Microwave dielectric properties of (1-x)CaTi03-xSm(Mg1 /2Ti1/2)03 [0. 1 _

The microwave dielectric properties of (I -x)CaTiO3-xSm(Mg1/2Tit,2)O3(0.1 <-x< 1.0) have been investigated. The system forms a solid solution throughout the entire compositional range. The dielectric constant decreases from 86 to 25 as x varies from 0.1 to 1.0. The Qxf varies non-linearly and increases for composition with x> 0.6. The nonmonotonic variation with composition x is more pronounced in Tt than in er. The microwave dielectric properties indicate the possibility of a phase transformation for x between 0.4 and 0.5

Annealing inducedlowcoercivity,nanocrystallineCo–Fe–Si thin films exhibitinginversecosine angular variation

Co–Fe–Si based films exhibit high magnetic moments and are highly sought after for applications like soft under layer sinper pendicular recording mediatomagneto-electro-mechanical sensor applications.In this workt he effect of annealing on s tructural,morphologicaland magnetic propertiesofco–Fe–Si thin films wasinvestigated.compositional analysis using x-rayphotoelectron spectroscopy and secondary ion massspectroscopyrevealedanativeoxidesurfacelayerconsistingofoxidesofco,feandsionthe surface. The morphology of theas deposited films shows mound like structures conformingtothe Volmer–Webergrowthmodel.Nanocrystallisationofamorphous films upon annealing was observed by glancing anglex-raydiffraction and transmission electron microscopy.Theevolutionofmagnetic properties with annealing is explained using the Herzermodel.Vibrating sample magnetometry measurements carried out at various angles from01 to 901 to the applied magnetic field were employed to study the angula rvariation of coercivity.The angular variation fits the modified Kondorsky model. Interestingly,the coercivity evolution with annealing deduced frommagneto-opticalKerreffectstudies indicates areversetrendcomparedtomagetisationobservedinthebulk.Thiscanbeattributedtoa domain wallpinningatnativeoxidelayeronthesurfaceofthin films. Theevolutionofsurfacemagnetic properties iscorrelatedwithmorphologyevolutionprobedusingatomicforcemicroscopy.The morphology aswellasthepresenceofthenativeoxidelayerdictatesthesurfacemagneticproperties and this is corroborated by the apparent difference in the bulk and surface magnetic properties