Effect of chlorine concentration on the spectral characteristics of electroluminescence in ZnS: Cu: Cl phosphor

ZnS: Cu: Cl phosphor prepared under a vacuum firing process is found to give blue electroluminescence with emission peak at 460 nm which remams unaltered with the frequency of the excitation voltage. Addition of excess chlorine in the phosphor gives blue, green and red emission at 460, 520 and 640 run. The intensity of the blue band decreases and It fmally disappears as chlorine concentration is increased. A scheme involving three energy levels attributed to Cu2+, Cu+ and Cl- centres in Zns explains the experimental results completely.

Fluorescenec Emission of SrS:Eu2+ Phosphor-Energy Level Splitting of Eu2+

A method of preparation of strontium sulphide phosphors doped with europium is given. Nitrogen laser excited fluorescence emission spectra of these phosphors in the visible region are recorded. A band with line structure in the region 350-430 nm and a new broad band at 460 nm are observed. The splitting pattern for the 6p levels of Eu 2+ are given.

Laser induced fluorescence of BaS: Sm phosphor and energy level splitting of Sm3+ ion

Fluorescence of BaS: Sm phosphor has been studied using a pulsed Nitrogen laser (337.1 nm) as the excitation source. The spectrum consists of a broad band in the region 540–660nm superposed by the characteristic Sm3+ lines. Energy level splitting pattern of Sm3+ due to crystal field effects has been calculated and relevent field parameters are evaluated. Analysis shows that Sm3+ takes up Ba2+ substitutional sites.

On the luminescence characteristics of cerium and copper doped barium sulphide phosphor

Photoluminescence, thermoluminescence and phosphorescence studies of cerium and copper doped BaS phosphors are attempted. Cu+ centres in BaS lattice activate red emission while Ce3+ sensitize the blue emission. Results are explained on the basis of superposition theory involving monomolecular kinetics. In Randall and Wilkins model, the decay and TL studies are found to corelate each other.

Effect of Substrate Temperature on the Structural and Luminescent Characteristics of RF-Magnetron-Sputtered ZnGa2O4:Dy3+ Thin Films

ZnGa2O4:Dy3+ phosphor thin films were deposited on quartz substrates by radio frequency rf magnetron sputtering and the effect of substrate temperature on its structural and luminescent properties was investigated. Polycrystalline film could be deposited even at room temperature. The crystalline behavior, Zn/Ga ratio, and surface morphology of the films were found to be highly sensitive to substrate temperature. Under UV illumination, the as-deposited films at and above 300°C gave white luminescence even without any postdeposition treatments. The photoluminescent PL emission can be attributed to the combined effect of multicolor emissions from the single luminescence center Dy3+ via host-sensitization. Maximum PL emission intensity was observed for the film deposited at 600°C, and the CIE chromaticity coordinates of the emission were determined to be x,y = 0.34, 0.31 .

Electrical and Optical Properties of Znga2o4 Thin Films Deposited By Pulsed Laser Deposition

ZnGa2O4 spinel is a promising new UV transparent electronic conductor. Enhancing the electrical conductivity of this potential oxide phosphor can make it a promising transparent conducting oxide. In this paper, we have investigated the effects of processing and doping on the conductivity of semiconducting ZnGa2O4, particularly thin films. Crystalline zinc gallate thin films have been deposited on fused quartz substrates employing the pulsed laser deposition (PLD) technique at room temperature for an oxygen partial pressure of 0.1 Pa (0.001mbar). The films were found to be UV transparent, the band gap of which shifted to 4.75eV on hydrogen annealing. The band gap of the oxygen stoichiometric bulk powder samples (4.55eV) determined from diffuse reflection spectrum (DRS) shifted to 4.81eV on reduction in a hydrogen atmosphere. The electrical conductivity improved when Sn was incorporated into the ZnGa2O4 spinel. The conductivity of ZnGa2O4:Sn thin films was further improved on reduction.

A study of the white electroluminescence in ZnS:Cu,Pr,Cl phosphors

The method of preparation of ZnS phosphors doped with praseodymium and copper is given. The electroluminescence (EL) spectrum of ZnS:Pr,Cl has two broad bands at 470 and 570 nm. ZnS:Cu,Pr,Cl gives white emission with spectral peaks at 470, 520, 570 and 640 nm. The EL spectra of both types of phosphor exhibit a conspicuous colour shift as the frequency of the excitation voltage is varied. Detailed investigations show that the relative intensities of spectral peaks are strongly dependent on the frequency of the excitation voltage. The colour shift is explained on the basis of the Schon-Klasens model.

Luminescence studies of strontium sulphide based phosphors for display applications

This thesis has focused on the synthesis and analysis of some important phosphors (nano, bulk and thin film) for display applications. ACTFEL device with SrS:Cu as active layer was also fabricated.Three bulk phosphors: SrS:Cu,CI; SrS:Dy,Cl; and SrS:Dy,Cu,Cl were synthesized and their structural, optical and electrical properties were investigated. Special emphasis was given to, the analysis of the role of defects and charge compensating centers, on the structural changes of the host and hence the luminance. A new model describing the sensitizing behaviour of Cu in SrS:Dy,Cu,Cl two component phosphor was introduced. It was also found that addition of NH4CI as flux in SrS:Cu caused tremendous improvement in the structural and luminescence properties.A novel technique for ACTFEL phosphor deposition at low temperature was introduced. Polycrystalline films of SrS:Cu,F were synthesized at low temperature by concomitant evaporation of host and dopant by electron beam evaporation and thermal evaporatin methods.Copper doped strontium sulphide nanophosphor was synthesized for the first time. Improvement in the luminescence properties was observed in the nanophosphor with respect to it' s bulk counterpart.

Effect of Ce3+ Ion on the X-Ray Induced Fluorescence Emission from CaS

The effect of Ce3+ on the fluorescence emission from CaS:Ce3+ phosphor is studied using X-ray excitation. Apart from the emission in the visible region, the phosphor also shows fluorescence emission in the ultraviolet region. Variation in wavelengths and intensities of these emissions due to change in dopant concentration is also analysed.

Fabrication and the study of zinc sulphide based electroluminescent devices

This thesis contains the author's work in preparing efficient EL phosphors, the details of fabrication of low voltage operated thin film EL (TFEL) devices and DC TFEL devices. Some of the important work presented here are related to the white light emitting ZnS:Cu,Pr,Cl phosphor which can be colour tuned by changing the excitation frequency, observation of energy transfer from Cu/Ag ions to rare earth ions in ZnS:(Cu/Ag), RE,Cl phosphors, development of TFEL device which can be operated below 50V, optimization of the device parameters for long life, high brightness in terms of the active and insulating layer thicknesses, observation of dependence of threshold voltage for the onset of emission on frequency of excitation when a novel dielectric Eu2O3 film was used as insulator and the devices with multicolor emission using ZnS doped with rare earth as active layer. Characterization based on other devices based on ZnS:Sm, ZnS:Pr, ZnS:Dy and their emission characteristics are also illustrated

Studies on electroluminescence using Powder and thin film devices

The subject of electroluminescence has currently acquired great importance because of its potential applications in display systems of a wide variety. A large number of scientists working in commercial, governmental as well as academic institutions all over the world are at present engaged in the intense effort to develop new and efficient phosphor materials and electroluminescent devices. This thesis presents the work carried out by the author in this field during the past few years. The studies discussed in this thesis are mostly confined to the development of some new phosphor materials, their uses in powder and thin film electroluminescent devices and to their electrical and spectral characteristics. Care has been taken to bring' out the physics involved in all the above aspects of the phenomenon

Synthesis and Photoluminescence Properties of Novel Red Phosphors for White Light Emitting Diode Applications

Several series of Eu3+ based red emitting phosphor materials were synthesized using solid state reaction route and their properties were characterized. The present studies primarily investigated the photoluminescence properties of Eu3+ in a family of closely related host structure with a general formula Ln3MO7. The results presented in the previous chapters throws light to a basic understanding of the structure, phase formation and the photoluminescence properties of these compounds and their co-relations. The variation in the Eu3+ luminescence properties with different M cations was studied in Gd3-xMO7 (M = Nb, Sb, Ta) system.More ordering in the host lattice and more uniform distribution of Eu3+ ions resulting in the increased emission properties were observed in tantalate system.Influence of various lanthanide ion (Lu, Y, Gd, La) substitutions on the Eu3+ photoluminescence properties in Ln3MO7 host structures was also studied. The difference in emission profiles with different Ln ions demonstrated the influence of long range ordering, coordination of cations and ligand polarizability in the emission probabilities, intensity and quantum efficiency of these phosphor materials. Better luminescence of almost equally competing intensities from all the 4f transitions of Eu3+ was noticed for La3TaO7 system. Photoluminescence properties were further improved in La3TaO7 : Eu3+ phosphors by the incorporation of Ba2+ ions in La3+ site. New red phosphor materials Gd2-xGaTaO7 : xEu3+ exhibiting intense red emissions under UV excitation were prepared. Optimum doping level of Eu3+ in these different host lattices were experimentally determined. Some of the prepared samples exhibited higher emission intensities than the standard Y2O3 : Eu3+ red phosphors. In the present studies, Eu3+ acts as a structural probe determining the coordination and symmetry of the atoms in the host lattice. Results from the photoluminescence studies combined with the powder XRD and Raman spectroscopy investigations helped in the determination of the correct crystal structures and phase formation of the prepared compounds. Thus the controversy regarding the space groups of these compounds could be solved to a great extent. The variation in the space groups with different cation substitutions were discussed. There was only limited understanding regarding the various influential parameters of the photoluminescence properties of phosphor materials. From the given studies, the dependence of photoluminescence properties on the crystal structure and ordering of the host lattice, site symmetries, polarizability of the ions, distortions around the activator ion, uniformity in the activator distribution, concentration of the activator ion etc. were explained. Although the presented work does not directly evidence any application, the materials developed in the studies can be used for lighting applications together with other components for LED lighting. All the prepared samples were well excitable under near UV radiation. La3TaO7 : 0.15Eu3+ phosphor with high efficiency and intense orange red emissions can be used as a potential red component for the realization of white light with better color rendering properties. Gd2GaTaO7 : Eu3+, Bi2+ red phosphors give good color purity matching to NTSC standards of red. Some of these compounds exhibited higher emission intensities than the standard Y2O3 : Eu3+ red phosphors. However thermal stability and electrical output using these compounds should be studied further before applications. Based on the studies in the closely related Ln3MO7 structures, some ideas on selecting better host lattice for improved luminescence properties could be drawn. Analyzing the CTB position and the number of emission splits, a general understanding on the doping sites can be obtained. These results could be helpful for phosphor designs in other host systems also, for enhanced emission intensity and efficiency.