Organic Reactions Catalysed by Modified Clays

Department of Applied Chemistry, Cochin University of Science and Technology

Characterization of Hydrothermally Annealed Low Temperature Bioactive Thin Film Coatings of Hydroxyapatite on TiAl6V4 Implant material

This thesis summarizes the results on the growth and characterisation of thin films of HA grown on TiAl6V4 (Ti) implant material at a lower substrate temperature by a combination of Pulsed laser deposition and a hydrothermal treatment to get sufficiently strong crystalline films suitable for orthopaedic applications. The comparison of the properties of the coated substrate has been made with other surface modification techniques like anodization and chemical etching. The in-vitro study has been conducted on the surface modified implants to assess its cell viability. A molecular level study has been conducted to analyze the adhesion mechanism of protein adhesion molecules on to HA coated implants.

Modification of Polypropylene and Polystyrene Using Nanosilica

The present work focuses on the modification of the commonly used thermoplastics, polypropylene and polystyrene using nanosilica preparcd from a cheap source of sodium silicate. Melt compounding technique has been used for nanocomposite preparation as it is simple and suited to injection moulding. Nanosilica in a polymer matrix provide significant enhancement in strength, stiffness and impact strength. Incorporation of silica particles in a polymer also improves its thennal stability. To achieve better dispersion of fillers in polymer matrices the mixing was done at different shear rates. The enhancement in material properties indicates that at higher shear rates there is greater interaction between particles and the matrix and it depends on filler concentration and type of polymer used. N anosilica is a useful filler in thennoplastic polymers and has been applied in automotive applications, electronic appliances and consumer goods.This thesis is divided into six chapters. General introduction to the topic is described in chapter 1. Salient features of polymer nanocomposites, their synthesis, properties and applications are presented. A review of relevant literature and the scope and objectives are also mentioned in this chapter.The materials used and the vanous experimental method and techniques employed in the study are described in chapter 2. Preparation of nanocomposites by melt blending using Thenno Haake Rheocord, preparation of samples, evaluation of mechanical and thennal properties using UTM, Impact testing and characterization using DMA, TGA and DSC and morphology by SEM are described.The preparation of nanosilica from a laboratory scale to a pilot plant scale is described in chapter 3. Generation of surface modified silica, evaluation of kinetic parameters of the synthesis reaction, scale up of the reactor and modeling of the reactor are also dealt with in this chapter.The modification of the commodity thennoplastic, Polypropylene using nanosilica is described in chapter 4. Preparation of PP/silica nanocomposites, evaluation of mechanical properties, thermal and crystallization characteristics, water absorption and ageing resistance studies are also presented.The modification of Polystyrene using synthesized nanosilica IS described in chapter 5. The method of preparation of PS/silica nanocomposites, evaluation of mechanical properties (static and dynamic), thermal properties melt flow characteristics using Haake Rheocord, water absorption and ageing resistance of these nanocomposites are studied.

Modification of Polypropylene/High Density Polyethylene Blend Using Nanokaolinite Clay and E-Glass Fibre: Preparation, Characterization and Micromechanical Modelling

Upgrading two widely used standard plastics, polypropylene (PP) and high density polyethylene (HDPE), and generating a variety of useful engineering materials based on these blends have been the main objective of this study. Upgradation was effected by using nanomodifiers and/or fibrous modifiers. PP and HDPE were selected for modification due to their attractive inherent properties and wide spectrum of use. Blending is the engineered method of producing new materials with tailor made properties. It has the advantages of both the materials. PP has high tensile and flexural strength and the HDPE acts as an impact modifier in the resultant blend. Hence an optimized blend of PP and HDPE was selected as the matrix material for upgradation. Nanokaolinite clay and E-glass fibre were chosen for modifying PP/HDPE blend. As the first stage of the work, the mechanical, thermal, morphological, rheological, dynamic mechanical and crystallization characteristics of the polymer nanocomposites prepared with PP/HDPE blend and different surface modified nanokaolinite clay were analyzed. As the second stage of the work, the effect of simultaneous inclusion of nanokaolinite clay (both N100A and N100) and short glass fibres are investigated. The presence of nanofiller has increased the properties of hybrid composites to a greater extent than micro composites. As the last stage, micromechanical modeling of both nano and hybrid A composite is carried out to analyze the behavior of the composite under load bearing conditions. These theoretical analyses indicate that the polymer-nanoclay interfacial characteristics partially converge to a state of perfect interfacial bonding (Takayanagi model) with an iso-stress (Reuss IROM) response. In the case of hybrid composites the experimental data follows the trend of Halpin-Tsai model. This implies that matrix and filler experience varying amount of strain and interfacial adhesion between filler and matrix and also between the two fillers which play a vital role in determining the modulus of the hybrid composites.A significant observation from this study is that the requirement of higher fibre loading for efficient reinforcement of polymers can be substantially reduced by the presence of nanofiller together with much lower fibre content in the composite. Hybrid composites with both nanokaolinite clay and micron sized E-glass fibre as reinforcements in PP/HDPE matrix will generate a novel class of high performance, cost effective engineering material.

Acidity and catalytic activity of rare earth modified Al/Zr pillared clays

The pillared montmorillonite has been prepared by exchanging Na+ in the interlayer of montmorillonite with Al hydroxy cation followed by calcination. Pillared clays are also prepared after exchanging Na' ions with Ce, La, Sm-ions and then pillarcd with aluminium oxides, The surface characterisation of the prepared catalysts has been done using XRD and surface area measurements. To probe the acidic property of the system, temperature programmed desorption (TPD) of NH, has been done. Toluene alkylation by benzyl chloride has been carried out for the evaluation of catalytic activity. The most active system is found to be mixed Al/Zr pillarcd montrnorillonite.

Catalysis by Modified Pillared Clays and Porous Clay Heterostructures

In this venture three distinct class of catalysts such as, pillared clays and transition metal loaded pillared clays , porous clay heterostructures and their transition metal loaded analogues and DTP supported on porous clay heterostructures etc. were prepared and characterized by various physico chemical methods. The catalytic activities of prepared catalysts were comparatively evaluated for the industrially important alkylation, acetalization and oxidation reactions.The general conclusions drawn from the present investigation are  Zirconium, iron - aluminium pillared clays were synthesized by ion exchange method and zirconium-silicon porous heterostructures were Summary and conclusions 259 prepared by intergallery template method. Transition metals were loaded in PILCs and PCHs by wet impregnation method.  Textural and acidic properties of the clays were modified by pillaring and post pillaring modifications.  The shift in 2θ value to lower range and increase in d (001) spacing indicate the success of pillaring process.  Surface area, pore volume, average pore size etc. increased dramatically as a result of pillaring process.  Porous clay heterostructures have higher surface area, pore volume, average pore diameter and narrow pore size distribution than that of pillared clays.  The IR spectrum of PILCs and PCHs are in accordance with literature without much variation compared to parent montmorillonite which indicate that basic clay structure is retained even after modification.  The silicon NMR of PCHs materials have intense peaks corresponding to Q4 environment which indicate that mesoporous silica is incorporated between clay layers.  Thermo gravimetric analysis showed that thermal stability is improved after the pillaring process. PCH materials have higher thermal stability than PILCs.  In metal loaded pillared clays, up to 5% metal species were uniformly dispersed (with the exception of Ni) as evident from XRD and TPR analysis. Chapter 9 260  Impregnation of transition metals in PILCs and PCHs enhanced acidity of catalysts as evident from TPD of ammonia and cumene cracking reactions.  For porous clay heterostructures the acidic sites have major contribution from weak and medium acid sites which can be related to the Bronsted sites as evident from TPD of ammonia.  Pillared clays got more Lewis acidity than PCHs as inferred from α- methyl styrene selectivity in cumene cracking reaction.  SEM images show that layer structure is preserved even after modification. Worm hole like morphology is observed in TEM image of PCHs materials  In ZrSiPCHS, Zr exists as Zr 4+ and is incorporated to silica pillars in the intergallary of clay layers as evident from XPS analysis.  In copper loaded zirconium pillared clays, copper exists as isolated species with +2 oxidation state at lower loading. At higher loading, Cu exists as clusters as evident from reduction peak at higher temperatures in TPR.  In vanadium incorporated PILCs and PCHs, vanadium exist as isolated V5+ in tetrahedral coordination which is confirmed from TPR and UVVis DRS analysis.  In cobalt loaded PCHs, cobalt exists as CoO with 2+ oxidation state as confirmed from XPS.  Cerium incorporated iron aluminium pillared clay was found to be the best catalyst for the hydroxylation of phenol in aqueous media due to the additional surface area provided by ceria mesopores and its redox properties. Summary and conclusions 261  Cobalt loaded zirconium porous clay heterostructures were found to be promising catalyst for the tertiary butylation of phenol due to higher surface area and acidic properties.  Copper loaded pillared clays were found to be good catalyst for the direct hydroxylation of benzene to phenol.  Vanadium loaded PCHs catalysts were found to be efficient catalysts for oxidation of benzyl alcohol.  DTP was firmly fixed on the mesoporous channels of PCHs by Direct method and functionalization method.  DTP supported PCHs catalyst were found to be good catalyst for acetalization of cyclohexanone with more than 90% conversion.

Surface properties and catalytic activity of phosphate modified zirconia

Preparation and physico-chemical characterization or phosphate modified zirconia systems and their application to Friedel-Crafts benzylation and benzoylation of toluene have been reported. The influence of transition metals on the surface properties and catalytic activity has also been discussed.

Acidity/basicity, electron donor properties and catalytic activity of sulphate modified stannic oxide

The surface electron donor properties of sulphate modified stannic oxide have been determined from the adsorption of electron acceptors of various electron affinities on the oxide surface. The acid base properties of stannic oxide have been determined by titration method using Hammett indicators. Catalytic activities of the oxide for esterification of acetic acid using n-butanol.reduction of cyclohexanone in 2-propanol and oxidation of cyclohexanol with benzophenone have been studied. The data have been correlated with the surface electron donor properties of these oxides. The activity for reduction and oxidation decreases and that for esterification reaction increases on modification with sulphate ion. It has heen found that electron donating capacity decreased when stannic oxide was modified with sulphate ion.

Acidity/basicity, electron donor properties and catalytic activity of sulphate modified ceria

The changes in surface acidity/basicity and catalytic activity of cerium oxide due to surface modification by sulphate ion have been investigated. Electron donor properties of both the modified and unmodified oxides have been studied using electron acceptors of various electron affinity values, viz. 7,7,8,8-tetracyanoquinodimethane, 2,3,5,6-tetrachloro--l, 4-benzoquinone. p-dinitrobenzene and m-dinitrobenzene in order to find out whether the increase in acidity on suphation is due to the generation of new acidic sites or they are formed at the expense of some of the basic sites. The surface acidity/basicity has been determined using a set of Hammett indicators. The data have been correlated with the catalytic activity of the oxides for esterification of acetic acid using l-butanol, reduction of cyclohexanone with 2- propanol and oxidation of cyclohexanol using benzophenone.

Catalysis by sulphated tin oxide modified with some transition metal oxides

In the present work, we have tried to evaluate systematically the surface properties of sulphated tin oxide systems modified with three different transition metal oxides viz. iron oxide, tungsten oxide and molybdenum oxide. The catalytic activities of these systems are checked and compared by carrying out some industrially important reactions such as oxidative dehydrogenation of ethylbenzene and Friedel-Crafts reactions.

Catalysis by some metal oxides modified with phosphate ions

Surface acidity of phosphate modified La2O3,CeO2 and SnO2 has been estimated by titrimetric Method using Hammett Indicators.Mixed Oxides of tin and lanthanum have also been prepared and subjected to phosphate modification.Surface characterizartion of the samples has been carried out using XRD, surface area,thermal analysis and IR spectroscopy. Phosphate content in the samples has been chemically estimated. The catalytic activity for benzylation and esterification reaction has also been investigated.

Liquid phase benzylation of o-xylene over pillared clays

Iron, aluminium and mixed iron aluminium pillared clays have been prepared by partial hydrolysis method and doped with IO% Mo, V and Cr. The samples have been characterised by XRD, FTIR and surface area and pore Volume measurements. The surface acid site distribution has been determined by temperature programmed desorption of ammonia. Vanadia incorporated systems show maximum acidity. Benzylation of o-xylene has been done as probe reaction to test catalytic activity. Benzyl chloride is a superior benzylating agent compared to benzyl alcohol in activity and selectivity. Cent percent selectivity towards monobenzylated product is obtained in all the cases. Fe pillared systems exhibit maximum activity. The catalytic activities of the systems can be correlated with the amount of strong add sites. The effects of various reaction variables on the reaction have been studied. Presence of moisture has a diminishing effect on the reaction rate.

Photoinduced oxidation of benzhydrol over lanthana modified sol-gel titania

Lanthana modified sol-gel titania is prepared through particulate sol-gel route and the physico-chemical characterizations of the prepared systems were done using X-Ray diffration, EDX, BET surface area-pore volume measurements and TG-DTG analysis. Benzophenone was observed to be the sole product in the TiO2 photocatalyzed oxidation of benzhydrol in oxygen purged acetonitrile. The influence of various parameters, like irradiation time, amount of catalyst, concentration of the catalyst and other factors on the photocatalytic oxidation has been investigated. The proposed mechanism envisages the involvement of a superoxide radical anion.

Catalysis by Transition Metal Modified Ceria and Ceria-Zirconia Mixed Oxides Prepared via Sol-Gel Route

The aim of catalysis research is to apply the catalyst successfully in economically important reactions in an environmentally friendly way. The present work focuses on the modification of structural and surface properties of ceria and ceria-zirconia catalysts by the incorporation of transition metals. The applications of these catalysts in industrially important reactions like ethylbenzene oxidation, alkylation of aromatics are also investigated.Sol-gel method is effective for the preparation of transition metal modified ceria and ceria-zirconia mixed oxide since it produces catalyst with highly dispersed incorporated metal. Unlike that of impregnation method plugging of pores is not prominent for sol-gel derived catalyst materials. This prevents loss of surface area on metal modification as evident for BET surface area measurements.The powder X-ray diffraction analysis confirms the cubic structure of transition metal modified ceria and ceria-zirconia catalysts. The thermal stability is evident from TGA/DTA analysis. DR UV-vis spectra provide information on the coordination environment of the incorporated metal. EPR analysis ofCr, Mn and Cu modified ceria and a ceria-zirconia catalyst reveals the presence of different oxidation states of incorporated metal.Temperature programmed desorption of ammonia and thermogravimetric desorption of 2,6-dimethyl pyridine confirms the enhancement of acidity on metal incorporation. High a-methyl styrene selectivity in cumene cracking reaction implies the presence of comparatively more number of Lewis acid sites with some amount of Bronsted acid sites. The formation of cyclohexanone during cyclohexanol decomposition confirms the presence of basic sites on the catalyst surface.Mn and Cr modified catalysts show better activity towards ethylbenzene oxidation. A redox mechanism through oxometal pathway is suggested.All the catalysts were found to be active towards benzylation of toluene and a-xylene. The selectivity towards monoalkylated products remains almost 100%. The catalytic activity is correlated with the Lewis acidity of the prepared systems.The activity of the catalysts towards methylation of phenols depends on the strength acid sites as well as the redox properties of the catalysts. A strong dependence of methylation activity on the total acidity is illustrated.