In situ observation of lithium hydride hydrolysis by DRIFT spectroscopy

Polycrystalline LiH was studied in situ using diffuse reflectance infrared Fourier transform (DRIFT) spectroscopy to investigate the effect water vapour has on the rate of production of the corrosion products, particularly LiOH. The reaction rate of the formation of surface LiOH was monitored by measurement of the hydroxyl (OH) band at 3676 cm(-1). The initial hydrolysis rate of LiH exposed to water vapour at 50% relative humidity was found to be almost two times faster than LiH exposed to water vapour at 2% relative humidity. The hydrolysis rate was shown to be initially very rapid followed by a much slower, almost linear rate. The change in hydrolysis rate was attributed to the formation of a coherent layer of LiOH on the LiH surface. Exposure to lower levels of water vapour appeared to result in the formation of a more coherent corrosion product, resulting in effective passivation of the surface to further attack from water. Crown Copyright (c) 2007 Published by Elsevier B.V. All rights reserved.

The trapping and decomposition of toxic gases such as hydrogen cyanide using modified mesoporous silicates

Selected silicas were modified with the covalently bound ligand 2,6-bis(benzoxazoyl)pyridine (BBOP), equilibrated with copper(II) nitrate, then challenged with toxic vapour containing HCN (8000 mg m(-3) at 80% relative humidity). The modified SBA-15 material (Cu-BBOP-SBA-15) had an improved breakthrough time for HCN (36 min at a flow rate of 30 cm(3) min(-1)) when compared to the other siliceous materials prepared in this study, equating to a hydrogen cyanide capacity of 58 mg g(-1), which is close to a reference activated carbon adsorbent (24 min at 50 cm(3) min(-1)) that can trap 64 mg g(-1). The enhanced performance observed with Cu-BBOP-SBA-15 has been related to the greater accessibility of the functional groups, arising from the ordered nature of the interconnected porous network and large mesopores of 5.5 nm within the material modified with the Cu(II)-BBOP complex. Modified MCM-41 and MCM-48 materials (Cu-BBOP-MCM-41 and Cu-BBOP-MCM-48) were found to have lower hydrogen cyanide capacities (38 and 32 mg g(-1) respectively) than the Cu-BBOP-SBA-15 material owing to the restricted size of the pores (2.2 and <2 nm respectively). The materials with poor nano-structured ordering were found to have low hydrogen cyanide capacities, between 11 and 19 mg g(-1), most likely owing to limited accessibility of the functional groups. (C) 2004 Elsevier Inc. All rights reserved.

Synthesis and characterization of packed mesoporous tungsteno-silicates: application to the catalytic dehydrogenation of 2-propanol

The synthesis of highly ordered mesoporous tungsteno-silicas in which a high percentage of tungsten is introduced into a silica framework is reported hereafter. Powder XRD and TEM have been used to characterize the materials synthesized at room temperature. The materials are shown to be homogeneous as there is no evidence for any crystalline species other than the silica framework. The pore diameter and the surface area of the materials, evaluated from the nitrogen adsorption isotherms and unit cell parameter indicate a pore diameter of about 2 nm and a surface area of 1400 m(2) g(-1) for a content of 10% tungsten. Catalyzed dehydration of 2-propanol has been investigated and the activity of the materials synthesized is significant, even for low tungsten content W-MCM-41 materials. (C) 2003 Elsevier B.V. All rights reserved.

Lithium and oxygen adsorption at the b-MnO2 (110) surface

The adsorption and co-adsorption of lithium and oxygen at the surface of rutile-like manganese dioxide(b-MnO2), which are important in the context of Li–air batteries, are investigated using density functional theory. In the absence of lithium, the most stable surface of b-MnO2, the (110), adsorbs oxygen in the form of peroxo groups bridging between two manganese cations. Conversely, in the absence of excess oxygen, lithium atoms adsorb on the (110) surface at two different sites, which are both tricoordinated to surface oxygen anions, and the adsorption always involves the transfer of one electron from the adatom to one of the five-coordinated manganese cations at the surface, creating (formally) Li+ and Mn3+ species. The co-adsorption of lithium and oxygen leads to the formation of a surface oxide, involving the dissociation of the O2 molecule, where the O adatoms saturate the coordination of surface Mn cations and also bind to the Li adatoms. This process is energetically more favourable than the formation of gas-phase lithium peroxide (Li2O2) monomers, but less favourable than the formation of Li2O2 bulk. These results suggest that the presence of b-MnO2 in the cathode of a nonaqueous Li–O2 battery lowers the energy for the initial reduction of oxygen during cell discharge.

Chemoselective and stereoselective lithium carbenoid mediated cyclopropanation of acyclic allylic alcohols

The reaction of geraniol with different lithium carbenoids generated from n-BuLi and the corresponding dihaloalkane has been evaluated. The reaction occurs in a chemo and stereoselective manner, which is consistent with a directing effect from the oxygen of the allylic moiety. Furthermore, a set of polyenes containing allylic hydroxyl or ether groups were chemoselectively and stereoselectively converted into the corresponding gemdimethylcyclopropanes in one single step in moderate to good yields mediated by a lithium carbenoid generated in situ by reaction of n-BuLi and 2,2-dibromopropane.