High-Speed Semiconductor Lasers based on Low-Dimensional Active Materials for Optical Telecommunication

The scope of this work is the fundamental growth, tailoring and characterization of self-organized indium arsenide quantum dots (QDs) and their exploitation as active region for diode lasers emitting in the 1.55 µm range. This wavelength regime is especially interesting for long-haul telecommunications as optical fibers made from silica glass have the lowest optical absorption. Molecular Beam Epitaxy is utilized as fabrication technique for the quantum dots and laser structures. The results presented in this thesis depict the first experimental work for which this reactor was used at the University of Kassel. Most research in the field of self-organized quantum dots has been conducted in the InAs/GaAs material system. It can be seen as the model system of self-organized quantum dots, but is not suitable for the targeted emission wavelength. Light emission from this system at 1.55 µm is hard to accomplish. To stay as close as possible to existing processing technology, the In(AlGa)As/InP (100) material system is deployed. Depending on the epitaxial growth technique and growth parameters this system has the drawback of producing a wide range of nano species besides quantum dots. Best known are the elongated quantum dashes (QDash). Such structures are preferentially formed, if InAs is deposited on InP. This is related to the low lattice-mismatch of 3.2 %, which is less than half of the value in the InAs/GaAs system. The task of creating round-shaped and uniform QDs is rendered more complex considering exchange effects of arsenic and phosphorus as well as anisotropic effects on the surface that do not need to be dealt with in the InAs/GaAs case. While QDash structures haven been studied fundamentally as well as in laser structures, they do not represent the theoretical ideal case of a zero-dimensional material. Creating round-shaped quantum dots on the InP(100) substrate remains a challenging task. Details of the self-organization process are still unknown and the formation of the QDs is not fully understood yet. In the course of the experimental work a novel growth concept was discovered and analyzed that eases the fabrication of QDs. It is based on different crystal growth and ad-atom diffusion processes under supply of different modifications of the arsenic atmosphere in the MBE reactor. The reactor is equipped with special valved cracking effusion cells for arsenic and phosphorus. It represents an all-solid source configuration that does not rely on toxic gas supply. The cracking effusion cell are able to create different species of arsenic and phosphorus. This constitutes the basis of the growth concept. With this method round-shaped QD ensembles with superior optical properties and record-low photoluminescence linewidth were achieved. By systematically varying the growth parameters and working out a detailed analysis of the experimental data a range of parameter values, for which the formation of QDs is favored, was found. A qualitative explanation of the formation characteristics based on the surface migration of In ad-atoms is developed. Such tailored QDs are finally implemented as active region in a self-designed diode laser structure. A basic characterization of the static and temperature-dependent properties was carried out. The QD lasers exceed a reference quantum well laser in terms of inversion conditions and temperature-dependent characteristics. Pulsed output powers of several hundred milli watt were measured at room temperature. In particular, the lasers feature a high modal gain that even allowed cw-emission at room temperature of a processed ridge wave guide device as short as 340 µm with output powers of 17 mW. Modulation experiments performed at the Israel Institute of Technology (Technion) showed a complex behavior of the QDs in the laser cavity. Despite the fact that the laser structure is not fully optimized for a high-speed device, data transmission capabilities of 15 Gb/s combined with low noise were achieved. To the best of the author`s knowledge, this renders the lasers the fastest QD devices operating at 1.55 µm. The thesis starts with an introductory chapter that pronounces the advantages of optical fiber communication in general. Chapter 2 will introduce the fundamental knowledge that is necessary to understand the importance of the active region`s dimensions for the performance of a diode laser. The novel growth concept and its experimental analysis are presented in chapter 3. Chapter 4 finally contains the work on diode lasers.

Molecular Beam Epitaxial Growth of III-V Semiconductor Nanostructures on Silicon Substrates

The main focus and concerns of this PhD thesis is the growth of III-V semiconductor nanostructures (Quantum dots (QDs) and quantum dashes) on silicon substrates using molecular beam epitaxy (MBE) technique. The investigation of influence of the major growth parameters on their basic properties (density, geometry, composition, size etc.) and the systematic characterization of their structural and optical properties are the core of the research work. The monolithic integration of III-V optoelectronic devices with silicon electronic circuits could bring enormous prospect for the existing semiconductor technology. Our challenging approach is to combine the superior passive optical properties of silicon with the superior optical emission properties of III-V material by reducing the amount of III-V materials to the very limit of the active region. Different heteroepitaxial integration approaches have been investigated to overcome the materials issues between III-V and Si. However, this include the self-assembled growth of InAs and InGaAs QDs in silicon and GaAx matrices directly on flat silicon substrate, sitecontrolled growth of (GaAs/In0,15Ga0,85As/GaAs) QDs on pre-patterned Si substrate and the direct growth of GaP on Si using migration enhanced epitaxy (MEE) and MBE growth modes. An efficient ex-situ-buffered HF (BHF) and in-situ surface cleaning sequence based on atomic hydrogen (AH) cleaning at 500 °C combined with thermal oxide desorption within a temperature range of 700-900 °C has been established. The removal of oxide desorption was confirmed by semicircular streaky reflection high energy electron diffraction (RHEED) patterns indicating a 2D smooth surface construction prior to the MBE growth. The evolution of size, density and shape of the QDs are ex-situ characterized by atomic-force microscopy (AFM) and transmission electron microscopy (TEM). The InAs QDs density is strongly increased from 108 to 1011 cm-2 at V/III ratios in the range of 15-35 (beam equivalent pressure values). InAs QD formations are not observed at temperatures of 500 °C and above. Growth experiments on (111) substrates show orientation dependent QD formation behaviour. A significant shape and size transition with elongated InAs quantum dots and dashes has been observed on (111) orientation and at higher Indium-growth rate of 0.3 ML/s. The 2D strain mapping derived from high-resolution TEM of InAs QDs embedded in silicon matrix confirmed semi-coherent and fully relaxed QDs embedded in defectfree silicon matrix. The strain relaxation is released by dislocation loops exclusively localized along the InAs/Si interfaces and partial dislocations with stacking faults inside the InAs clusters. The site controlled growth of GaAs/In0,15Ga0,85As/GaAs nanostructures has been demonstrated for the first time with 1 μm spacing and very low nominal deposition thicknesses, directly on pre-patterned Si without the use of SiO2 mask. Thin planar GaP layer was successfully grown through migration enhanced epitaxy (MEE) to initiate a planar GaP wetting layer at the polar/non-polar interface, which work as a virtual GaP substrate, for the GaP-MBE subsequently growth on the GaP-MEE layer with total thickness of 50 nm. The best root mean square (RMS) roughness value was as good as 1.3 nm. However, these results are highly encouraging for the realization of III-V optical devices on silicon for potential applications.

Modification and Analysis of Group-13-Nitride Semiconductor Surfaces: Influence of Adsorbates on Device Characteristics and Processing

Im Rahmen dieser interdisziplinären Doktorarbeit wird eine (Al)GaN Halbleiteroberflächenmodifikation untersucht, mit dem Ziel eine verbesserte Grenzfläche zwischen dem Material und dem Dielektrikum zu erzeugen. Aufgrund von Oberflächenzuständen zeigen GaN basierte HEMT Strukturen üblicherweise große Einsatzspannungsverschiebungen. Bisher wurden zur Grenzflächenmodifikation besonders die Entfernung von Verunreinigungen wie Sauerstoff oder Kohlenstoff analysiert. Die nasschemischen Oberflächenbehandlungen werden vor der Abscheidung des Dielektrikums durchgeführt, wobei die Kontaminationen jedoch nicht vollständig entfernt werden können. In dieser Arbeit werden Modifikationen der Oberfläche in wässrigen Lösungen, in Gasen sowie in Plasma analysiert. Detaillierte Untersuchungen zeigen, dass die inerte (0001) c-Ebene der Oberfläche kaum reagiert, sondern hauptsächlich die weniger polaren r- und m- Ebenen. Dies kann deutlich beim Defektätzen sowie bei der thermischen Oxidation beobachtet werden. Einen weiteren Ansatz zur Oberflächenmodifikation stellen Plasmabehandlungen dar. Hierbei wird die Oberflächenterminierung durch eine nukleophile Substitution mit Lewis Basen, wie Fluorid, Chlorid oder Oxid verändert, wodurch sich die Elektronegativitätsdifferenz zwischen dem Metall und dem Anion im Vergleich zur Metall-Stickstoff Bindung erhöht. Dies führt gleichzeitig zu einer Erhöhung der Potentialdifferenz des Schottky Kontakts. Sauerstoff oder Fluor besitzen die nötige thermische Stabilität um während einer Silicium-nitridabscheidung an der (Al)GaN Oberfläche zu bleiben. Sauerstoffvariationen an der Oberfläche werden in NH3 bei 700°C, welches die nötigen Bedingungen für die Abscheidung darstellen, immer zu etwa 6-8% reduziert – solche Grenzflächen zeigen deswegen auch keine veränderten Ergebnisse in Einsatzspannungsuntersuchungen. Im Gegensatz dazu zeigt die fluorierte Oberfläche ein völlig neues elektrisches Verhalten: ein neuer dominanter Oberflächendonator mit einem schnellen Trapping und Detrapping Verhalten wird gefunden. Das Energieniveau dieses neuen, stabilen Donators liegt um ca. 0,5 eV tiefer in der Bandlücke als die ursprünglichen Energieniveaus der Oberflächenzustände. Physikalisch-chemische Oberflächen- und Grenzflächenuntersuchung mit XPS, AES oder SIMS erlauben keine eindeutige Schlussfolgerung, ob das Fluor nach der Si3N4 Abscheidung tatsächlich noch an der Grenzfläche vorhanden ist, oder einfach eine stabilere Oberflächenrekonstruktion induziert wurde, bei welcher es selbst nicht beteiligt ist. In beiden Fällen ist der neue Donator in einer Konzentration von 4x1013 at/cm-2 vorhanden. Diese Dichte entspricht einer Oberflächenkonzentration von etwa 1%, was genau an der Nachweisgrenze der spektroskopischen Methoden liegt. Jedoch werden die elektrischen Oberflächeneigenschaften durch die Oberflächenmodifikation deutlich verändert und ermöglichen eine potentiell weiter optimierbare Grenzfläche.