Enhancement of Diffraction Efficiency and Storage Life of Poly (Vinyl Chloride) Based Optical Recording Medium with the Incorporation of an Electron Donor

The differaction efficiency,sensitivity and storage life of Methylene Blue sencitized poly (vinyl chloride) film was improved by the addition of an electron donor in the matrix. The addition of pyridine enhanced the diffraction efficiency by two times and storage life of the gratings was increased to 2-3 days.

Fabrication and Characterization of Methylene-Blue-Doped Polyvinyl Alcohol–Polyacrylicacid Blend for Holographic Recording

A methylene-blue-sensitized polymer blend of polyvinyl alcohol and polyacrylic acid is fabricated and tested for holographic recording. It was found to have good characteristics such as high sensitivity, storage stability, ease of fabrication, and environmental stability. Optimization of the ratio of polyvinyl alcohol polyacrylic acid, the sensitizer concentration, pH, energy, diffraction efficiency measurements, etc., have been done. pH is found to have a great influence on the recovery of the dye in this matrix. The results of experimental investigations into the properties of this new material are reported.

Methylene Blue Doped Polymers: efficient Media for Optical Recording

Polymer materials find application in optical storage technology, namely in the development of high information density and fast access type memories. A new polymer blend of methylene blue sensitized polyvinyl alcohol (PVA) and polyacrylic acid (PAA) in methanol is prepared and characterized and its comparison with methylene blue sensitized PVA in methanol and complexed methylene blue sensitized polyvinyl chloride (CMBPVC) is presented. The optical absorption spectra of the thin films of these polymers showed a strong and broad absorption region at 670-650 nm, matching the wavelength of the laser used. A very slow recovery of the dye on irradiation was observed when a 7:3 blend of polyvinyl alcohol/polyacrylic acid at a pHof 3.8 and a sensitizer concentration of 4.67 10 5 g/ml were used. A diffraction efficiency of up to 20% was observed for the MBPVA/alcohol system and an energetic sensitivity of 2000 mJ/cm2 was obtained in the photosensitive films with a spatial frequency of 588 lines/mm.

Reusable Recording Medium Based on MBPVA and Vinyl Acetate

A new photopolymerizable recording media is introduced based on poly (vinyl alcohol) and vinyl acetate sensitized with methylene blue. It is observed that this MBPVA/VAc system can be reused a number of times without significant decrease in diffraction efficiency. The PVA-VAc ratio was optimized at 2:1. Diffraction efficiency of 6.3% was obtained without any fixing at a dye concentration of 9.3 10 4 mol/l at an exposure of 750 mJ/cm2. The material is attractive on account of its reusability.

Enhancement of Diffraction Efficiency and Storage Life of Poly (Vinyl Chloride) Based Optical Recording Medium with the Incorporation of an Electron Donor

The differaction efficiency,sensitivity and storage life of Methylene blue sensitized poly(vinyl chloride) film was improved by the addition of an electron donor in the matrix. The addition of pyridine enhanced the diffraction efficiency by two times and storage life of the gratings was increased to 2-3 days.

Fabrication and Characterization of Methylene-Blue-Doped Polyvinyl Alcohol–Polyacrylic Acid Blend for Holographic Recording

A methylene-blue-sensitized polymer blend of polyvinyl alcohol and polyacrylic acid is fabricated and tested for holographic recording. It was found to have good characteristics such as high sensitivity, storage stability, ease of fabrication, and environmental stability. Optimization of the ratio of polyvinyl alcohol polyacrylic acid, the sensitizer concentration, pH, energy, diffraction efficiency measurements, etc., have been done. pH is found to have a great influence on the recovery of the dye in this matrix. The results of experimental investigations into the properties of this new material are reported.

Methylene Blue Doped Polymers:Efficient Media for Optical Recording

Polymer materials find application in optical storage technology, namely in the development of high information density and fast access type memories. A new polymer blend of methylene blue sensitized polyvinyl alcohol (PVA) and polyacrylic acid (PAA) in methanol is prepared and characterized and its comparison with methylene blue sensitized PVA in methanol and complexed methylene blue sensitized polyvinyl chloride (CMBPVC) is presented. The optical absorption spectra of the thin films of these polymers showed a strong and broad absorption region at 670-650 nm, matching the wavelength of the laser used. A very slow recovery of the dye on irradiation was observed when a 7:3 blend of polyvinyl alcohol/polyacrylic acid at a pHof 3.8 and a sensitizer concentration of 4.67 10 5 g/ml were used. A diffraction efficiency of up to 20% was observed for the MBPVA/alcohol system and an energetic sensitivity of 2000 mJ/cm2 was obtained in the photosensitive films with a spatial frequency of 588 lines/mm.

Reusable Recording Medium Based on MBPVA and vinyl Acetate

A new photopolymerizable recording media is introduced based on poly (vinyl alcohol) and vinyl acetate sensitized with methylene blue. It is observed that this MBPVA/VAc system can be reused a number of times without significant decrease in diffraction . The PVA-VAc ratio was optimized at 2:1. Diffraction efficiency of 6.3% was obtained without any fixing at a dye concentration of 9.3 10 4 mol/l at an exposure of 750 mJ/cm2. The material is attractive on account of its reusability.

Reusable recording medium based on MBPVA and vinyl acetate

A new photopolymerizable recording media is introduced based on poly (vinyl alcohol) and vinyl acetate sensitized with methylene blue. It is observed that this MBPVA/VAc system can be reused a number of times without significant decrease in diffraction efficiency. The PVA-VAc ratio was optimized at 2:1. Diffraction efcienc4y of 6.3% was obtained without any fixing at a dye concentration of 9.3 x 10- mol/l at an exposure of 750mJ/cm2. The material is attractive on account of its reusability.

Complex methylene-blue-sensitized polyvinyl chloride: a polymer matrix for hologram recording

A new polymer matrix sensitized with methylene blue for use as an optical recording material is described here. The characterization is done to determine the optimal recording conditions. These films need no chemical development and are found to be stable for several months. The matrix has excellent shelf life and needs an exposure only as short as 20 s. Direct imaging was done on this material.

Reusable Recording Medium Based on MBPVA and Vinyl Acetate

A new photopolymerizable recording media is introduced based on poly (vinyl alcohol) and vinyl acetate sensitized with methylene blue. It is observed that this MBPVA/VAc system can be reused a number of times without significant decrease in diffraction efficiency. The PVA-VAc ratio was optimized at 2:1. Diffraction efcienc4y of 6.3% was obtained without any fixing at a dye concentration of 9.3 x 10- mol/l at an exposure of 750mJ/cm2. The material is attractive on account of its reusability.

Reusable Recording Medium based on MBPVA and Vinyl Acetate

A new photopolymerizable recording media is introduced based on poly (vinyl alcohol) and vinyl acetate sensitized with methylene blue. It is observed that this MBPVA/VAc system can be reused a number of times without significant decrease in diffraction efficiency. The PVA-VAc ratio was optimized at 2:1. Diffraction efcienc4y of 6.3% was obtained without any fixing at a dye concentration of 9.3 x 10- mol/l at an exposure of 750mJ/cm2. The material is attractive on account of its reusability.

Studies on Photosensitive polymers for Optical Recording

Department of Polymer Science and Rubber Technology,Cochin University of Science and Technology

Movement of Input and Output Prices of Rice in Kerala and its Impact on Area, Yield and Outp

Rice is the most extensively cultivated crop in the world, particularly concentrated in Asia and the Far East. Asian countries together make up for as much as 91.80 per cent of the world production of rice in 1986. The main objective of the present study is to analyse the rice economy of Kerala over time and space at the State, district and taluk level. The thesis analyses the trends in area, yield and total production of rice during the three seasons in the state, districts and taluks and studies the trends in input and output prices of rice and coconut in the state, districts and taluks. The researcher estimates the impact of input and output prices on area, yield and total output of rice in the state, districts and selected taluks and examines the conversion of paddy field into coconut garden and rubber plantation.