Using an additive to control the electrospinning of fibres of poly(epsilon-caprolactone)

Electrospinning is a route to polymer fibres with diameters considerably smaller than available from most fibre-producing techniques. We explore the use of a low molecular weight compound as an effective control additive during the electrospinning of poly(epsilon-caprolactone). This approach extends the control variables for the electrospinning of nanoscale fibres from the more usual ones such as the polymer molecular weight, solvent and concentration. We show that through the use of dual solvent systems, we can alter the impact of the additive on the electrospinning process so that finer as well as thicker fibres can be prepared under otherwise identical conditions. As well as the size of the fibres and the number of beads, the use of the additive allows us to alter the level of crystallinity as well as the level of preferred orientation of the poly(epsilon-caprolactone) crystals. This approach, involving the use of a dual solvent and a low molar mass compound, offers considerable potential for application to other polymer systems. (C) 2010 Society of Chemical Industry

Chapter 16: Electrospinning of polymer solutions

Electrospinning is a technique that involves the production of nanoscale to microscale sized polymer fibres through the application of an electric field to a droplet of polymer solution passed through a spinneret tip. This chapter considers the optimisisation of the electrospinning process and in particular the variation with solution concentration. We show the strong connection between overlapping chains and the successful spinning of fibres. We use small-angle neutron scattering to evaluate the molecular conformations in the solutions and in the fibres.

Conducting nanofibres produced by electrospinning

Electrospun fibres based on polypyrrole have been prepared. The incorporation of preformed polypyrrole into fibres electrospun from a carrier polymer can only be achieved when materials are prepared with particulates smaller than the cross-section of the fibre; even so there are some problems, with the substantial loss of material from the electrode tip. As an alternative approach, soluble polypyrroles can be prepared but these are not of sufficient viscosity to prepare electrospun fibres, once again a carrier polymer must be employed. More effective loadings are gained by the process of coating the outer surface of a pre-spun fibre; in this way electrospun fibres coated with polypyrrole can be prepared. This approach has been adapted to produce silver coated polymer fibres by the use of copolymers of styrene and 3-vinyl benzaldehyde.

The potential of electrospinning in rapid manufacturing processes

We review the process of electrospinning and how this new technique for generating a rich morphology of nano and micro scale fibres sits alongside established procedures for rapid manufacturing. We introduce the key elements of electrospinning and how these influence the nature and distribution of the fibres produced. We describe the range of polymers available for electrospinning and the limitations to the use of these materials. Using this base we review the potential approaches to using electrospinning as part of a broader rapid manufacturing system and the possible applications for such a hybrid system.

Development of orientation during electrospinning of fibres of poly(ε-caprolactone)

We explore the influence of a rotating collector on the internal structure of poly(ε-caprolactone) fibres electrospun from a solution in dichloroethane. We find that above a threshold collector speed, the mean fibre diameter reduces as the speed increases and the fibres are further extended. Small-angle and wide-angle X-ray scattering techniques show a preferred orientation of the lamellar crystals normal to the fibre axis which increases with collector speed to a maximum and then reduces. We have separated out the processes of fibre alignment on the collector and the orientation of crystals within the fibres. There are several stages to this behaviour which correspond to the situations (a) where the collector speed is slower than the fibre spinning rate, (b) the fibre is mechanically extended by the rotating collector and (c) where the deformation leads to fibre fracture. The mechanical deformation leads to a development of preferred orientation with extension which is similar to the prediction of the pseudo-affine deformation model and suggests that the deformation takes place during the spinning process after the crystals have formed.