The effect of annealing on the local structure of glassy polycarbonate

Annealing of polycarbonate glasses at temperatures belowTg leads to an increase in yield stress and a drop in the impact strength. Although such behaviour may be related to the corresponding reduction in free volume upon annealing, variations in the wide-angle X-ray scattering curves indicate some modification to the local structure. The area of an intrachain peak at s ∼ 0.7 Å−1 is monitored with respect to annealing temperature and time. It is proposed that the variations may be described by an increasing level of interlocking or (nesting) between neighbouring chain segments, a process which is a natural consequence of the molecular shape of polycarbonate.

Low-temperature partial dissociation of water on Cu(110)

The low-temperature reactivity of water (D2O) adsorbed on clean and oxygen pre-covered Cu(1 1 0) was studied using high resolution X-ray photoelectron spectroscopy (HRXPS) and low energy electron diffraction (LEED). On the clean surface partial dissociation to hydroxyl was observed already at 95 K. Upon annealing to 220 K hydrogen bonded water-hydroxyl chains are formed. Upon further annealing water desorbs leaving behind a layer of hydroxyl, most of which desorbs recombinatively eventually. With pre-adsorbed oxygen water reacts to hydroxyl lifting the added-row reconstruction even below 225 K. Upon annealing this adsorbate layer passes through essentially the same stages as without pre-adsorbed oxygen.