Reusable Recording Medium Based on MBPVA and Vinyl Acetate

A new photopolymerizable recording media is introduced based on poly (vinyl alcohol) and vinyl acetate sensitized with methylene blue. It is observed that this MBPVA/VAc system can be reused a number of times without significant decrease in diffraction efficiency. The PVA-VAc ratio was optimized at 2:1. Diffraction efficiency of 6.3% was obtained without any fixing at a dye concentration of 9.3 10 4 mol/l at an exposure of 750 mJ/cm2. The material is attractive on account of its reusability.

Reusable Recording Medium Based on MBPVA and vinyl Acetate

A new photopolymerizable recording media is introduced based on poly (vinyl alcohol) and vinyl acetate sensitized with methylene blue. It is observed that this MBPVA/VAc system can be reused a number of times without significant decrease in diffraction . The PVA-VAc ratio was optimized at 2:1. Diffraction efficiency of 6.3% was obtained without any fixing at a dye concentration of 9.3 10 4 mol/l at an exposure of 750 mJ/cm2. The material is attractive on account of its reusability.

Reusable recording medium based on MBPVA and vinyl acetate

A new photopolymerizable recording media is introduced based on poly (vinyl alcohol) and vinyl acetate sensitized with methylene blue. It is observed that this MBPVA/VAc system can be reused a number of times without significant decrease in diffraction efficiency. The PVA-VAc ratio was optimized at 2:1. Diffraction efcienc4y of 6.3% was obtained without any fixing at a dye concentration of 9.3 x 10- mol/l at an exposure of 750mJ/cm2. The material is attractive on account of its reusability.

Reusable Recording Medium Based on MBPVA and Vinyl Acetate

A new photopolymerizable recording media is introduced based on poly (vinyl alcohol) and vinyl acetate sensitized with methylene blue. It is observed that this MBPVA/VAc system can be reused a number of times without significant decrease in diffraction efficiency. The PVA-VAc ratio was optimized at 2:1. Diffraction efcienc4y of 6.3% was obtained without any fixing at a dye concentration of 9.3 x 10- mol/l at an exposure of 750mJ/cm2. The material is attractive on account of its reusability.

Reusable Recording Medium based on MBPVA and Vinyl Acetate

A new photopolymerizable recording media is introduced based on poly (vinyl alcohol) and vinyl acetate sensitized with methylene blue. It is observed that this MBPVA/VAc system can be reused a number of times without significant decrease in diffraction efficiency. The PVA-VAc ratio was optimized at 2:1. Diffraction efcienc4y of 6.3% was obtained without any fixing at a dye concentration of 9.3 x 10- mol/l at an exposure of 750mJ/cm2. The material is attractive on account of its reusability.

Microwave studies of a poly vinyl acetate (PVA)-based phantom for applications in medical imaging

A phantom that exhibits complex dielectric properties similar to low-water-content biological tissues over the electromagnetic spectrum of 2000–3000 MHz has been synthesized from carbon black, graphite powder, and poly vinyl acetate (PVA)-based adhesive. The material overcomes various problems that are inherent in conventional phantoms such as decomposition and deterioration due to the invasion of bacteria or mold. The absorption coefficients of the material for various concentrations of carbon and graphite are studied. A combination of 50% poly-vinyl-acetate-based adhesive, 20% carbon, and 30% graphite exhibits a high absorption coefficient, which suggests another application of the material as a good microwave absorber for the interior lining of tomographic chamber in microwave imaging. The cavity-perturbation technique is adopted to study the dielectric properties of the material.

Effect of II‐VI Semiconductor Nanomaterials and Electron Irradiation on Polystyrene (PS) & Poly(ethylene‐co‐vinyl acetate) (EVA)

Organic-inorganic nanocomposites combine unique properties of both the constituents in one material. Among this group of materials, clay based as well as ZnO, TiO2 nanocomposites have been found to have diverse applications. Optoelectronic devices require polymerinorganic systems to meet certain desired properties. Dielectric properties of conventional polymers like poly(ethylene-co-vinyl acetate) (EVA) and polystyrene (PS) may also be tailor tuned with the incorporation of inorganic fillers in very small amounts. Electrical conductivity and surface resistivity of polymer matrices are found to improve with inorganic nanofillers. II-VI semiconductors and their nano materials have attracted material scientists because of their unique optical properties of photoluminescence, UV photodetection and light induced conductivity. Cadmium selenide (CdSe), zinc selenide (ZnSe) and zinc oxide (ZnO) are some of the most promising members of the IIVI semiconductor family, used in light-emitting diodes, nanosensors, non-linear optical (NLO) absorption etc. EVA and PS materials were selected as the matrices in the present study because they are commercially used polymers and have not been the subject of research for opto-electronic properties with semiconductor nanomaterials

Development of novel surface coatings based on acrylic copolymers

The present study describes the preparation of Vinyl acetate-Butyl acrylate copolymer lattices of varying compositions and solid contents by semicontinuous emulsion polymerization method. This copolymer lattices were used as binder to develop a new surface coating formulation. The properties of this surface coating were improved by using nano TiO2 colloidal sol as a pigment. Antimicrobial activity of surface coatings was improved by the addition of carboxymethyl chitosan as biocide. Uniformly dispersed tyre crumb was used to give a mat finish to the coating. The mechanical properties adhesive properties, thermal properties etc. of the coatings are presented in thesis.

Copper Doped Methylene Blue Sensitized Poly(vinyl alcohol)–Acrylamide Films for Stable Diffraction Efficiency

Copper doped methylene blue sensitized poly(vinyl alcohol) (MBPVA)–acrylamide films were fabricated to improve the storage life of recorded gratings. The films were fabricated using gravity settling method and the copper chloride concentration was optimized as 3:18 10 3 mol/l for a dye concentration of 6:2 10 4 mol/l. The gratings recorded on the optimized film constitution could be stored for months with stable diffraction efficiency (24%) without any chemical or thermal fixing techniques. The resolution of the material is found to be unaffected with the addition of copper chloride.

Copper Doped Methylene Blue Sensitized Poly(vinyl alcohol)–Acrylamide Films for Stable Diffraction Efficiency

Copper doped methylene blue sensitized poly(vinyl alcohol) (MBPVA)–acrylamide films were fabricated to improve the storage life of recorded gratings. The films were fabricated using gravity settling method and the copper chloride concentration was optimized as 3:18 10 3 mol/l for a dye concentration of 6:2 10 4 mol/l. The gratings recorded on the optimized film constitution could be stored for months with stable diffraction efficiency (24%) without any chemical or thermal fixing techniques. The resolution of the material is found to be unaffected with the addition of copper chloride.

Enhancement of Diffraction Efficiency and Storage Life of Poly (Vinyl Chloride) Based Optical Recording Medium with the Incorporation of an Electron Donor

The differaction efficiency,sensitivity and storage life of Methylene Blue sencitized poly (vinyl chloride) film was improved by the addition of an electron donor in the matrix. The addition of pyridine enhanced the diffraction efficiency by two times and storage life of the gratings was increased to 2-3 days.

Optimization of pH and Direct Imaging Conditions of Complexed Methylene Blue Sensitized Poly(vinyl chloride) Films

Significant results of our experimental investigations on the dependence of pH on real time transmission characteristics on recording media fabricated by doping PVC with complexed methylene blue are presented. The optimum pH value for faster bleaching was found to be 4×5. In typical applications, the illumination from one side, normal to the surface of this material, initiates a chemical sequence that records the incident light pattern in the polymer. Thus direct imaging can be successfully done on this sample. The recorded letters were very legible with good contrast and no scattering centres. Diffraction efficiency measurements were also carried out on this material.

Copper Doped Methylene Blue Sensitized Poly(vinyl alcohol)–Acrylamide Filmsfor Stable Diffraction Efficiency

Copper doped methylene blue sensitized poly(vinyl alcohol) (MBPVA)–acrylamide films were fabricated to improve the storage life of recorded gratings. The films were fabricated using gravity settling method and the copper chloride concentration was optimized as 3:18 10 3 mol/l for a dye concentration of 6:2 10 4 mol/l. The gratings recorded on the optimized film constitution could be stored for months with stable diffraction efficiency (24%) without any chemical or thermal fixing techniques. The resolution of the material is found to be unaffected with the addition of copper chloride.

Enhancement of Diffraction Efficiency and Storage Life of Poly (Vinyl Chloride) Based Optical Recording Medium with the Incorporation of an Electron Donor

The differaction efficiency,sensitivity and storage life of Methylene blue sensitized poly(vinyl chloride) film was improved by the addition of an electron donor in the matrix. The addition of pyridine enhanced the diffraction efficiency by two times and storage life of the gratings was increased to 2-3 days.

Optimization of pH and Direct Imaging Conditions of Complexed Methylene Blue Sensitized Poly(vinyl chloride) Films

Significant results of our experimental investigations on the dependence of pH on real time transmission characteristics on recording media fabricated by doping PVC with complexed methylene blue are presented. The optimum pH value for faster bleaching was found to be 4×5. In typical applications, the illumination from one side, normal to the surface of this material, initiates a chemical sequence that records the incident light pattern in the polymer. Thus direct imaging can be successfully done on this sample. The recorded letters were very legible with good contrast and no scattering centres. Diffraction efficiency measurements were also carried out on this material.