Characterization of Short Nylon-6 Fiber/Acrylonitrile Butadiene Rubber Composite by Thermogravimetry

The thermal degradation of short nylon-6 fiber reinforced acrylonitrile butadiene rubber (NBR) composites with and without epoxy-based bonding agent has been studied by thermogravimetric analysis (TGA). It was found that the onset of degradation shifted from 330.5 to 336.1°C in the presence of short nylon fiber, the optimum fiber loading being 20 phr. The maximum rate of degradation of the composites was lower than that of the unfilled rubber compound, and it decreased with increase in fiber concentration. The presence of epoxy resin-based bonding agent in the virgin elastomer and the composites improved the thermal stability. Results of kinetic studies showed that the degradation of NBR and the short nylon fiber reinforced composites followed first-order kinetics.

Thermal degradation of short polyester fiber polyurethane elastomer composite

The thermal degradation of short polyester fiber reinforced polyurethane composites with and without different bonding agents has been studied by thermogravimetric analysis . It was found that degradation of the polyurethane takes place in two steps and that of the composites takes place in three steps. With the incorporation of 30 phr of fiber in the matrix , the onset of degradation was shifted from 230 to 238 ° C. The presence of bonding agents in the virgin elastomer and the composite gave an improved thermal stability . Results of kinetic studies showed that the degradation of polyurethane and the reinforced composites with and without bonding agents follows first -order reaction kinetics

Acid activated montmorillonite: an efficient immobilization support for improving reusability, storage stability and operational stability of enzymes

Three enzymes, α-amylase, glucoamylase and invertase, were immobilized on acid activated montmorillonite K 10 via two independent techniques, adsorption and covalent binding. The immobilized enzymes were characterized by XRD, N2 adsorption measurements and 27Al MAS-NMR spectroscopy. The XRD patterns showed that all enzymes were intercalated into the clay inter-layer space. The entire protein backbone was situated at the periphery of the clay matrix. Intercalation occurred through the side chains of the amino acid residues. A decrease in surface area and pore volume upon immobilization supported this observation. The extent of intercalation was greater for the covalently bound systems. NMR data showed that tetrahedral Al species were involved during enzyme adsorption whereas octahedral Al was involved during covalent binding. The immobilized enzymes demonstrated enhanced storage stability. While the free enzymes lost all activity within a period of 10 days, the immobilized forms retained appreciable activity even after 30 days of storage. Reusability also improved upon immobilization. Here again, covalently bound enzymes exhibited better characteristics than their adsorbed counterparts. The immobilized enzymes could be successfully used continuously in the packed bed reactor for about 96 hours without much loss in activity. Immobilized glucoamylase demonstrated the best results.

Studies on the littoral processes in relation to stability of beaches around Cchin

The coastal and nearshore areas have played vital role in the trade and economic development of coastal nations since ancient times. In recent years, the demands for utilization of these areas have increased for purposes of navigation, setting up of offshore structures for oil industry, exploitation of the available fishery and mineral resources, and to provide recreational facilities along the coast as a part of the coastal zone management. It is in this context the studies on nearshore processes receive greater priorities. Stability of beaches is controlled by the interaction of various physical parameters such as winds, waves, currents, tides and the nature and constituents of the beaches. The results of studies carried out by the author on the dynamical effects of these environmental parameters on the shoreline processes along the beaches around Cochin are presented in this thesis. The section of the coast investigated is about 57 km of shore from Azhikode to Anthakaranazhi situated on the central Kerala coast. Four regions namely Narakkal, Malipuram, Fort Cochin and Anthakaranazhi were chosen for detailed study