Studies on the Surface Properties and Catalytic Activity of Metal Chromites on Thermal Decomposition of Ammonium Perchlorate

Department of Applied Chemistry, Cochin University of Science and Technology

Sol-Gel Nanocrystalline Catalytic Titania Powders and Functional Coatings

In the present work Titania bulk powders and coatings were prepared by subjecting titanium isopropoxide solution to a controlled hydrolysis-condensation process. The powders were characterized using techniques such as FTIR for their chemical interactions, TG-DTA for the thermal decomposition features, XRD for the phase assemblage, BET specific surface area analysis for the textural features. The study discusses the preparation methods and the characterization techniques employed and a detailed discussion on the physico-chemical characterization of the prepared systems. The influence of dopants and leaching on the physico-chemical properties as well as their influence on photo activity is also included. The structural/functional coatings of different Titania compositions includes in this study. Coatings on pre-treated glass surfaces with the best compositions prepared showed 90 % transmittance in the visible region.

Preparation and characterisation of "Y-Fe203 as tape recording material

Optimum conditions for the preparation of tape recording quality Y-Fe20 s by the thermal decomposition of ferrous oxalate dihydrate have been established. Formation of the intermediate F%O~ which is most important in forming Y-FezO 3 takes place only in the presence of water vapour. Various stages of decomposition have been characterised by DTA, TG, DTG, and x-ray powder diffraction. The method for the preparation of acicular "Y-Fe208 that matches very well with the commercial tape recording material has been developed

Development of pure and doped gamma ferric oxide

Optimum conditions and experimental details for the formation of v-Fe203 from goethite have been worked out. In another method, a cheap complexing medium of starch was employed for precipitating acicular ferrous oxalate, which on decomposition in nitrogen and subsequent oxidation yielded acicular y-Fe203. On the basis of thermal decomposition in dry and moist nitrogen, DTA, XRD, GC and thermodynamic arguments, the mechanism of decomposition was elucidated. New materials obtained by doping ~'-Fe203 with 1-16 atomic percent magnesium, cobalt, nickel and copper, were synthesised and characterized

Synthesis and characterization of γ-Fe2O3—a magnetic tape material

Acicular FeC~O4-2H20 was precipitated from glycerol and starch media. Thermal decomposition of this oxalate in dry and moist nitrogen yielded primarily FeO and Fe 3Oa respectively. Characterization was attempted through DTA, TG, x-ray diffraction, TEM and magnetization studies. It was found that the oxalate can be completely decomposed to FeaO~ in moist nitrogen (PH~o ,"-" 35 torr) at 775 K and then oxidised by dry air to acicular "/-Fe~Oa at 575 K. The resulting material has saturation magnetization (,-,., 70 emu/g), coercive field (N300 Oe) and squareness ratio ( ,~, 0-60-0-65), which values art comparable with those of the commercial samples

Analytical Characterization, Thermal And Ftir Studies Of Urinary Calculi

Urolithiasis is identified to be a major urological disorder affecting people all over the world irrespective of their age, sex and race. Urinary stone samples resected from the urinary bladders of two patients belonging to tropical region, Kollam District of Kerala State, India are investigated by using XRD,SEM, EDAX, TGA, DSC and FTIR to understand its chemical structure. Uric acid shows exothermic peak around 432°C is due to the decomposition with the evolution of CO and cracking of the remaining products. Results of analytical studies reveal that samples under investigation consist mainly in uric acid and hydrated uric acid. Hydrogen bonding exists in hydrated uric acid samples