Hardening of concrete with a planned delayed ettringite formation

Delayed ettringite formation (DEF) in cementitious materials is widely considered as a harmful chemical reaction that causes extensive damages in hardened concrete. However, preventative measures and possible improvements in general are not extensively studied and require further attention. In this study was presented an investigation into a type of controlled DEF in places of finely dispersed crystallisation nuclei and provide evidence that the process may improve compressive strength of cementitious materials. The Alkali-Silica Reaction (ASR) in hydrated concrete was achieved with the addition of fly ash and was further accelerated with the Duggan’s test. Achieved strengths and monitoring of microstructure development conducted with electronic microscopy revealed that growth of ettringite crystals in the nuclei led to harmless internal compressive stresses, expansion of hydrated concrete and overall strengthening of the concrete matrix.

The composition and crystallinity of the near-surface regions of weathered alkali feldspars

Our ability to identify thin non-stoichiometric and amorphous layers beneath mineral surfaces has been tested by undertaking X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM) work on alkali feldspars from pH 1 dissolution experiments. The outcomes of this work were used to help interpret XPS and TEM results from alkali feldspars weathered for <10,000 years in soils overlying the Shap Granite (north-west England). The chemistry of effluent solutions indicates that silica-rich layers a few nanometers in thickness formed during the pH I experiments. These layers can be successfully identified by XPS and have lower Al/Si, Na/Si, K/Si and Ca/Si values than the outermost similar to 9 nm of unweathered controls. Development of Al-Si non-stoichiometry is coupled with loss of crystal structure to produce amorphous layers that are identifiable by TEM where >similar to 2.5 nm thick, whereas the crystallinity of albite is retained despite leaching of Na to depths of tens to hundreds on nanometers. Integration of XPS data over the outermost 6-9 nm of naturally weathered Shap feldspars shows that they have stoichiometric Al/Si and K/Si ratios, which is consistent with findings of previous TEM work on the same material that they lack amorphous layers. There is some XPS evidence for loss of K from the outermost couple of nanometers of Shap orthoclase, and the possibility of leaching of Na from albite to greater depths cannot be excluded using the XPS or TEM results. This study demonstrates that the leached layer model, as formulated from laboratory experiments, is inapplicable to the weathering of alkali feldspars within acidic soils, which is an essentially stoichiometric reaction. (C) 2008 Elsevier Ltd. All rights reserved.

Bending, twisting, and breaking CuCN chains to produce framework materials: the reactions of CuCN with alkali-metal halides

The reactions of the low-temperature polymorph of copper(I) cyanide (LT-CuCN) with concentrated aqueous alkali-metal halide solutions have been investigated. At room temperature, KX (X = Br and I) and CsX (X = Cl, Br, and I) produce the addition products K[Cu-2(CN)(2)Br](H2O)-H-. (I), K-3[Cu-6(CN)(6)I-3](.)2H(2)O (II), Cs[Cu-3(CN)(3)Cl] (III), Cs[Cu-3(CN)(3)Br] (IV), and Cs-2[Cu-4(CN)(4)I-2](H2O)-H-. (V), with 3-D frameworks in which the -(CuCN)- chains present in CuCN persist. No reaction occurs, however, with NaX (X = Cl, Br, I) or KCl. The addition compounds, I-V, reconvert to CuCN when washed. Both low- and high-temperature polymorphs of CuCN (LT- and HT-CuCN) are produced, except in the case of Cs[Cu-3(CN)(3)Cl] (III), which converts only to LT-CuCN. Heating similar AX-CuCN reaction mixtures under hydrothermal conditions at 453 K for 1 day produces single crystals of I-V suitable for structure determination. Under these more forcing conditions, reactions also occur with NaX (X = Cl, Br, I) and KCl. NaBr and KCl cause some conversion of LT-CuCN into HT-CuCN, while NaCl and NaI, respectively, react to form the mixed-valence Cu(I)/Cu(II) compounds [Cu-II(OH2)(4)][Cu-4(I)(CN)(6)], a known phase, and [Cu-II(OH2)(4)][Cu-4(I)(CN)(4)I-2] (VI), a 3-D framework, which contains infinite -(CuCN)- chains. After 3 days of heating under hydrothermal conditions, the reaction between KI and CuCN produces [Cu-II(OH2)(4)][Cu-2(I)(CN)I-2](2) (VII), in which the CuCN chains are broken into single Cu-CN-Cu units, which in turn are linked into chains via iodine atoms and then into layers via long Cu-C and Cu-Cu interactions.