Raman spectra of polymethyl methacrylate optical fibres excited by a 532 nm diode pumped solid state laser

Polymethyl methacrylate (PMMA) optical fibres are fabricated by a preform drawing process. The Raman spectra of PMMA fibres are recorded using a diode pumped solid state laser emitting at 532 nm and a CCD-spectrograph in the 400–3800 cm−1 range. The variation of the Raman intensity with the length of the optical fibre is studied. Investigations are carried out on the variation of FWHM of the Raman peak at 2957 cm−1 with the length of the optical fibre and pump power. The differential scattering cross section and gain coefficient of the Raman peak at 2957 cm−1 in PMMA are calculated in relation to that of toluene.

Raman spectra of polymethyl methacrylate optical fibres excited by a 532 nm diode pumped solid state laser

Polymethyl methacrylate (PMMA) optical fibres are fabricated by a preform drawing process. The Raman spectra of PMMA fibres are recorded using a diode pumped solid state laser emitting at 532 nm and a CCD-spectrograph in the 400–3800 cm−1 range. The variation of the Raman intensity with the length of the optical fibre is studied. Investigations are carried out on the variation of FWHM of the Raman peak at 2957 cm−1 with the length of the optical fibre and pump power. The differential scattering cross section and gain coefficient of the Raman peak at 2957 cm−1 in PMMA are calculated in relation to that of toluene

Fabrication and Characterisation of Dye Doped Polymer Optical Fibres With Different Refractive Index Profiles for Photonic Applications

International School of Photonics, Cohin University of Science and Technology

Studies on pulp propogation in single mode optical fibres

Studies on pulse propagation in single mode optical fibers have attracted interest from a wide area of science and technology as they have laid down the foundation for an in-depth understanding of the underlying physical principles, especially in the field of optical telecommunications. The foremost among them is discovery of the optical soliton which is considered to be one of the most significant events of the twentieth century owing to its fantastic ability to propagate undistorted over long distances and to remain unaflected after collision with each other. To exploit the important propertia of optical solitons, innovative mathematical models which take into account proper physical properties of the single mode optical fibers demand special attention. This thesis contains a theoretical analysis of the studies on soliton pulse propagation in single mode optical fibers.

Evanescent Wave Fibre Optic Sensors for Trace Analysis of Fe3+ in Water

In this communication, we discuss the details of fabricating an off-line fibre optic sensor (FOS) based on evanescent wave absorption for detecting trace amounts of Fe3+ in water. Two types of FOS are developed; one type uses the unclad portion of a multimode silica fibre as the sensing region whereas the other employs the microbent portion of a multimode plastic fibre as the sensing region. Sensing is performed by measuring the absorption of the evanescent wave in a reagent medium surrounding the sensing region. To evaluate the relative merits of the two types of FOS in Fe3+ sensing, a comparative study of the sensors is made, which reveals the superiority of the latter in many respects, such as smaller sensing length, use of a double detection scheme (for detecting both core and cladding modes) and higher sensitivity of cladding mode detection at an intermediate range of concentration along with the added advantage that plastic fibres are inexpensive. A detection limit of 1 ppb is observed in both types of fibre and the range of detection can be as large as 1 ppb–50 ppm. All the measurements are carried out using a LabVIEW set-up.

Evanescent wave fibre optic sensors for trace analysis of Fe3+ in water

In this communication, we discuss the details of fabricating an off-line fibre optic sensor (FOS) based on evanescent wave absorption for detecting trace amounts of Fe3+ in water. Two types of FOS are developed; one type uses the unclad portion of a multimode silica fibre as the sensing region whereas the other employs the microbent portion of a multimode plastic fibre as the sensing region. Sensing is performed by measuring the absorption of the evanescent wave in a reagent medium surrounding the sensing region. To evaluate the relative merits of the two types of FOS in Fe3+ sensing, a comparative study of the sensors is made, which reveals the superiority of the latter in many respects, such as smaller sensing length, use of a double detection scheme (for detecting both core and cladding modes) and higher sensitivity of cladding mode detection at an intermediate range of concentration along with the added advantage that plastic fibres are inexpensive. A detection limit of 1 ppb is observed in both types of fibre and the range of detection can be as large as 1 ppb–50 ppm. All the measurements are carried out using a LabVIEW set-up.

Design, Fabrication and Characterization of Passive and Active Polymer Photonic Devices

The rapid developments in fields such as fibre optic communication engineering and integrated optical electronics have expanded the interest and have increased the expectations about guided wave optics, in which optical waveguides and optical fibres play a central role. The technology of guided wave photonics now plays a role in generating information (guided-wave sensors) and processing information (spectral analysis, analog-to-digital conversion and other optical communication schemes) in addition to its original application of transmitting information (fibre optic communication). Passive and active polymer devices have generated much research interest recently because of the versatility of the fabrication techniques and the potential applications in two important areas – short distant communication network and special functionality optical devices such as amplifiers, switches and sensors. Polymer optical waveguides and fibres are often designed to have large cores with 10-1000 micrometer diameter to facilitate easy connection and splicing. Large diameter polymer optical fibres being less fragile and vastly easier to work with than glass fibres, are attractive in sensing applications. Sensors using commercial plastic optical fibres are based on ideas already used in silica glass sensors, but exploiting the flexible and cost effective nature of the plastic optical fibre for harsh environments and throw-away sensors. In the field of Photonics, considerable attention is centering on the use of polymer waveguides and fibres, as they have a great potential to create all-optical devices. By attaching organic dyes to the polymer system we can incorporate a variety of optical functions. Organic dye doped polymer waveguides and fibres are potential candidates for solid state gain media. High power and high gain optical amplification in organic dye-doped polymer waveguide amplifier is possible due to extremely large emission cross sections of dyes. Also, an extensive choice of organic dye dopants is possible resulting in amplification covering a wide range in the visible region.

Evanescent wave fibre optic sensors for trace analysis of Fe3+ in water

In this communication, we discuss the details of fabricating an off-line fibre optic sensor (FOS) based on evanescent wave absorption for detecting trace amounts of Fe3+ in water. Two types of FOS are developed; one type uses the unclad portion of a multimode silica fibre as the sensing region whereas the other employs the microbent portion of a multimode plastic fibre as the sensing region. Sensing is performed by measuring the absorption of the evanescent wave in a reagent medium surrounding the sensing region. To evaluate the relative merits of the two types of FOS in Fe3+ sensing, a comparative study of the sensors is made, which reveals the superiority of the latter in many respects, such as smaller sensing length, use of a double detection scheme (for detecting both core and cladding modes) and higher sensitivity of cladding mode detection at an intermediate range of concentration along with the added advantage that plastic fibres are inexpensive. A detection limit of 1 ppb is observed in both types of fibre and the range of detection can be as large as 1 ppb–50 ppm. All the measurements are carried out using a LabVIEW set-up.

Evanescent wave fibre optic sensors for trace analysis of Fe3+ in water

In this communication, we discuss the details of fabricating an off-line fibre optic sensor (FOS) based on evanescent wave absorption for detecting trace amounts of Fe3+ in water. Two types of FOS are developed; one type uses the unclad portion of a multimode silica fibre as the sensing region whereas the other employs the microbent portion of a multimode plastic fibre as the sensing region. Sensing is performed by measuring the absorption of the evanescent wave in a reagent medium surrounding the sensing region. To evaluate the relative merits of the two types of FOS in Fe3+ sensing, a comparative study of the sensors is made, which reveals the superiority of the latter in many respects, such as smaller sensing length, use of a double detection scheme (for detecting both core and cladding modes) and higher sensitivity of cladding mode detection at an intermediate range of concentration along with the added advantage that plastic fibres are inexpensive. A detection limit of 1 ppb is observed in both types of fibre and the range of detection can be as large as 1 ppb–50 ppm. All the measurements are carried out using a LabVIEW set-up.

Tailored Ion Imprinted Polymer Materials for the Preconcentrative Separation of Noble Metals

Tailored ion imprinted polymer materials for the preconcentrative separation of noble metals. This study deals with the synthesis, separation,characterization and analytical application of the noble metals especially palladium and platinum. Platinum group metals(PGM) are currently receiving world wide attention. This group include Palladium(Pt),rhodium(Rh), ruthenium(Ru), iridium(Ir) and osmium(Os).PGM are used as catalysts for a wide variety of hydrogenation, oxidation, isomerization,cyclization,dehydrogenation and dehalogenation reactions.The corrosion resistance of PGM enables them to use in jewellery,electrical and glass industries,extrusion of synthetic fibres,manufacture of laboratory utensils,dental and medical devices. This study clearly establishes selective recovery of platinum from other noble and transition elements.

Swelling behaviour of isora/natural rubber composites in oils used in automobiles

Natural rubber/isora fibre composites were cured at various temperatures. The solvent swelling characteristics of natural rubber composites containing both untreated and alkali treated fibres were investigated in aromatic and aliphatic solvents like toluene, and n-hexane. The diffusion experiments were conducted by the sorption gravimetric method. The restrictions on elastomer swelling exerted by isora fibre as well as the anisotropy of swelling of the composite have been confirmed by this study. Composite cured at 100°C shows the lowest percentage swelling. The uptake of aromatic solvent is higher than that of aliphatic solvent for the composites cured at all temperatures. The effect of fibre loading on the swelling behaviour of the composite was also investigated in oils like petrol, diesel, lubricating oil etc. The % swelling index and swelling coefficient of the composite were found to decrease with increase in fibre loading. This is due to the increased hindrance exerted by the fibres at higher fibre loadings and also due to the good fibre-rubber interactions. Maximum uptake of solvent was observed with petrol followed by diesel and then lubricating oil. The presence of bonding agent in the composites restrict the swelling considerably due to the strong interfacial adhesion. At a fixed fibre loading, the alkali treated fibre composite showed lower percentage swelling compared to the untreated one.

Self adhesion of short Kevlar fibre -thermoplastic polyurethane composite

The self adhesion behaviour of thermoplastic polyurethane (TPU) in itself and its composite with short Kevlar fibre with respect to contact time, temperature, pressure, and fibre loading has been studied. The adhesion strength showed two linear increments of different slopes with respect to the square root of time: with temperature and pressure of contact, the adhesion strength was improved. The maximum strength was obtained with 20 phr of short fibre in only one of the mating substrates in the peel test sample. The duration for wetting and diffusion was shifted to longer time intervals with fibres loaded in both the substrates.

Thermal degradation of short kevlar fibre thermoplastic polyurethane composite

The thermal degradation of short kevlar fibre-thermoplastic polyurethane (TPU) composites has been studied by Thermogravimetric Analysis (TGA) and Differential Scanning Calorimetry (DSC). TGA showed that the thermal degradation of TPU takes place in two steps with peak maxima (T1max and T2ma,) at 383°C and 448°C, respectively. In the presence of 10-40 phr of short kevlar fibres, T1_ and T2max were shifted to lower temperatures. The temperature of onset of degradation was increased from 245 to 255°C at 40 parts per hundred rubber (phr) fibre loading. Kinetic studies showed that the degradation of TPU and kevlar-TPU composite follows first-order reaction kinetics. The DSC study showed that there is an improvement in thermal stability of TPU in the presence of 20 phr of short kevlar fibres.

Short Isora Fibre Reinforced Natural Rubber Composites

The present study deals with the short isora fibre reinforced natural rubber composites. In recent years there has been a tremendous advancement in the field of science and technology of short fibre reinforced polymer composites. The low density, high strength, high stiffness to weight ratio, excellent durability and design flexibility are the primary reasons for their use in many diversified fields such as air crafts, automobiles, marine industry etc. Compared to the various natural and synthetic fibres used as reinforcement for elastomer composites isora fibre is superior in many aspects. `Isora' is a natural lignocellulosic fibre which is easily available in South India especially in Kerala. The fibre is separated from the bark of the Helicteres isora plant by retting process. This fibre has excellent mechanical properties and is easily amenable to physical and chemical modifications. The study shows that composites with poor interfacial bonding tend to dissipate more energy than that with to interfacial bonding. The mechanical loss also can be related to interfacial bonding. The effect of chemical treatment of isora fibre on damping was also studied. Both in the low and high temperature region which indicates that this composite posseses low damping and hence good interfacial bonding characteristics. Hence these composites are better candidates for high damping applications. Composites with longitudinally oriented fibres showed high storage modulus than transversely oriented ones due to the effective stress transfer between fibre and matrix.

Studies on the Development and Control of Desiccation cracks in compacted clay liner soils

The present study aimed at critically looking at the current practice of the installation of compacted clay liner using bentonite enhanced sand (BES). The application of bentonite is currently the most accepted practice for lining purposes. The ideal bentonite sand combination, which satisfies the liner requirements is 20% bentonite and 80% sand, was selected as one of the liner materials for the investigation of development of desiccation cracks. Locally available sundried marine clay and its combination with bentonite were also included in the study. The desiccation tests on liner materials were conducted for wet/dry cycles to simulate the seasonal variations. Digital image processing techniques were used to measure the crack intensity factor (CIF), a useful and effective parameter for quantification of desiccation cracking. The repeatability of the tests could be well established, as the variation in CIF values of identical samples had a very narrow range of 0 to 2%. The studies on the development of desiccation cracks showed that the CIF of bentonite enhanced sand mixture (BES) was 18.09%, 39.75% and 21.22% for the first, second and third cycles respectively, while it was only 9.83%, 7.52% and 4.58% respectively for sun dried marine clay (SMC). Thus the locally available, alternate liner material suggested, viz SMC, is far superior to BES, when subjected to alternate wet/dry cycles. Further, the improvement of these liner materials when amended with randomly distributed fibre reinforcements was also investigated. Three types of fibres ,namely nylon fibre, polypropylene monofilament and polypropylene fibre mesh were used for the study of fibre amended BES and SMC.The influence of these amendments on the properties of the above liner materials is also studied. The results showed that there is definite improvement in the properties of the liner materials when it is reinforced with discrete random fibres. The study also proved that the desiccation cracks could be controlled with the help of fibre reinforcement.