and Cu-BBOP-MCM-48) were found to have lower hydrogen cyanide capacities (38 and 32 mg g(-1) respectively) than the Cu-BBOP-SBA-15 material owing to the restricted size of the pores (2.2 and <2 nm respectively). The materials with poor nano-structured ordering were found to have low hydrogen cyanide capacities, between 11 and 19 mg g(-1), most likely owing to limited accessibility of the functional groups. (C) 2004 Elsevier Inc. All rights reserved.