Multiferroic Behavior of Gd Based Manganite

Here we report the multiferroic nature of charge ordered manganite Gd0.5Sr0.5MnO3 for the first time. The temperature variation of dielectric constant shows broad relaxor type ferroelectric transition at around 210K and magnetization measurements shows weak ferromagnetism at 50K. The dielectric peak is very close to charge ordering temperature which is an evidence of the link between electronic state and increase of dielectric response. Butterfly variation of capacitance with voltage confirms ferroelectric nature of the sample at room temperature

Mn2þ-induced room-temperature ferromagnetism and spin-glass behavior in hydrothermally grown Mn-doped ZnO nanorods

The magnetic properties of Mn-doped ZnO (ZnO:Mn) nanorods grown by hydrothermal process at a temperature of 200 8C and a growth time of 3 h have been studied. The samples were characterized by using powder X-ray diffraction with Rietveld refinement, scanning electron microscopy, energy-dispersive X-ray analysis and SQUID magnetometry. Mn (3 wt%) and (5 wt%)-doped ZnO samples exhibit paramagnetic and ferromagnetic behavior, respectively, at room temperature. The spin-glass behavior is observed from the samples with respect to the decrease of temperature. At 10 K, both samples exhibit a hysteresis loop with relatively low coercivity. The room-temperature ferromagnetism in 5 wt% Mn-doped ZnO nanorods is attributed to the increase in the specific area of grain boundaries, interaction between dopant Mn2þ ions substituted at Zn2þ site and the interaction between Mn2þ ions and Zn2þ ions from the ZnO host lattice