Reusable Recording Medium Based on MBPVA and Vinyl Acetate

A new photopolymerizable recording media is introduced based on poly (vinyl alcohol) and vinyl acetate sensitized with methylene blue. It is observed that this MBPVA/VAc system can be reused a number of times without significant decrease in diffraction efficiency. The PVA-VAc ratio was optimized at 2:1. Diffraction efficiency of 6.3% was obtained without any fixing at a dye concentration of 9.3 10 4 mol/l at an exposure of 750 mJ/cm2. The material is attractive on account of its reusability.

Reusable Recording Medium Based on MBPVA and vinyl Acetate

A new photopolymerizable recording media is introduced based on poly (vinyl alcohol) and vinyl acetate sensitized with methylene blue. It is observed that this MBPVA/VAc system can be reused a number of times without significant decrease in diffraction . The PVA-VAc ratio was optimized at 2:1. Diffraction efficiency of 6.3% was obtained without any fixing at a dye concentration of 9.3 10 4 mol/l at an exposure of 750 mJ/cm2. The material is attractive on account of its reusability.

Reusable recording medium based on MBPVA and vinyl acetate

A new photopolymerizable recording media is introduced based on poly (vinyl alcohol) and vinyl acetate sensitized with methylene blue. It is observed that this MBPVA/VAc system can be reused a number of times without significant decrease in diffraction efficiency. The PVA-VAc ratio was optimized at 2:1. Diffraction efcienc4y of 6.3% was obtained without any fixing at a dye concentration of 9.3 x 10- mol/l at an exposure of 750mJ/cm2. The material is attractive on account of its reusability.

Reusable Recording Medium Based on MBPVA and Vinyl Acetate

A new photopolymerizable recording media is introduced based on poly (vinyl alcohol) and vinyl acetate sensitized with methylene blue. It is observed that this MBPVA/VAc system can be reused a number of times without significant decrease in diffraction efficiency. The PVA-VAc ratio was optimized at 2:1. Diffraction efcienc4y of 6.3% was obtained without any fixing at a dye concentration of 9.3 x 10- mol/l at an exposure of 750mJ/cm2. The material is attractive on account of its reusability.

Reusable Recording Medium based on MBPVA and Vinyl Acetate

A new photopolymerizable recording media is introduced based on poly (vinyl alcohol) and vinyl acetate sensitized with methylene blue. It is observed that this MBPVA/VAc system can be reused a number of times without significant decrease in diffraction efficiency. The PVA-VAc ratio was optimized at 2:1. Diffraction efcienc4y of 6.3% was obtained without any fixing at a dye concentration of 9.3 x 10- mol/l at an exposure of 750mJ/cm2. The material is attractive on account of its reusability.

Copper Doped Methylene Blue Sensitized Poly(vinyl alcohol)–Acrylamide Films for Stable Diffraction Efficiency

Copper doped methylene blue sensitized poly(vinyl alcohol) (MBPVA)–acrylamide films were fabricated to improve the storage life of recorded gratings. The films were fabricated using gravity settling method and the copper chloride concentration was optimized as 3:18 10 3 mol/l for a dye concentration of 6:2 10 4 mol/l. The gratings recorded on the optimized film constitution could be stored for months with stable diffraction efficiency (24%) without any chemical or thermal fixing techniques. The resolution of the material is found to be unaffected with the addition of copper chloride.

Copper Doped Methylene Blue Sensitized Poly(vinyl alcohol)–Acrylamide Films for Stable Diffraction Efficiency

Copper doped methylene blue sensitized poly(vinyl alcohol) (MBPVA)–acrylamide films were fabricated to improve the storage life of recorded gratings. The films were fabricated using gravity settling method and the copper chloride concentration was optimized as 3:18 10 3 mol/l for a dye concentration of 6:2 10 4 mol/l. The gratings recorded on the optimized film constitution could be stored for months with stable diffraction efficiency (24%) without any chemical or thermal fixing techniques. The resolution of the material is found to be unaffected with the addition of copper chloride.

Methylene Blue Doped Polymers: efficient Media for Optical Recording

Polymer materials find application in optical storage technology, namely in the development of high information density and fast access type memories. A new polymer blend of methylene blue sensitized polyvinyl alcohol (PVA) and polyacrylic acid (PAA) in methanol is prepared and characterized and its comparison with methylene blue sensitized PVA in methanol and complexed methylene blue sensitized polyvinyl chloride (CMBPVC) is presented. The optical absorption spectra of the thin films of these polymers showed a strong and broad absorption region at 670-650 nm, matching the wavelength of the laser used. A very slow recovery of the dye on irradiation was observed when a 7:3 blend of polyvinyl alcohol/polyacrylic acid at a pHof 3.8 and a sensitizer concentration of 4.67 10 5 g/ml were used. A diffraction efficiency of up to 20% was observed for the MBPVA/alcohol system and an energetic sensitivity of 2000 mJ/cm2 was obtained in the photosensitive films with a spatial frequency of 588 lines/mm.

Copper Doped Methylene Blue Sensitized Poly(vinyl alcohol)–Acrylamide Filmsfor Stable Diffraction Efficiency

Copper doped methylene blue sensitized poly(vinyl alcohol) (MBPVA)–acrylamide films were fabricated to improve the storage life of recorded gratings. The films were fabricated using gravity settling method and the copper chloride concentration was optimized as 3:18 10 3 mol/l for a dye concentration of 6:2 10 4 mol/l. The gratings recorded on the optimized film constitution could be stored for months with stable diffraction efficiency (24%) without any chemical or thermal fixing techniques. The resolution of the material is found to be unaffected with the addition of copper chloride.

Methylene Blue Doped Polymers:Efficient Media for Optical Recording

Polymer materials find application in optical storage technology, namely in the development of high information density and fast access type memories. A new polymer blend of methylene blue sensitized polyvinyl alcohol (PVA) and polyacrylic acid (PAA) in methanol is prepared and characterized and its comparison with methylene blue sensitized PVA in methanol and complexed methylene blue sensitized polyvinyl chloride (CMBPVC) is presented. The optical absorption spectra of the thin films of these polymers showed a strong and broad absorption region at 670-650 nm, matching the wavelength of the laser used. A very slow recovery of the dye on irradiation was observed when a 7:3 blend of polyvinyl alcohol/polyacrylic acid at a pHof 3.8 and a sensitizer concentration of 4.67 10 5 g/ml were used. A diffraction efficiency of up to 20% was observed for the MBPVA/alcohol system and an energetic sensitivity of 2000 mJ/cm2 was obtained in the photosensitive films with a spatial frequency of 588 lines/mm.

A new metal ion doped panchromatic photopolymer for holographic applications

This thesis has discussed the development of a new metal ion doped panchromatic photopolymer for various holographic applications. High-quality panchromatic holographic recording material with high diffraction efficiency, high photosensitivity and high spatial resolution is one of the key factors for the successful recording of true colour holograms. The capability of the developed material for multicolour holography can be investigated.In the present work, multiplexing studies were carried out using He-Ne laser (632.8 nm). Multiplexing can be done using low wavelength lasers like Ar+ ion (488 nm) and frequency doubled Nd: YAG (532 nm) lasers, so as to increase the storage capacity. The photopolymer film studied had a thickness of only 130 Cm. Films with high thickness (~500 Cm) is highly essential for competitive holographic memories . Hence films with high thickness can be fabricated and efforts can be made to record more holograms or gratings in the material.In the present study, attempts were made to record data page in silver doped MBPVA/AA photopolymer film. Image of a checkerboard pattern was recorded in the film, which could be reconstructed with good image fidelity. Efforts can be made to determine the bit error rate (BER) which provides a quantitative measure of the image quality of the reconstructed image . Multiple holographic data pages can also be recorded in the material making use of different multiplexing techniques.Holographic optical elements (HOEs) are widely used in optical sensors, optical information processing, fibre optics, optical scanners and solar concentrators . The suitability of the developed film for recording holographic optical elements like lenses, beam splitters and filters can be studied.The suitability of a reflection hologram recorded in acrylamide based photopolymer for visual indication of environmental humidity is reported . Studies can be done to optimize the film composition for recording of reflection holograms.An improvement in the spatial resolution of PVA/acrylamide based photopolymer by using a low molecular-weight poly (vinyl alcohol) binder was recently reported . Effect of the molecular weight of the binder matrix on the holographic properties of the developed photopolymer system can be investigated.Incorporation of nanoparticles into photopolymer system is reported to enhance the resolution and improve the dimensional stability of the system . Hence efforts can be made to incorporate silver nanoparticles into the photopolymer and its influence on the holographic properties can be studied.This thesis was a small venture towards the realization of a big goal, a competent holographic recording material with excellent properties for practical holographic applications. As a result of the present research, we could successfully develop an efficient panchromatic photopolymer system and could demonstrate its suitability for recording transmission holograms and holographic data page. The developed photopolymer system is expected to have significant applications in the fields of true-color display holography, wavelength multiplexing holographic storage, and holographic optical elements. Highly concentrated and determined effort has yet to be put forth for this expectation to become a reality.