CuInS2/In2S3 Cells using a Cost-effective Technique: Significance of Precursor Ratios on Cell Parameters

Thin film solar cells having structure CuInS2/In2S3 were fabricated using chemical spray pyrolysis (CSP) technique over ITO coated glass. Top electrode was silver film (area 0.05 cm2). Cu/In ratio and S/Cu in the precursor solution for CuInS2 were fixed as 1.2 and 5 respectively. In/S ratio in the precursor solution for In2S3 was fixed as 1.2/8. An efficiency of 0.6% (fill factor -37.6%) was obtained. Cu diffusion to the In2S3 layer, which deteriorates junction properties, is inevitable in CuInS2/In2S3 cell. So to decrease this effect and to ensure a Cu-free In2S3 layer at the top of the cell, Cu/In ratio was reduced to 1. Then a remarkable increase in short circuit current density was occurred from 3 mA/cm2 to 14.8 mA/cm2 and an efficiency of 2.13% was achieved. Also when In/S ratio was altered to 1.2/12, the short circuit current density increased to 17.8 mA/cm2 with an improved fill factor of 32% and efficiency remaining as 2%. Thus Cu/In and In/S ratios in the precursor solutions play a crucial role in determining the cell parameters

Prospects of sprayed CZTS thin film solar cells from the perspective of material characterization and device performance

This thesis is devoted to the development of a relatively new, rapidly developing quaternary semiconducting material (viz., Cu2ZnSnS4) used for photovoltaic applications. This semiconductor, commonly known as CZTS, is closely related to a family of materials that have been used for solar cell applications. It is a compound semiconductor made of copper, zinc, tin and sulfur, which are sufficiently abundant elements; none of them is harmful to the environment even at large scale usage. Aim of this study is to fabricate CZTS solar cells through chemical spray pyrolysis (CSP) technique. At first the influence of various spray parameters like substrate temperature, spray rate, precursor ratio etc. on the opto-electronic properties of CZTS films will be studied in detail. Then the fabrication of CZTS/In2S3 hetero junctions and various ways to improve the performance parameters will be tried