New High Permittivity and Low Loss Ceramics in the Bao-Ti02- Nb205 Composition

New dielectric ceramics with formula BaTi3Nb4, O„ and Ba6Til4Nbz039 have been prepared and characterized. BaTi3Nba017 was densified to 92% of TD after firing at 1310 oC for 4 h. However, Ba6Ti 1 4Nb2O39 fired under optimized conditions (1260 ` C for 4 h) showed only 85% TD together with secondary phase. The crystal system of both of the compositions is orthorhombic

Effect of chlorine concentration on the spectral characteristics of electroluminescence in ZnS: Cu: Cl phosphor

ZnS: Cu: Cl phosphor prepared under a vacuum firing process is found to give blue electroluminescence with emission peak at 460 nm which remams unaltered with the frequency of the excitation voltage. Addition of excess chlorine in the phosphor gives blue, green and red emission at 460, 520 and 640 run. The intensity of the blue band decreases and It fmally disappears as chlorine concentration is increased. A scheme involving three energy levels attributed to Cu2+, Cu+ and Cl- centres in Zns explains the experimental results completely.

Finite size effects on the structural and magnetic properties of sol–gel synthesized NiFe2O4 powders

Nanoparticles of nickel ferrite have been synthesized by the sol–gel method and the effect of grain size on its structural and magnetic properties have been studied in detail. X-ray diffraction (XRD) studies revealed that all the samples are single phasic possessing the inverse spinel structure. Grain size of the sol–gel synthesized powders has been determined from the XRD data and the strain graph. A grain size of 9 nm was observed for the as prepared powders of NiFe2O4 obtained through the sol–gel method. It was also observed that strain was induced during the firing process. Magnetization measurements have been carried out on all the samples prepared in the present series. It was found that the specific magnetization of the nanosized NiFe2O4 powders was lower than that of the corresponding coarse-grained counterparts and decreased with a decrease in grain size. The coercivity of the sol–gel synthesized NiFe2O4 nanoparticles attained a maximum value when the grain size was 15nm and then decreased as the grain size was increased further.