Small-angle x-ray scattering study of flow alignment of a thermotropic liquid crystal in the nematic and smectic phases

WThe capillary flow alignment of the thermotropic liquid crystal 4-n-octyl-4′-cyanobiphenyl in the nematic and smectic phases is investigated using time-resolved synchrotron small-angle x-ray scattering. Samples were cooled from the isotropic phase to erase prior orientation. Upon cooling through the nematic phase under Poiseuille flow in a circular capillary, a transition from the alignment of mesogens along the flow direction to the alignment of layers along the flow direction (mesogens perpendicular to flow) appears to occur continuously at the cooling rate applied. The transition is centered on a temperature at which the Leslie viscosity coefficient α3 changes sign. The configuration with layers aligned along the flow direction is also observed in the smectic phase. The transition in the nematic phase on cooling has previously been ascribed to an aligning-nonaligning or tumbling transition. At high flow rates there is evidence for tumbling around an average alignment of layers along the flow direction. At lower flow rates this orientation is more clearly defined. The layer alignment is ascribed to surface-induced ordering propagating into the bulk of the capillary, an observation supported by the parallel alignment of layers observed for a static sample at low temperatures in the nematic phase.

Dielectric relaxation around the nematic-isotropic transition of liquid crystalline polymers

This study is concerned with a series of acrylate based side-chain liquid crystalline (LC) polymers. Previous studies have shown that these LC polymers have a preference for parallel or perpendicular alignment with respect to the polymer chain which depends on the length of the coupling chain joining the mesogenic unit to the polymer backbone. On the other hand, the dielectric relaxation of these side-chain LC polymers shows a strong relaxation associated to the mesogenic unit dynamics. For samples with parallel alignment, it was found that the dielectric relaxation of the nematic is weaker and broader than the relaxation of the isotropic. By contrast, for samples with perpendicular alignment, the isotropic to nematic transition reduces the broadening the relaxation and increases the relaxation strength. These two features are more evident for samples with short coupling units for which the dielectric relaxation observed appears to be strongly coupled with the backbone dynamics.

Liquid crystal phase formation by biopolymers

This review discusses liquid crystal phase formation by biopolymers in solution. Lyotropic mesophases have been observed for several classes of biopolymer including DNA, peptides, polymer/peptide conjugates, glycopolymers and proteoglycans. Nematic or chiral nematic (cholesteric) phases are the most commonly observed mesophases, in which the rod-like fibrils have only orientational order. Hexagonal columnar phases are observed for several systems (DNA, PBLG, polymer/peptide hybrids) at higher concentration. Lamellar (smectic) phases are reported less often, although there are examples such as the layer arrangement of amylopectin side chains in starch. Possible explanations for the observed structures are discussed. The biological role of liquid crystal phases for several of these systems is outlined. Commonly, they may serve as a template to align fibrils for defined structural roles when the biopolymer is extruded and dried, for instance in the production of silk by spiders or silkworms, or of chitin in arthropod shells. In other cases, liquid crystal phase formation may occur in vivo simply as a consequence of high concentration, for instance the high packing density of DNA within cell nuclei.

Electro-optical properties of liquid crystal copolymers and their relationship to structural order

A range of side chain liquid crystal copolymers have been prepared using mesogenic and non-mesogenic units. It is found that high levels of the non-mesogenic moieties may be introduced without completely disrupting the organization of the liquid crystal phase. Incorporation of this comonomer causes a marked reduction in the glass transition temperature (Tg), presumably as a result of enhanced backbone mobility and a corresponding lowering of the nematic transition temperature, thereby restricting the temperature range for stability of the liquid crystal phase. The effect of the interactions between the various components of these side-chain polymers on their electro-optic responses is described. Infrared (i.r.) dichroism measurements have been made to determine the order parameters of the liquid crystalline side-chain polymers. By identifying a certain band (CN stretching) in the i.r. absorption spectrum, the order parameter of the mesogenic groups can be obtained. The temperature and composition dependence of the observed order parameter are related to the liquid crystal phase transitions and to the electro-optic response. It is found that the introduction of the non-mesogenic units into the polymer chain lowers the threshold voltage of the electro-optic response over and above that due to the reduction in the order parameter. The dynamic electro-optic responses are dominated by the temperature-dependent viscosity and evidence is presented for relaxation processes involving the polymer backbone which are on a time scale greater than that for the mesogenic side-chain units.

The effect of the molecular weight on the electro-optic properties of methacrylate-based side-chain liquid crystal polymers

A series of methacrylate-based side-chain liquid crystal polymers has been prepared with a range of molecular weights. For the high molecular weight polymers a smectic phase is observed with a very narrow nematic range; however, for low molecular weight polymers only the nematic phase is observed. A marked reduction in the glass transition temperature, TSN and TNI is observed with a reduction in the molecular weight. The orientational order parameters for these polymers in the liquid crystal phase have been determined using infra-red dichroism. It is found that the higher the molecular weight of the polymer, the greater is the threshold voltage of the electro-optic response and the lower the order parameter. The increase in the threshold voltage with increasing molecular weight may be related to the intrinsic curvature elasticity and hence to the coupling between the mesogenic units and the polymer backbone.

Liquid crystalline elastomers: the relationship between macroscopic behaviour and the level of backbone anisotropy

Nematic monodomain liquid crystalline elastomers have been prepared through in situ cross-linking of an acrylate based side-chain liquid crystalline polymer in a magnetic field. At the nematic–isotropic transition, the sample is found to undergo an anisotropic shape change. There is found to be an increase in dimensions perpendicular — and a decrease parallel — to the director, this is consistent with alignment of the polymer backbone parallel to the direction of mesogen alignment in the nematic state. From a quantitative investigation of this behaviour, we estimate the level of backbone anisotropy for the elastomer. As second measure of the backbone anisotropy, the monodomain sample was physically extended. We have investigated, in particular, the situation where a monodomain sample is deformed with the angle between the director and the extension direction approaching 90°. The behaviour on extension of these acrylate samples is related to alternative theoretical interpretations and the backbone anisotropy determined. Comparison of the chain anisotropy derived from these two approaches and the value obtained from previous small-angle neutron scattering measurements on deuterium labelled mixtures of the same polymer shows that some level of chain anisotropy is retained in the isotropic or more strictly weakly paranematic state of the elastomer. The origin and implications of this behaviour are discussed.

Memory effects in liquid crystal elastomers

Free-standing monodomain liquid crystal elastomer samples are shown to have a complete memory of the orientational configuration at the time of cross-linking. This memory is demonstrated through samples in which the parent polymer system is first aligned in a magnetic field prior to cross-linking. These films show reversible nematic-isotropic phase transitions and x-ray scattering patterns characteristic of nematic phases. The liquid crystal elastomer films exhibit a remarkable memory effect, in that the sample may be held at temperatures well above the nematic-isotropic transition for extended periods ( > 2 weeks), but on cooling into the liquid crystal phase region, both the original director alignment and the degree of preferred orientation are recovered. It is demonstrated that these novel memory effects are equilibrium in nature. The origins of this phenomena in terms of coupling between the mesogenic side-chains and the polymer network are discussed.

Coupling between mesogenic units and polymer backbone in side-chain liquid crystal polymers and elastomers

The levels of alignment of the mesogenic units and of the polymer backbone trajectory for polyacrylate based nematic side-chain liquid crystal polymers and elastomers were evaluated by using wide angle X-ray and small angle neutron scattering procedures. The X-ray scattering measurements show that substantial levels of preferred orientation of the mesogenic units may be introduced through magnetic fields for uncrosslinked polymers and through mechanical extension for liquid crystal elastomers. Small angle neutron scattering measurements show that for highly aligned samples an anisotropic polymer backbone trajectory is observed in which the envelope is slightly extended by ∼ 10% in the direction parallel to the axis of alignment of the mesogenic units. The sense of this coupling differs from that recorded for other uncrosslinked side-chain liquid crystal polymers. Possible mechanisms to account for this anisotropy and its relationship to the properties of liquid crystal elastomers are discussed. The observed deformation behaviour of the liquid crystal elastomer is non-affine and this appears to confirm the dominating influence of the liquid crystal order of the side chains on the mechanical properties of these novel networks.

A single director switching mode for monodomain liquid crystal elastomer

We report rotation of a single director in a nematic monodomain, acrylate based side-chain elastomer which was subjected to mechanical fields applied at angles in the range to the director, , present at the time of network formation. Time and spatially resolving wide angle X-ray scattering, together with polarised light microscopy measurements revealed a pronounced, almost discontinuous switching mode at a critical extension as the strain was applied at angles approaching to , whereas a more continuous rotation was seen when the strain was applied at more acute angles. This director reorientation was more or less uniform across the complete sample and was accompanied by a modest decrease in orientation parameter . At strains sufficient to induce switching there was some continuous distribution of director orientations with fluctuations of 10 although there was no evidence for any localised director inhomogenities such as domain formation. The observed deformation behaviour of these acrylate-based nematic monodomains was in accord with the predictions of a theory developed by Bladon et al., in that the complete set of data could be accounted for through a single parameter describing the chain anisotropy. The experimentally deduced chain anisotropy parameter was in broad agreement with that obtained from small-angle neutron scattering procedures, but was somewhat greater than that obtained by spontaneous shape changes at the nematic-isotropic transition.

Side-chain liquid crystalline elastomers: the relationship between the orientational ordering of the polymer backbone and the length of the coupling chain

The influence of cross-linking on the phase behaviour of a series of side-chain liquid crystalline elastomers has been studied. For samples cross-linked in the temperature range corresponding to the nematic phase, the phase transition was shifted compared to that observed when an identical sample was cross-linked in the isotropic phase. This shift represented a stabilisation of the nematic phase in the former case, in line with theoretical expectations. By utilising a novel, slow cross-linking method, which allows the polymer backbone to take up an equilibrium conformation prior to network formation, it proved possible to monitor the shifts in phase transition temperature as a function of the length of the methylene chain coupling the mesogenic units to the polymer backbone. The results obtained are related to the backbone anisotropy and indicate that the level of orientational order of the polymer in the nematic phase backbone increases with a reduction in the length of the coupling chain.

Cinnamate ester containing liquid crystalline side chain polymers

The synthesis of methacrylate esters of 4-cyanophenyl-(4-(ω-hydroxyalkyloxy)) cinnamates, with spacer lengths of 2 and 6 methylene units and the synthesis of the corresponding acrylate ester with a spacer of 2 methylene units are described. The methacrylate monomers were polymerized by free radical polymerization, both as homopolymers and as copolymers with the analogous benzoate monomer of spacer length 6. The acrylate ester could not be polymerized successfully under the same reaction conditions. Polymers were characterized by NMR spectroscopy, gel permeation chromatography, differential scanning calorimetry, and thermo-optic observations. Of the monomers prepared, only the cinnamate with a hexamethylene spacer shows a mesophase, seen on supercooling of the melt. All of the polymers prepared were liquid crystalline, with smectic behavior predominating in the polymethacrylates with the longer spacer group. A narrow nematic region is seen just below the clearing temperature with a range of 3–9°C, nematic character is increased in the copolymer series with the degree of incorporation of the cinnamate monomer with the spacer group of length 2.

Synthesis and phase behaviour of a homologous series of polymethacrylate-based side-chain liquid crystal polymers

The homologous series of side chain liquid crystal polymers, the poly[x-(4-methoxyazobenzene- 40-oxy)alkyl methacrylate]s, has been prepared in which the length of the flexible alkyl spacer has been varied from 3 to 11 methylene units. All the polymers exhibit liquid crystalline behaviour. The propyl and butyl members show exclusively nematic behaviour. The pentyl, hexyl, octyl and decyl members show a nematic and a smectic A phase while the heptyl, nonyl and undecyl homologues exhibit only a smectic A phase. The smectic A phase has been studied using X-ray diffraction and assigned as a smectic A1 phase in which the side chains are fully overlapped and the backbones are confined to lie between the smectic layers. For the nonyl member an incommensurate smectic phase is observed. The dependence of the transition temperatures on the length of the flexible spacer is understood in terms of the average shapes of the side chains.

Coupling liquid MALDI MS to liquid chromatography

Matrix-assisted laser desorption/ionisation (MALDI) coupled with time-of-flight (TOF) mass spectrometry (MS) is a powerful tool for the analysis of biological samples, and nanoflow high-performance liquid chromatography (nanoHPLC) is a useful separation technique for the analysis of complex proteomics samples. The off-line combination of MALDI and nanoHPLC has been extensively investigated and straightforward techniques have been developed, focussing particularly on automated MALDI sample preparation that yields sensitive and reproducible spectra. Normally conventional solid MALDI matrices such as α-cyano-4-hydroxycinnamic acid (CHCA) are used for sample preparation. However, they have limited usefulness in quantitative measurements and automated data acquisition because of the formation of heterogeneous crystals, resulting in highly variable ion yields and desorption/ ionization characteristics. Glycerol-based liquid support matrices (LSM) have been proposed as an alternative to the traditional solid matrices as they provide increased shot-to-shot reproducibility, leading to prolonged and stable ion signals and therefore better results. This chapter focuses on the integration of the liquid LSM MALDI matrices into the LC-MALDI MS/MS approach in identifying complex and large proteomes. The interface between LC and MALDI consists of a robotic spotter, which fractionates the eluent from the LC column into nanoliter volumes, and co-spots simultaneously the liquid matrix with the eluent fractions onto a MALDI target plate via sheath flow. The efficiency of this method is demonstrated through the analysis of trypsin digests of both bovine serum albumin (BSA) and Lactobacillus plantarum WCFS1 proteins.