Thermal stability of myofibrillar protein from Indian major carps

The characteristics and stability of natural actomyosin (NAM) from rohu (Labeo rohita), catla (Catla catla) and mrigal (Cirrhinus mrigala) were investigated. The total extractable actomyosin (AM) was higher (7.60mgml−1) in the case of rohu compared with that from catla and mrigal (5mgml−1). Although the specific AM ATPase activity was similar (0.43–0.5 μmolPmin−1 mgP−1) among the three species, the total ATPase activity was lower in mrigal (25 μmol g−1 meat) compared with the other species (37 μmol g−1 meat). The inactivation rate constants (kd) of AM Ca ATPase activity showed differences in the stabilities of actomyosin among these fish, the actomyosin from catla being least stable. The NAM from these species was stable up to 20 ◦C at pH 7.0. Catla AM became unstable at 30 ◦C, while rohu and mrigal AM could withstand up to 45 ◦C. The thermal denaturation with respect to solubility, turbidity, ATPase activity, sulphhydryl group and surface hydrophobicity showed noticeable changes at around these temperatures

Thermal Degradation of Short Nylon -6 Fiber-Reinforced Styrene Butadiene Rubber Composite

The thermal properties of short Nylon-6 fiber-reinforced Styrene butadiene rubber (SBR) composites were studied by Thermogravimetric Analysis (TGA). The effect of epoxy-based bonding agent on thermal degradation of the gum and the composites was also studied. The thermal stability of the SBR was enhanced in the presence of Nylon-6 fibers and the stability of the composites increased in the presence of bonding agent. The epoxy resin did not significantly change the thermal stability of SBR gum vulcanizate. Results of kinetic studies showed that the degradation of SBR and the short nylon fiber-reinforced composites with and without bonding agents followed first-order kinetics.

Thermal degradation of short kevlar fibre thermoplastic polyurethane composite

The thermal degradation of short kevlar fibre-thermoplastic polyurethane (TPU) composites has been studied by Thermogravimetric Analysis (TGA) and Differential Scanning Calorimetry (DSC). TGA showed that the thermal degradation of TPU takes place in two steps with peak maxima (T1max and T2ma,) at 383°C and 448°C, respectively. In the presence of 10-40 phr of short kevlar fibres, T1_ and T2max were shifted to lower temperatures. The temperature of onset of degradation was increased from 245 to 255°C at 40 parts per hundred rubber (phr) fibre loading. Kinetic studies showed that the degradation of TPU and kevlar-TPU composite follows first-order reaction kinetics. The DSC study showed that there is an improvement in thermal stability of TPU in the presence of 20 phr of short kevlar fibres.

Thermal degradation of short polyester fiber polyurethane elastomer composite

The thermal degradation of short polyester fiber reinforced polyurethane composites with and without different bonding agents has been studied by thermogravimetric analysis . It was found that degradation of the polyurethane takes place in two steps and that of the composites takes place in three steps. With the incorporation of 30 phr of fiber in the matrix , the onset of degradation was shifted from 230 to 238 ° C. The presence of bonding agents in the virgin elastomer and the composite gave an improved thermal stability . Results of kinetic studies showed that the degradation of polyurethane and the reinforced composites with and without bonding agents follows first -order reaction kinetics