Synthesis, Characterization and Catalytic Activity of Nanocrystalline Ceria Modified With Zirconia

The use of catalysts in chemical and refining processes has increased rapidly since 1945, when oil began to replace coal as the most important industrial raw material. Catalysis has a major impact on the quality of human life as well as economic development. The demand for catalysts is still increasing since catalysis is looked up as a solution to eliminate or replace polluting processes. Metal oxides represent one of the most important and widely employed classes of solid catalysts. Much effort has been spent in the preparation, characterization and application of metal oxides. Recently, great interest has been devoted to the cerium dioxide (CeO2) containing materials due to their broad range of applications in various fields, ranging from catalysis to ceramics, fuel cell technologies, gas sensors, solid state electrolytes, ceramic biomaterials, etc., in addition to the classical application of CeO2 as an additive in the so-called three way catalysts (TWC) for automotive exhaust treatment. Moreover, it can promote water gas shift and steam reforming reactions, favours catalytic activity at the interfacial metal-support sites. The solid solutions of ceria with Group IV transitional-metals deserve particular attention for their applicability in various technologically important catalytic processes. Mesoporous CeO2−ZrO2 solid solutions have been reported to be employed in various reactions which include CO oxidation, soot oxidation, water-gas shift reaction, and so on. Inspired by the unique and promising characteristics of ceria based mixed oxides and solid solutions for various applications, we have selected ceria-zirconia oxides for our studies. The focus of the work is the synthesis and investigation of the structural and catalytic properties of modified and pure ceria-zirconia mixed oxide.

Sol-Gel Nanocrystalline Catalytic Titania Powders and Functional Coatings

In the present work Titania bulk powders and coatings were prepared by subjecting titanium isopropoxide solution to a controlled hydrolysis-condensation process. The powders were characterized using techniques such as FTIR for their chemical interactions, TG-DTA for the thermal decomposition features, XRD for the phase assemblage, BET specific surface area analysis for the textural features. The study discusses the preparation methods and the characterization techniques employed and a detailed discussion on the physico-chemical characterization of the prepared systems. The influence of dopants and leaching on the physico-chemical properties as well as their influence on photo activity is also included. The structural/functional coatings of different Titania compositions includes in this study. Coatings on pre-treated glass surfaces with the best compositions prepared showed 90 % transmittance in the visible region.

Modified mesoporous MCM-41 as hosts for photochromic spirobenzopyrans

The influence of the chemical composition and silylation of mesoporous MCM-41 materials on the photochromic behaviour of adsorbed spiropyran (BIPS) and 6-nitrospiropyran was studied. Upon incorporation, the spiropyrans underwent ring opening to form either zwitterionic merocyanine or its corresponding O-protonated form. In all silica MCM-41 or in the MCM-41 containing aluminium, the O-protonated merocyanine was predominantly formed. In the case of MCM-41 modified by silylation of the OH groups, a mixture of zwitterionic merocyanine and spiropyran was present. The photochromic response was studied by means of steady-state irradiation and by laser flash photolysis. Steady-state irradiation (λ > 450 nm) of the solid samples gives rise in all cases to an intensity decrease of the absorption bands corresponding to either the protonated or the unprotonated merocyanine form (reverse photochromism). In contrast, laser flash photolysis at 308 nm of spiropyrans supported on silylated MCM-41 allows observation of the photochemical ring opening of residual spiropyran to the corresponding zwitterionic form (normal photochromism).

Sol-Gel Mesoporous Silica Aerogels and Bio Hybrids for Functional Applications

The thesis covers a systematic investigation on the synthesis of silica aerogels and microspheres with tailored porosity, at ambient conditions by varying the experimental parameters as well as using organic templates. Organically modified silica-gelatin and silica-chitosan hybrids were developed for the first time using alkylalkoxysilanes such as MTMS and VTMS. Application of novel silica-biopolymer antiwetting coatings on different substrates such as glass, leather and textile is also demonstrated in the thesis.

Photodegradation of Methylorange over Zirconia Doped TiO2 Using Solar Energy

The heterogeneous photocatalytic degradation of methylorange over TiO2 is studied and is found to be cost effective. Effect of Zirconium metal incorporation over titania system is investigated. Photocatalytic degradation of methylorange using solar radiation is found to be highly economical when compared with the processes using artificial UV radiation, which require substantial electrical power input. The characterization of titania as well as modified zirconium metal doped titania systems are done using XRD, FTIR and EDAX measurements. The catalytic activities of different systems are also compared and is tried to correlate with the crystallite size and presence of dopant metal.

Iron Promoted Sulphated Zirconia Systems as Efficient Catalysts for Phenol Hydroxylation

The present work investigates on the applicability of metal promoted sulphated zirconia catalysts for the hydroxylation of phenol under mild conditions. The percentage conversion and product distribution was highly sensitive towards the reaction parameters like the catalyst composition, reaction temperature, H202/ phenol ratio and the solvent used.

Preparation and characterization of nanocrystalline transition metal-loaded sulfated titania through sol-gel method

Transition metal-loaded (3%) nanocrystalline sulfated titania (ST) powders are prepared using the sol–gel technique. Anatase is found as the active phase in all the samples. Sulfate ion impregnation decreases the crystallite size and stabilizes the anatase phase of TiO2. Acidity of the samples is found to increase by the incorporation of sulfate ion and also by the modification by transition metal ions. All the prepared catalysts are found stable up to 700 °C.

Studies on catalysis by transition metal promoted sulphated zirconia

The present project was a systematic investigation of the physico-chemical properties and catalytic activity of some transition metal promoted sulphated zirconia systems. The characterisation and catalytic activity results were compared with that of pure Zr02 and simple sulphated zirconia systems. Sulphated zirconia samples were prepared by a controlled impregnation technique. In the case of metal incorporated systems, a single step impregnation was carried out using required amounts of sulphuric acid and metal salt solutions. As a preliminary step, optimisation of calcination temperature and sulphate content was achieved. For further studies, the optimised sulphate loading of 10 ml per gram of hydrous zirconium oxide and a calcination temperature of 700°C was employed. Metal incorporation had a positive influence on the physico-chemical properties. Vapour phase cumene conversion served as a test reaction for acidity. Some industrially important reactions like Friedel-Crafts reaction, phenol hydroxylation, nitration, etc. were selected to test the catalytic activity of the prepared systems.

Tuning mesoporous molecular sieve SBA-15 for the immobilization of α-amylase

The present work describes the immobilization of α-amylase over well ordered mesoporous molecular sieve SBA-15 with different pore diameters synthesized by post synthesis treatment (PST) hydrothermally after reaction at 40°C. The materials were characterized by N 2 adsorption–desorption studies, small angle X-ray diffraction, scanning electron microscopy and high resolution transmission electron microscopy. Since α-amylase obtained from Bacillus subtilis has dimensions of 35 × 40 × 70 Å it is expected that the protein have access to the pore of SBA-15 (PST-120°C) with diameter 74 Å. The pore dimension is appropriate to prevent considerable leaching. The rate of adsorption of the enzyme on silica of various pore sizes revealed the influence of morphology, pore diameter, pore volume and pH.

Liquid phase benzoylation of arenes over iron promoted sulphated zirconia

The present work undertakes the preparation and physico-chemical characterisation of iron promoted sulphated zirconia (SZ) with different amounts of iron loading and their application to Friedel-Crafts benzoylation of benzene, toluene and xylene under different experimental conditions, XRD and laser Raman techniques reveal the stabilisation of the tetragonal phase of zirconia and the existence of iron in highly dispersed form as Fe203 on the catalyst surface. The surface acidic properties were determined by ammonia temperature programmed desorption (TPD) and perylene adsorption, The results were supported by the TGA studies after adsorption of pyridine and 2,6-dimethylpyridine (2,6-DMP), Strong Lewis acid sites on the surface, which are evident from TPD and perylene adsorption studies. explain the high catalytic activity of the systems towards benzoylation. The experimental results provide evidence for the truly heterogeneous nature of the reaction. The studies also establish the resistance to deactivation in the metal incorporated sulphated systems.

Influence of sulphate content on the physico-chemical properties and catalytic activity of some sulphated zirconia systems

The present work attempts a systematic examination of the effect of sulphate content on the physico-chemical properties and catalytic activity of sulphated zirconia and iron promoted sulphated zirconia systems. Sulphate content is estimated by EDX analysis. The amount of sulphate incorporated has been found to influence the surface area, crystal structure and the acid strength distribution. Ammonia TPD and adsorption studies using perylene have enabled the determination of surface acidic properties. The results are supported by the thermodesorption studies using pyridine and 2,6-dimethylpyridine. The catalytic activity towards benzoylation reaction has been correlated with the surface acidity of the systems.

Surface properties and catalytic activity of phosphate modified zirconia

Preparation and physico-chemical characterization or phosphate modified zirconia systems and their application to Friedel-Crafts benzylation and benzoylation of toluene have been reported. The influence of transition metals on the surface properties and catalytic activity has also been discussed.

Synthesis, characterization and benzylation activity of nanocrystalline chromia loaded sulfated titania prepared via sol–gel route

Chromia loaded sulfated titania has been synthesized via sol–gel route with different chromia loadings. These catalysts are characterized using conventional techniques such as XRD analysis, FTIR analysis, surface area and pore volume measurements, EDX, SEM and UV–Vis diffuse reflectance spectral analysis. Acidity is measured using spectrophotometric monitoring of adsorption of perylene, thermogravimetric desorption of 2,6-dimethylpyridine and temperature programmed desorption of ammonia. Activity studies are done in the liquid phase. It has been concluded that Lewis acid sites are responsible for the benzylation of arenes with benzyl chloride.

Thermal characterization of nanocrystalline porous CePO4 ceramics

A laser-induced photoacoustic technique was employed to investigate thermal transport through nanocrystalline CePO4 samples prepared via the sol–gel route. Evaluation of thermal diffusivity was carried out using the one-dimensional model of Rosencwaig and Gersho for the reflection configuration of the photoacoustic method. Structural analyses of samples revealed that they are nanoporous in nature, possessing micron-sized grains. Analysis of results shows that thermal diffusivity value varies with sintering temperature. Results are explained in terms of the variation in porosity with sintering temperature and the effects of various scattering mechanisms on the propagation of phonons through the nanoporous ceramic matrix. Further analyses confirm that apart from porosity, grain boundary resistance and interface thermal resistance influence the effective value of thermal diffusivity of the samples under investigation.