Photoacoustic signal saturation and optical limiting in C70-toluene solution

Pulsed photoacoustic studies in solutions of C70 in toluene are made using the 532-nm radiation from a frequency-doubled Nd:YAG laser. It is found that contrary to expectation, there is no photoacoustic (PA) signal enhancement in the power-limiting range of laser fluences. Instead, the PA signal tends to saturate during optical power-limiting phenomenon. This could be due to the enhanced optical absorption from the photoexcited state and hence the depletion of the ground-state population. PA measurements also ruled out the possibility of multiphoton absorption in the C70 solution. We demonstrate that the nonlinear absorption leading to optical limiting is mainly due to reverse saturable absorption.

Near fifty percent sodium substituted lanthanum manganites—A potential magnetic refrigerant for room temperature applications

Nearly half of lanthanum sites in lanthanum manganites were substituted with monovalent ion-sodium and the compound possessed distorted orthorhombic structure. Ferromagnetic ordering at 300K and the magnetic isotherms at different temperature ranges were analyzed for estimating magnetic entropy variation. Magnetic entropy change of 1.5 J kg 1 K 1 was observed near 300 K. An appreciable magnetocaloric effect was also observed for a wide range of temperatures near 300K for small magnetic field variation. Heat capacity was measured for temperatures lower than 300K and the adiabatic temperature change increases with increase in temperature with a maximum of 0.62K at 280 K