The influence of hydration on the tensile and compressive properties of avian keratinous tissues

Despite recent research exploring the elastic properties of avian keratins, data on failure properties are less common in the literature. In this paper we present data on the failure properties and moduli of both avian feather and claw keratin in tension and the modulus of claw keratin in compression. Increased water content acts to decrease stiffness and strength but to increase strain at failure. The modulus of claw did not differ significantly when tested under tension and compression.

Effect of temperature and strain rate on the compressive behaviour of supramolecular polyurethane

Supramolecular polyurethanes (SPUs) possess thermoresponsive and thermoreversible properties, and those characteristics are highly desirable in both bulk commodity and value-added applications such as adhesives, shape-memory materials, healable coatings and lightweight, impact-resistant structures (e.g. protection for mobile electronics). A better understanding of the mechanical properties, especially the rate and temperature sensitivity, of these materials are required to assess their suitability for different applications. In this paper, a newly developed SPU with tuneable thermal properties was studied, and the response of this SPU to compressive loading over strain rates from 10−3 to 104 s−1 was presented. Furthermore, the effect of temperature on the mechanical response was also demonstrated. The sample was tested using an Instron mechanical testing machine for quasi-static loading, a home-made hydraulic system for moderate rates and a traditional split Hopkinson pressure bars (SHPBs) for high strain rates. Results showed that the compression stress-strain behaviour was affected significantly by the thermoresponsive nature of SPU, but that, as expected for polymeric materials, the general trends of the temperature and the rate dependence mirror each other. However, this behaviour is more complicated than observed for many other polymeric materials, as a result of the richer range of transitions that influence the behaviour over the range of temperatures and strain rates tested.

Hardening of concrete with a planned delayed ettringite formation

Delayed ettringite formation (DEF) in cementitious materials is widely considered as a harmful chemical reaction that causes extensive damages in hardened concrete. However, preventative measures and possible improvements in general are not extensively studied and require further attention. In this study was presented an investigation into a type of controlled DEF in places of finely dispersed crystallisation nuclei and provide evidence that the process may improve compressive strength of cementitious materials. The Alkali-Silica Reaction (ASR) in hydrated concrete was achieved with the addition of fly ash and was further accelerated with the Duggan’s test. Achieved strengths and monitoring of microstructure development conducted with electronic microscopy revealed that growth of ettringite crystals in the nuclei led to harmless internal compressive stresses, expansion of hydrated concrete and overall strengthening of the concrete matrix.

Investigation of the fracture mode for hard and soft wheat endosperm using the loading-unloading bending test

Investigation of the fracture mode for hard and soft wheat endosperm was aimed at gaining a better understanding of the fragmentation process. Fracture mechanical characterization was based on the three-point bending test which enables stable crack propagation to take place in small rectangular pieces of wheat endosperm. The crack length can be measured in situ by using an optical microscope with light illumination from the side of the specimen or from the back of the specimen. Two new techniques were developed and used to estimate the fracture toughness of wheat endosperm, a geometric approach and a compliance method. The geometric approach gave average fracture toughness values of 53.10 and 27.0 J m(-2) for hard and soft endosperm, respectively. Fracture toughness estimated using the compliance method gave values of 49.9 and 29.7 J m(-2) for hard and soft endosperm, respectively. Compressive properties of the endosperm in three mutually perpendicular axes revealed that the hard and soft endosperms are isotropic composites. Scanning electron microscopy (SEM) observation of the fracture surfaces and the energy-time curves of loading-unloading cycles revealed that there was a plastic flow during crack propagation for both the hard and soft endosperms, and confirmed that the fracture mode is significantly related to the adhesion level between starch granules and the protein matrix.

Novel material combinations for enhanced infrared filter performance

The introduction of non-toxic fluride compounds as direct replacements for Thorium Fluoride (ThF4) has renewed interest in the use of low index fluoride compounds in high performance infrared filters. This paper reports the results of an investigation into the effects of combining these low index materials, particularly Barium Fluoride (BaF2), with the high index material Lead Telluride (PbTe) in bandpass and edge filters. Infrared filter designs using conventional and the new material ombination are compared, and infrared filters using these material combinations have been manufactured and have been shown to suffer problems with residual stress. A possible solution to this problem utilising Zinc Sulphide (ZnS) layers with compensating compressive stress is discussed.

Ex vivo expansion of limbal stem cells is affected by substrate properties

Limbal epithelial stem cells play a key role in the maintenance and regulation of the corneal surface. Damage or destruction of these cells results in vascularisation and corneal opacity. Subsequent limbal stem cell transplantation requires an ex vivo expansion step and preserving cells in an undifferentiated state remains vital. In this report we seek to control the phenotype of limbal epithelial stem cells by the novel application of compressed collagen substrates. We have characterised the mechanical and surface properties of conventional collagen gels using shear rheology and scanning electron microscopy. In doing so, we provide evidence to show that compressive load can improve the stiffness of collagen substrates. In addition Western blotting and immunohistochemistry display increased cytokeratin 3 (CK3) protein expression relating to limbal epithelial cell differentiation on stiff collagen substrates. Such gels with an elastic modulus of 2900 Pa supported a significantly higher number of cells than less stiff collagen gels (3 Pa). These findings have substantial influence in the development of ocular surface constructs or experimental models particularly in the fields of stem cell research, tissue engineering and regenerative medicine.

Effect of shear rupture on aggregate scale formation in sea ice

A discrete element model is used to study shear rupture of sea ice under convergent wind stresses. The model includes compressive, tensile, and shear rupture of viscous elastic joints connecting floes that move under the action of the wind stresses. The adopted shear rupture is governed by Coulomb’s criterion. The ice pack is a 400 km long square domain consisting of 4 km size floes. In the standard case with tensile strength 10 times smaller than the compressive strength, under uniaxial compression the failure regime is mainly shear rupture with the most probable scenario corresponding to that with the minimum failure work. The orientation of cracks delineating formed aggregates is bimodal with the peaks around the angles given by the wing crack theory determining diamond-shaped blocks. The ice block (floe aggregate) size decreases as the wind stress gradient increases since the elastic strain energy grows faster leading to a higher speed of crack propagation. As the tensile strength grows, shear rupture becomes harder to attain and compressive failure becomes equally important leading to elongation of blocks perpendicular to the compression direction and the blocks grow larger. In the standard case, as the wind stress confinement ratio increases the failure mode changes at a confinement ratio within 0.2–0.4, which corresponds to the analytical critical confinement ratio of 0.32. Below this value, the cracks are bimodal delineating diamond shape aggregates, while above this value failure becomes isotropic and is determined by small-scale stress anomalies due to irregularities in floe shape.

Potential reduction of concrete deterioration through controlled DEF in hydrated concrete

Delayed ettringite formation (DEF) is a chemical reaction with proven damaging effects on hydrated concrete. Ettringite crystals can cause cracks and their widening due to pressure on cracked walls caused by the positive volume difference in the reaction. Concrete may show improvements in strength at early ages but further growth of cracks causes widening and spreading through the concrete structure. In this study, finely dispersed crystallization nuclei achieved by adding air-entraining agent (AEA) and short vibration of specimens is presented as the main prerequisite for reducing DEF-induced deterioration of hydrated concrete. The study presents the method and mechanism for obtaining the required nucleation. Controlling long-term DEF by providing AEA-induced crystallisation nuclei, prevented excessive and rapid initial strength improvements, and resulted in a slight increase of compressive strength of fine grained concrete with only marginally lower density.

Modelling the reorientation of sea-ice faults as the wind changes direction

A discrete-element model of sea ice is used to study how a 90° change in wind direction alters the pattern of faults generated through mechanical failure of the ice. The sea-ice domain is 400km in size and consists of polygonal floes obtained through a Voronoi tessellation. Initially the floes are frozen together through viscous–elastic joints that can break under sufficient compressive, tensile and shear deformation. A constant wind-stress gradient is applied until the initially frozen ice pack is broken into roughly diamond-shaped aggregates, with crack angles determined by wing-crack formation. Then partial refreezing of the cracks delineating the aggregates is modelled through reduction of their length by a particular fraction, the ice pack deformation is neglected and the wind stress is rotated by 90°. New cracks form, delineating aggregates with a different orientation. Our results show the new crack orientation depends on the refrozen fraction of the initial faults: as this fraction increases, the new cracks gradually rotate to the new wind direction, reaching 90° for fully refrozen faults. Such reorientation is determined by a competition between new cracks forming at a preferential angle determined by the wing-crack theory and at old cracks oriented at a less favourable angle but having higher stresses due to shorter contacts across the joints

Continuum sea ice rheology determined from subcontinuum mechanics

[1] A method is presented to calculate the continuum-scale sea ice stress as an imposed, continuum-scale strain-rate is varied. The continuum-scale stress is calculated as the area-average of the stresses within the floes and leads in a region (the continuum element). The continuum-scale stress depends upon: the imposed strain rate; the subcontinuum scale, material rheology of sea ice; the chosen configuration of sea ice floes and leads; and a prescribed rule for determining the motion of the floes in response to the continuum-scale strain-rate. We calculated plastic yield curves and flow rules associated with subcontinuum scale, material sea ice rheologies with elliptic, linear and modified Coulombic elliptic plastic yield curves, and with square, diamond and irregular, convex polygon-shaped floes. For the case of a tiling of square floes, only for particular orientations of the leads have the principal axes of strain rate and calculated continuum-scale sea ice stress aligned, and these have been investigated analytically. The ensemble average of calculated sea ice stress for square floes with uniform orientation with respect to the principal axes of strain rate yielded alignment of average stress and strain-rate principal axes and an isotropic, continuum-scale sea ice rheology. We present a lemon-shaped yield curve with normal flow rule, derived from ensemble averages of sea ice stress, suitable for direct inclusion into the current generation of sea ice models. This continuum-scale sea ice rheology directly relates the size (strength) of the continuum-scale yield curve to the material compressive strength.

Modelling signatures of pulsed magnetopause reconnection in cusp ion dispersion signatures seen at middle altitudes

It is shown that the open magnetosphere model can reproduce both the down-going and the up-going magnetosheath ions seen in the cusp and mantle regions by the Polar satellite at middle altitudes. ?he pass studied shows a series of discontinuities in the ion dispersion, most of which are shown to arise from pulses of magnetopause reconnection rate. A total of 9 pulses are detected in an interval estimated to be about 30 min long, giving a mean repetition period of about 3 min: they vary in length between 0.5 min and 3.5 min and are separated by periods of much slower reconnection of duration 1-3 min. One step is not as predicted for reconnection rate pulses but is explained in terms of compressive motions caused by a pulse of solar wind dynamic pressure. The reconnection site is found to be 16 +/- 3 R-E from the ionosphere along the separatrix field line, placing it at low latitudes on the dayside magnetopause.

Electronic structure of Pd multi-layers on Re(0001): the role of charge transfer

Understanding the origin of the properties of metal-supported metal thin films is important for the rational design of bimetallic catalysts and other applications, but it is generally difficult to separate effects related to strain from those arising from interface interactions. Here we use density functional (DFT) theory to examine the structure and electronic behavior of few-layer palladium films on the rhenium (0001) surface, where there is negligible interfacial strain and therefore other effects can be isolated. Our DFT calculations predict stacking sequences and interlayer separations in excellent agreement with quantitative low-energy electron diffraction experiments. By theoretically simulating the Pd core-level X-ray photoemission spectra (XPS) of the films, we are able to interpret and assign the basic features of both low-resolution and high-resolution XPS measurements. The core levels at the interface shift to more negative energies, rigidly following the shifts in the same direction of the valence d-band center. We demonstrate that the valence band shift at the interface is caused by charge transfer from Re to Pd, which occurs mainly to valence states of hybridized s-p character rather than to the Pd d-band. Since the d-band filling is roughly constant, there is a correlation between the d-band center shift and its bandwidth. The resulting effect of this charge transfer on the valence d-band is thus analogous to the application of a lateral compressive strain on the adlayers. Our analysis suggests that charge transfer should be considered when describing the origin of core and valence band shifts in other metal / metal adlayer systems.