Laser-induced thermal characterization of nano Ag metal dispersed ceramic alumina matrix

In this paper, we report the measurements of thermal diffusivity of nano Ag metal dispersed ceramic alumina matrix sintered at different temperatures using laser induced non-destructive photoacoustic technique. Measurements of thermal diffusivity also have been carried out on specimens with various concentration of nano metal. Analysis of the data is done on the basis of one-dimensional model of Rosencwaig and Gersho. The present measurements on the thermal diffusivity of nano metal dispersed ceramic alumina shows that porosity has a great influence on the heat transport and the thermal diffusivity value. The present analysis also shows that the inclusion of nano metal into ceramic matrix increases its interconnectivity and hence the thermal diffusivity value. The present study on the samples sintered at different temperature shows that the porosity of the ceramics varies considerably with the change in sintering temperature. The results are interpreted in terms of phonon assisted heat transfer mechanism and the exclusion of pores with the increase in sintering temperature.

Laser-induced thermal characterization of nano Ag metal dispersed ceramic alumina matrix

In this paper, we report the measurements of thermal diffusivity of nano Ag metal dispersed ceramic alumina matrix sintered at different temperatures using laser induced non-destructive photoacoustic technique. Measurements of thermal diffusivity also have been carried out on specimens with various concentration of nano metal. Analysis of the data is done on the basis of one-dimensional model of Rosencwaig and Gersho. The present measurements on the thermal diffusivity of nano metal dispersed ceramic alumina shows that porosity has a great influence on the heat transport and the thermal diffusivity value. The present analysis also shows that the inclusion of nano metal into ceramic matrix increases its interconnectivity and hence the thermal diffusivity value. The present study on the samples sintered at different temperature shows that the porosity of the ceramics varies considerably with the change in sintering temperature. The results are interpreted in terms of phonon assisted heat transfer mechanism and the exclusion of pores with the increase in sintering temperature

Laser-induced thermal characterization of nano Ag metal dispersed ceramic alumina matrix

In this paper, we report the measurements of thermal diffusivity of nano Ag metal dispersed ceramic alumina matrix sintered at different temperatures using laser induced non-destructive photoacoustic technique. Measurements of thermal diffusivity also have been carried out on specimens with various concentration of nano metal. Analysis of the data is done on the basis of one-dimensional model of Rosencwaig and Gersho. The present measurements on the thermal diffusivity of nano metal dispersed ceramic alumina shows that porosity has a great influence on the heat transport and the thermal diffusivity value. The present analysis also shows that the inclusion of nano metal into ceramic matrix increases its interconnectivity and hence the thermal diffusivity value. The present study on the samples sintered at different temperature shows that the porosity of the ceramics varies considerably with the change in sintering temperature. The results are interpreted in terms of phonon assisted heat transfer mechanism and the exclusion of pores with the increase in sintering temperature

Electron donating properties and catalytic actiVity of cerium oxide and its mixed oxides with alumina

The electron donating properties of Ce02 and its mixed oxides with alumina have been determined from the studies of adsorption of electron acceptors of various electron affinities on the surface of these oxides. The catalytic activity of these oxides towards some reactions such as oxidation of alcohols and reduction of ketones have been Correlated with their surface electrondonor properties. The surface acidity/basicity of these oxides have also been determined by titration method using a set of Hammett indicators.

Basicity and electron donor properties of lanthanum oxide and its mixed oxides with alumina

The electron donating properties of La2O3 activated at 300, 500 and 800·C and its mixed oxides with alumina are reported from the studies on adsorption of electron acceptors of varying electron affinity on La203. The electron acceptors with their electron affinity values given in parenthesis are: 7,7,8,8-tetracyanoquinodimethane (2.84 eV), 2,3,5,6-tetrachloro-I,4-benzoquinone (2.40 eV) and p-dinitrobenzene(l.77eV). The basicity of the oxide has been determined by titration with n-butylamine and Ho.max values are reported. The limit of electron transfer from the oxide to the electron acceptor is between 2.40 and 1.77 eV. It is observed that La203 promotes the surface electron properties of alumina without changing its limit of electron transfer.

Surface electron properties of yttrium oxide supported on alumina

Cochin University of Science and Technology

Acid-base, electron-donating and magnetic properties of Nd2O3 and its mixed oxides with alumina catalysts

The electron donor properties of Nd2O3 activated at 300, 500 and 800°C were investigated through studies on the adsorption of electron acceptors of various electron affinities - 7, 7, 8,8-tetracyanoquinodimethane (2.84 eV). 2, 3, 5, 6-tetrachloro-l , 4-benzoquinone (2.40 eV). p-dinitrobenzene (1.77 eV), and m-dinitrobenzene (1.26 eV) in solvents acetonitrile and 1, 4-dioxan. The extent of electron transfer during adsorption has been found from magnetic measurements and electronic spectral data. The corresponding data on mixed oxides of neodymium and aluminium are reported for various. compositions. The acid-base properties of catalysts were also determined using a set of Hammett indicators.

Surface acidity/basicity of yttria and its mixed oxides with alumina catalysts

Acid/base strength distribution of Y2O3 and its mixed oxides with alumina catalysts are measured on Hammett acidity function scale and expressed in terms of H0max value. Basicity of Y2O3 increases with increase in activation temperature and for mixed oxides the basicity increases with increase in concentration of Y2O3, in the catalyst.

Acetalization of ketones on K-10 clay and rare earth exchanged HFAU-Y zeolites: A mild and facile procedure for the synthesis of dimethylacetals

Dimethylacetals of ketones; cyclohexanone, acetophenone, and benzophenone have been prepared by reacting ketones with methanol under mild reaction conditions. Large pore zeolites (H-Y and its rare earth metal, Ce3+, La3+, and RE3+ modified forms), and mesoporous clay (K-10 montmorillonite and its cerium exchanged counterpart) with regular pore structure, silica and silica-alumina have been used as catalysts. Clay catalysts are found to be much more active than zeolites, thanks to slightly bigger pore size. The nature of the pores of the solid acid catalysts determine acetalization efficiency of a particular catalyst. As evidenced by the reaction time studies, the catalyst decay is greater over the zeolites than over the clays. Carrying out the reaction with ketones of different molecular sizes it is shown that K-10 clays and rare earth exchanged H-Y zeolites are promising environmentally friendly catalysts for their use in the production fine chemicals.

Dehydration of aldoximes on rare earth exchanged (La3+, Ce3+, RE3+, Sm3+) Na–Y zeolites: A facile route for the synthesis of nitriles

Rare earth exchanged Na–Y zeolites, H-mordenite, K-10 montmorillonite clay and amorphous silica-alumina were effectively employed for the continuous synthesis of nitriles. Dehydration of benzaldoxime and 4-methoxybenzaldoxime were carried out on these catalysts at 473 K. Benzonitrile (dehydration product) was obtained in near quantitative yield with benzaldoxime whereas; 4-methoxybenzaldoxime produces both Beckmann rearrangement (4-methoxyphenylformamide) as well as dehydration products (4-methoxy benzonitrile) in quantitative yields. The production of benzonitrile was near quantitative under heterogeneous reaction conditions. The optimal protocol allows nitriles to be synthesized in good yields through the dehydration of aldoximes. Time on stream (TOS) studies show decline in the activity of the catalysts due to neutralization of acid sites by the basic reactant and product molecules and water formed during the dehydration of aldoximes.

Surface Electron Donor Properties of Dy2O3,Y2O3 and Their Mixed Oxides with Alumina Catalyst

The limit of electron transfer in electron affinity from the oxide surface to the electron acceptor (EA) are reported from the adsorption of EA on DY203, mixed oxides of DY203 with alumina and mixed oxides of Y203 with y-alumina. The extent of electron transfer is understood from magnetic measurements.

Photoacoustic study of the effect of degassing temperature on thermal diffusivity of hydroxyl loaded alumina

The thermal diffusivity of y-alumina is determined by the photoacoustic method. The method is calibrated by determining the thermal diffusivity of copper and aluminum. The effect of the chemisorbed hydroxyl groups or thermal diffusivity is studied by degassing the sample at different temperatures.

Acid-base and Electron Donor Properties of Pr6O11 and Its Mixtures with Alumina

The electron donor properties of Pr6O11 activated at 300. 500 and 800°C are reported from the studies on adsorption of electron acceptors of various electron affinity (7. 7, 8, 8-tetracyanoquinodimethane. 2, 3. 5, 6-tetrachloro-l, 4-benzoquin one. p-dinitrobenzene. and m-dinitrobenzene) in three solvents (acetonitrile, 1,4-dioxan and ethyl acetate). The extent of electron transfer during adsorption is understood from magnetic measurements and ESR spectral data. The corresponding data on mixed oxides of Pr and Al are reported for various compositions, The acid / base properties of these oxides are determined using a set of Hammett indicators.

Photoacoustic Thermal Characterization of Porous Rare-Earth Phosphate Ceramics

The laser induced non-destructive photoacoustic technique has been employed to measure the thermal diffusivity of lanthanum phosphate ceramics prepared by the sol–gel route. The thermal diffusivity value was evaluated by knowing the transition frequency between the thermally thin to thermally thick region from the log–log plot of photoacoustic amplitude versus chopping frequency. Analysis of the data was carried out on the basis of the one-dimensional model of Rosencwaig and Gersho. The present investigation reveals that the sintering temperature has great influence on the propagation of heat carriers and hence on the thermal diffusivity value. The results were interpreted in terms of variations in porosity with sintering temperature as well as with changes in grain size.