Advances in cycloaddition polymerizations

Cycloaddition reactions have been employed in polymer synthesis since the mid-nineteen sixties. This critical review will highlight recent notable advances in this field. For example, [2 + 2] cycloaddition reactions have been utilized in numerous polymerizations to enable the construction of strained polymer systems such as poly(2-azetidinone)s that can, in turn, afford polyfunctional beta-amino acid derived polymers. Polymers have also been synthesized successfully via (3 + 2) cycloaddition methods utilizing both thermal and high-pressure conditions. 'Click chemistry'-a process involving the reaction of azides with olefins, has also been adopted to generate linear and hyperbranched polymer architectures in a very efficient manner. [4 + 2] Cycloadditions have also been utilized under thermal and high-pressure conditions to produce rigid polymers such as polyimides and polyphenylenes. These cycloaddition polymerization methods afford polymers with potential for use in high performance polymers applications such as high temperature resistant coatings and polymeric organic light emitting diodes.

The trapping and decomposition of toxic gases such as hydrogen cyanide using modified mesoporous silicates

Selected silicas were modified with the covalently bound ligand 2,6-bis(benzoxazoyl)pyridine (BBOP), equilibrated with copper(II) nitrate, then challenged with toxic vapour containing HCN (8000 mg m(-3) at 80% relative humidity). The modified SBA-15 material (Cu-BBOP-SBA-15) had an improved breakthrough time for HCN (36 min at a flow rate of 30 cm(3) min(-1)) when compared to the other siliceous materials prepared in this study, equating to a hydrogen cyanide capacity of 58 mg g(-1), which is close to a reference activated carbon adsorbent (24 min at 50 cm(3) min(-1)) that can trap 64 mg g(-1). The enhanced performance observed with Cu-BBOP-SBA-15 has been related to the greater accessibility of the functional groups, arising from the ordered nature of the interconnected porous network and large mesopores of 5.5 nm within the material modified with the Cu(II)-BBOP complex. Modified MCM-41 and MCM-48 materials (Cu-BBOP-MCM-41 and Cu-BBOP-MCM-48) were found to have lower hydrogen cyanide capacities (38 and 32 mg g(-1) respectively) than the Cu-BBOP-SBA-15 material owing to the restricted size of the pores (2.2 and <2 nm respectively). The materials with poor nano-structured ordering were found to have low hydrogen cyanide capacities, between 11 and 19 mg g(-1), most likely owing to limited accessibility of the functional groups. (C) 2004 Elsevier Inc. All rights reserved.

Novel solid networks containing Sn-H as a greener replacement for soluble alkyl Sn-H reagents in radical assisted organic synthesis

DiGrignard reagents of the form XMg(CH2)(n)MgX, where X = Br or I and n = 6, 8, 10 or 12, were allowed to react with PhSnCl3 to produce highly cross-linked Ph-Sn polymeric networks. The Sn-H moiety was incorporated into these insoluble network polymers by treatment with Br-2 and NaBH4. Excellent accessibility of the Sn-H was displayed by these solvent penetrable but insoluble networks, giving them higher Sn-H loadings than all previously reported supported reagents. These reagents were totally regenerable in NaBH4 for radical assisted organic synthesis and no detectable leaching of the Sn into solution was observed during these reactions.