Selective N-monomethylation of aniline over Zn1-xNixFe2O4 (x=0, 0.2, 0.5, 0.8 and 1) type systems

The reaction of aniline with methanol was carried out over Zn1-xNixFe2O4 (x= 0, 0.2, 0.5, 0.8 and 1) type systems in a fixed-bed down-flow reactor. It was observed that systems possessing low ``x'' values are highly selective and active for mono N-alkylation of aniline leading to N-methyl aniline. Selectivity for N-methyl aniline over ZnFe2O4 was more than 99% under the optimized reaction conditions. Even at methanol to aniline molar ratio of 2, the yield of N-methyl aniline was nearly 55.5%, whereas its yield exceeded 67% at the molar ratio of 7. The Lewis acid sites of the catalysts are mainly responsible for the good catalytic performance. Cation distribution in the spinel lattice influences their acido-basic properties, and hence, these factors have been considered as helpful to evaluate the activity and stability of the systems.

Liquid phase benzoylation of arenes over iron promoted sulphated zirconia

The present work undertakes the preparation and physico-chemical characterisation of iron promoted sulphated zirconia (SZ) with different amounts of iron loading and their application to Friedel-Crafts benzoylation of benzene, toluene and xylene under different experimental conditions, XRD and laser Raman techniques reveal the stabilisation of the tetragonal phase of zirconia and the existence of iron in highly dispersed form as Fe203 on the catalyst surface. The surface acidic properties were determined by ammonia temperature programmed desorption (TPD) and perylene adsorption, The results were supported by the TGA studies after adsorption of pyridine and 2,6-dimethylpyridine (2,6-DMP), Strong Lewis acid sites on the surface, which are evident from TPD and perylene adsorption studies. explain the high catalytic activity of the systems towards benzoylation. The experimental results provide evidence for the truly heterogeneous nature of the reaction. The studies also establish the resistance to deactivation in the metal incorporated sulphated systems.