Effect of preparation on magnetic properties of Mn-Zn ferrite

Mixed ferrites belonging to the type Mn0.9Zn0.1Fe2O4 have been prepared by the double sintering method and by the chemical co-precipitation for comparing their magnetic properties. Sintered and precipitated ferrites exhibit different characteristics, especially in their magnetic properties like magnetization (Ms), coercive field (Hc) and Curie temperature (Tc). The sintered particles were size reduced in order to compare with the nanosized co-precipitated particles. The effect of grinding has also been studied. Particles have been collected at regular intervals of grinding and their properties have been studied. The increase in the coercive field has been recorded by a hysteresis curve tracer confirming size reduction. X-ray diffraction studies confirmed the structure and consequent size reduction

Surface Properties and Catalytic Activity of Manganese Ferrospinels

In recent years considerable advances have been achieved in the study of the surface structure and mechanism of action of environmentally benign heterogeneous catalysts. The study entitled as surface properties and catalytic activity of manganese ferrospinels. In the present study we have prepared manganese ferrospinels of general formula Mn(1-x)BxFe2O4 via low temperature controlled co-precipation method. The study employed low temperature co-precipitation method for the preparation ofMn(1-x)BxFe2O4 specimens, where B is a metal cation such as Cr,Co, Ni,Cu and Zn. The catalytic activities of the systems were investigated for liquid-phase benzoylation of aromatic compounds and phenol hydroxylation and for vapour-phase reactions such as aniline alkylation, phenol methylation and ODH of ethylbenzene. The different series of manganese ferrites are proved to be excellent catalysts for various industrially important reactions such as Friedel-crafts benzoylation of aromatic compounds, methylation of aniline and phenol, hydroxylation of phenol and oxidative dehydrogenation of ethylbenzene. Due to the tightening of the environmental regulations, production of diphenols from phenol hydroxylation and reduction of phenolic pollutants in waste waters using these catalysts can be a promising approach because it demands only simple techniques and produce little environmental pollution.

Preparation and Characterisation of Spinel Ferrites - Their Incorporation in Rubber Matrix and Evaluation of Properties

The objectives of the proposed work are preparation of ceramic nickel zinc ferrite belonging to the series Ni1-XZnXFe2O4 with x varying from 0 to 1in steps of 0.2, structrural, magnetic and electrical characterization of Ni1-XZnXFe2O4, preparation and evaluation of Cure characteristics of Rubber Ferrite Composites (RFCs), magnetic characterization of RFCs using vibrating sample magnetometer (VSM), electrical characterization of RFCs and estimation of magnetostriction constant form HL parameters. The study deals with the structural and magnetic properties of ceramic fillers, variation of coercivity with composition and the variation of magnetization for different filler loadings are compared and correlated. The dielectric properties of ceramic Ni1-XZnXFe2O4 and rubber ferrite composites containing Ni1-XZnXFe2O4 were evaluated and the ac electrical conductivity (ac) of ceramic as well as composite samples can be calculated by using a simple relationship of the form ac = 2f tan 0r, with the data available from dielectric measurements. The results suggest that the ac electrical conductivity is directly proportional to the frequency

Acidity, basicity and catalytic activity of La−Zn mixed oxides

Surface acidity/Basicity of mixed oxides of La and Zn activated at three different temperatures were determined. The data have been correlated with the catalytic activity for liquid phase reduction of cyclohexanone in isopropanol.

Catalytic oxidation of cyclohexane over Cu-Zn-Cr ternary spinel systems

Spinel systems with the composition of Cu 1−x Zn x Cr 2 O 4 [x = 0 CCr, x = 0.25 CZCr-1, x = 0.5 CZCr-2, x = 0.75 CZCr-3 and x = 1 ZCr] were prepared by homogeneous co-precipitation method and were characterized by X-ray diffraction (XRD) and FT-IR spectroscopy. Elemental analysis was done by EDX, and surface area measurements by the BET method. The redox behavior of these catalysts in cyclohexane oxidation at 243 K using TBHP as oxidant was examined. Cyclohexanone was the major product over all catalysts with some cyclohexanol. 69.2% selectivity to cyclohexanol and cyclohexanone at 23% conversion of cyclohexane was realized over zinc chromite spinels in 10 h.

On the Synthesis and Multifunctional Properties of some Nanocrystalline Spinel Ferrites and Magnetic Nanocomposites

This thesis lays importance in the preparation and characterization of a few selected representatives of the ferrite family in the nanoregime. The candidates being manganese zinc ferrite and cobalt ferrite prepared by coprecipitation and sol-gel combustion techniques respectively. The thesis not only stresses importance on the preparation techniques and optimization of the reaction conditions, but emphasizes in investigating the various properties namely structural, magnetic and electrical. Passivated nickel nanocomposites are synthesized using polystyrene beads and adopting a novel route of ion exchange reduction. The structural and magnetic properties of these magnetic nanocomposites are correlated. The magnetocaloric effect (MCE) exhibited by these materials are also investigated with a view to finding out the potential of these materials as magnetic refrigerants. Calculations using numerical methods are employed to evaluate the entropy change on selected samples.

Catalysis By Ferrites And Cobaltites For The Alkylation And Oxidation Of Organic Compounds

Catalysis is a very important process from an industrial point of view since the production of most industrially important chemicals involves catalysis.Solid acid catalysts are appealing since the nature of acid sites is known and their chemical behavior in acid catalyzed reactions can be rationalized by means of existing theories and models. Mixed oxides crystallizing in spinel structure are of special interest because the spinel lattice imparts extra stability to the catalyst under various reaction conditions so that theses systems have sustained activities for longer periods. The thesis entitled" Catalysis By Ferrites And Cobaltites For The Alkylation And Oxidation Of Organic Compounds " presents the preparation ,characterization ,and activity studies of the prepared spinels were modified by incorporating other ions and by changing the stoichiometry.The prepared spinels exhibiting better catalytic activity towards the studied reactions with good product selectivity.Acid-base properties and cation distribution of the spinels were found to control the catalytic activity.

Impact of zinc substitution on the structural and magnetic properties of chemically derived nanosized manganese zinc mixed ferrites

Mn1-xZnxFe2O4 nanoparticles (x=0-1) were synthesized by wet chemical co-precipitation techniques. X-ray diffraction, transmission electron microscopy and high-resolution transmission electron microscopy were effectively utilized to investigate the different structural parameters. The elemental analysis was conducted using energy-dispersive spectrum and inductively coupled plasma analysis. The magnetic properties such as magnetization and coercivity were measured using vibrating sample magnetometer. The observed magnetization values of the nanoparticles were found to be lower compared to the bulk counterpart. The magnetization showed a gradual decrease with zinc substitution except for a small increase from x=0.2 to 0.3. The Curie temperature was found to be enhanced in the case of ferrites in the nanoregime. The variation in lattice constant, reduced magnetization values, variation of magnetization with zinc substitution, the presence of a net magnetic moment for the zinc ferrite and the enhancement in Curie temperature in Mn1-xZnxFe2O4 all provide evidence to the existence of a metastable cation distribution together with possible surface effects at the nanoregime.

Ferrofluid thin films as optical gaussmeters proposed for field and magnetic moment sensing

Ferrofluids belonging to the series, Ni x Fe1-x Fe2O4 and Zn x Fe1-x Fe2O4, were synthesized using cold co-precipitation. Liquid films of these ferrofluids were prepared by encapsulating the ferrofluids in between two optically smooth and ultrasonically cleaned glass plates. Magnetic field induced laser transmission through these ferrofluid films has been investigated. Magnetic field values can be calibrated in terms of output laser power in the low field region in which the variation is linear. This set up can be used as a cheap optical gaussmeter in the low field regime. Using the same set-up, the saturation magnetization of the sample used can also be calculated with a sample that is pre-characterized. Hence both magnetization of the sample, as well as applied magnetic field can be sensed and calculated with a precalibrated sample.

Studies on the structural, electrical and magnetic properties of composites based on spinel ferrites

This thesis mainly deals with the preparation and studies on magnetic composites based on spinel ferrites prepared both chemically and mechanically. Rubber ferrite composites (RFC) are chosen because of their mouldability and flexibility and the ease with which the dielectric and magnetic properties can be manipulated to make them as useful devices. Natural rubber is chosen as the Matrix because of its local availability and possible value addition. Moreover, NR represents a typical unsaturated nonpolar matrix. The work can be thought of as two parts. Part l concentrates on the preparation and characterization of nanocomposites based on y-Fe203. Part 2 deals with the preparation and characterization of RFCs containing Nickel zinc ferrit In the present study magnetic nanocomposites have been prepared by ionexchange method and the preparation conditions have been optimized. The insitu incorporation of the magnetic component is carried out chemically. This method is selected as it is the easiest and simplest method for preparation of nanocomposite. Nanocomposite samples thus prepared were studied using VSM, Mossbauer spectroscopy, Iron content estimation, and ESR spectroscopy. For the preparation of RFCs, the filler material namely nickel zinc ferrite having the general formula Ni)_xZnxFez04, where x varies from 0 to 1 in steps of 0.2 have been prepared by the conventional ceramic techniques. The system of Nil_xZn"Fe204 is chosen because of their excellent high frequency characteristics. After characterization they are incorporated into the polymer matrix of natural rubber by mechanical method. The incorporation is done according to a specific recipe and for various Loadings of magnetic fillers and also for all compositions. The cure characteristics, magnetic properties and dielectric properties of these composites are evaluated. The ac electrical conductivity of both ceramic nickel zinc ferrites and rubber ferrite composites are also calculated using a simple relation. The results are correlated.

On the magnetic properties of ultra-Þne zinc ferrites

Zinc ferrite belongs to the class of normal spinels where it is assumed to have a cation distribution of Zn2`(Fe3`)2(O2~)4, and it is purported to be showing zero net magnetisation. However, there have been recent reports suggesting that zinc ferrite exhibits anomaly in its magnetisation. Zinc ferrite samples have been prepared by two di¤erent routes and have been analysed using low energy ion scattering, Mo¬ ssbauer spectroscopy and magnetic measurements. The results indicate that zinc occupies octahedral sites, contrary to the earlier belief that zinc occupies only the tetrahedral sites in a normal spinel. The amount of zinc on the B site increases with decrease in particle size. The LEIS results together with the Mo¬ ssbauer results and the magnetic measurements lead to the conclusion that zinc occupies the B site and the magnetisation exhibited by ultraÞne particles of zinc is due to short range ordering

Tailoring magnetic and dielectric properties of rubber ferrite composites containing mixed ferrites

Rubber ferrite composites containing various mixed ferrites were prepared for different compositions and various loadings. The magnetic and dielectric properties of the fillers as well as the ferrite filled matrixes were evaluated separately. The results are correlated. Simple equations are proposed to predetermine the magnetic and dielectric properties. The validity of these equations is verified and they are found to be in good agreement. These equations are useful in tailoring the magnetic and dielectric properties of these composites with predetermined properties

Processability, hardness, andmagnetic properties of rubber ferrite composites containingmanganese zinc ferrites

Rubber ferrite composites have the unique advantage of mouldability, which is not easily obtainable using ceramic magnetic materials. The incorporation of mixed ferrites in appropriate weight ratios into the rubber matrix not only modi es the dielectric properties of the composite but also imparts magnetic properties to it. Mixed ferrites belonging to the series of Mn(1 – x )Znx Fe2O4 have been synthesised with diVerent values of x in steps of 0·2, using conventional ceramic processing techniques. Rubber ferrite composites were prepared by the incorporation of these pre-characterised polycrystallineMn(1 – x )Znx Fe2O4 ceramics into a natural rubber matrix at diVerent loadings according to a speci c recipe. The processability of these elastomers was determined by investigating their cure characteristics. The magnetic properties of the ceramic llers as well as of the rubber ferrite composites were evaluated and the results were correlated. Studies of the magnetic properties of these rubber ferrite composites indicate that the magnetisation increases with loading of the ller without changing the coercive eld. The hardness of these composites shows a steady increase with the loading of the magnetic llers. The evaluation of hardness andmagnetic characteristics indicates that composites with optimummagnetisation and almost minimum stiVness can be achieved with a maximum loading of 120 phr of the ller at x=0·4. From the data on the magnetisation of the composites, a simple relationship connecting the magnetisation of the rubber ferrite composite and the ller was formulated. This can be used to synthesise rubber ferrite composites with predetermined magnetic properties