NIR to UV absorption spectra and the optical constants of phthalocyanines in glassy medium

Optical absorption studies of phthalocyanines (Pc-s) in borate glass matrix have been reported for the first time. Measurements have been done corresponding to photon energies between 1.1 and 6.2 eV for free base, manganese, iron, nickel, molybdenum, cobalt and copper phthalocyanines. Several new discrete transitions are observed in the UV–vis region of the spectra in addition to a strong continuum component of absorption in the IR region. Values of some of the important optical constants viz. absorption coefficient (α), molar extinction coefficient (ε), absorption cross-section (σa), band width (Δλ), electric dipole strength (q2) and oscillator strength (f) for the relevant electronic transitions are also presented. All the data reported for Pc-s in the new matrix have been compared with those corresponding to solution, vapor and thin film media.

Comparative effectiveness of solar disinfection using small-scale batch reactors with reflective, absorptive and transmissive rear surfaces

This study investigated the enhancement of solar disinfection using custom-made batch reactors with reflective (foil-backed) or absorptive (black-backed) rear surfaces, under a range of weather conditions in India. Plate counts of Escherichia coli ATCC11775 were made under aerobic conditions and under conditions where reactive oxygen species (ROS) were neutralised, i.e. in growth medium supplemented with 0.05% w/v sodium pyruvate plus incubation under anaerobic conditions. While the addition of either an absorptive or a reflective backing enhanced reactor performance under strong sunlight, the reflective reactor was the only system to show consistent enhancement under low sunlight, where the process was slowest. Counts performed under ROS-neutralised conditions were slightly higher than those in air, indicating that a fraction of the cells become sub-lethally injured during exposure to sunlight to the extent that they were unable to grow aerobically. However, the influence of this phenomenon on the dynamics of inactivation was relatively small

Enhanced UV emission from ZnO nanoflowers synthesized by the hydrothermal process

ZnO nanoflowers were synthesized by the hydrothermal process at an optimized growth temperature of 200 ◦C and a growth/reaction time of 3 h. As-prepared ZnO nanoflowers were characterized by x-ray diffraction, scanning electron microscopy, UV–visible and Raman spectroscopy. X-ray diffraction and Raman studies reveal that the as-synthesized flower-like ZnO nanostructures are highly crystalline with a hexagonal wurtzite phase preferentially oriented along the (1 0 1 1) plane. The average length (234–347 nm) and diameter (77–106 nm) of the nanorods constituting the flower-like structure are estimated using scanning electron microscopy studies. The band gap of ZnO nanoflowers is estimated as 3.23 eV, the lowering of band gap is attributed to the flower-like surface morphology and microstructure of ZnO. Room temperature photoluminescence spectrum shows a strong UV emission peak at 392 nm, with a suppressed visible emission related to the defect states, indicating the defect free formation of ZnO nanoflowers that can be potentially used for UV light-emitting devices. The suppressed Raman bands at 541 and 583 cm−1 related to defect states in ZnO confirms that the ZnO nanoflowers here obtained have a reduced presence of defects

Boosted UV emission at 349 nm from mesoporous ZnS

Relatively oxygen-free mesoporous cubic ZnS particles were synthesised via a facile solvo-hydrothermal route using a water–acetonitrile combination. Boosted UV emission at 349 nm is observed from the ZnS prepared by the solvo-hydrothermal route. The increased intensity of this UV emission is attributed to activation of whispering gallery modes of almost elliptical microstructures made of porous nanostructures.