Characterization of low dielectric constant polyaniline thin film synthesized by ac plasma polymerization technique

Polyaniline thin films were prepared by ac plasma polymerization technique. Capacitance, dielectric loss, dielectric constant and ac conductivity of these films were investigated in the frequency range from 100 Hz to 1MHz and in the temperature range from 300 to 373 K. Capacitance and dielectric loss decreased with frequency and increased with temperature. This type of behaviour was found to be in good agreement with an existing model. The ac conductivity σ(ω) was found to vary as ωs with the index s 1. Annealing of polyaniline thin films in high vacuum at 373K for 1 h was found to reduce the dielectric loss. FTIR studies reveal that the aromatic ring is retained in the polyaniline thin films, which enhances the thermal stability of the polymer films

Large enhanced dielectric permittivity in polyaniline passivated core-shell nano magnetic iron oxide by plasma polymerization

Commercial samples of Magnetite with size ranging from 25–30nm were coated with polyaniline by using radio frequency plasma polymerization to achieve a core shell structure of magnetic nanoparticle (core)–Polyaniline (shell). High resolution transmission electron microscopy images confirm the core shell architecture of polyaniline coated iron oxide. The dielectric properties of the material were studied before and after plasma treatment. The polymer coated magnetite particles exhibited a large dielectric permittivity with respect to uncoated samples. The dielectric behavior was modeled using a Maxwell–Wagner capacitor model. A plausible mechanism for the enhancement of dielectric permittivity is proposed

Contact potential induced enhancement of magnetization in polyaniline coated nanomagnetic iron oxides by plasma polymerization

The present work derives motivation from the so called surface/interfacial magnetism in core shell structures and commercial samples of Fe3O4 and c Fe2O3 with sizes ranging from 20 to 30 nm were coated with polyaniline using plasma polymerization and studied. The High Resolution Transmission Electron Microscopy images indicate a core shell structure after polyaniline coating and exhibited an increase in saturation magnetization by 2 emu/g. For confirmation, plasma polymerization was performed on maghemite nanoparticles which also exhibited an increase in saturation magnetization. This enhanced magnetization is rather surprising and the reason is found to be an interfacial phenomenon resulting from a contact potential.