Preparation, Characterisation And Microwave Dielectric Properties Of Anbn-1o3n (N=5,6,8) Type Perovskite Compounds

The present study on the preparation , characterization and microwave dielectric properties of AnBn-1O3n (N=5,6,8) type perovskite compounds. The explored ceramics show dielectric constant between 11 and 54,quality factor in the range 2400 to 88900 GHz and Tf in the range -73 to +231ppm/0C.Most of the investigated cation deficient hexagonal perovskites show intermediate dielectric constant with high quality factors. This study gives a general introduction about material, scientific and technological aspects of DRs.Three important ,€r ,Q and Tf, used for the DR characterization are described. The relationship of the above parameters with the fundamental material characteristics is discussed. Different modes are excited when a DR is excited with suitable microwave spectrum of frequencies .A description of analytical determination of frequencies and construction of mode charts used for sample design and mode identification are also discussed. In this study several ceramics are developed for DR purposes, very little attention has been paid to grow the single crystals. It might be due to the fact that the difficulties and time involved in the growth of single crystals, big enough to function as microwave resonators make them expensive .However single crystals of these materials may have very high Q values. It is also possible that a better understanding of the dielectric properties in relation to the structure can be arrived using single crystals. Hence one of the future directions of dielectric resonator research should be to grow good quality single crystals of the above materials.

Studies on the Toughening of Epoxy Resins

This thesis aims to develop new toughened systems for epoxy resin via physical and chemical modifications. Initially the synthesis of DGEBA was carried out and the properties compared with that of the commercial sample. Subsequently the modifier resins to be employed were synthesized. The synthesized resin were characterized by spectroscopic method (FTIR and H NMR), epoxide equivalent and gel permeation chromatography. Chemical modification involves the incorporation of thermoset resins such a phenolics, epoxy novolacs, cardanol epoxides and unsaturated polyester into the epoxy resin by reactive belnding. The mechanical and thermal properties of the blends were studied. In the physical modification route, elastomers, maleated elastomers and functional elastomers were dispersed as micro-sized rubber phase into the continuous epoxy phase by a solution blending technique as against the conventional mechanical blending technique. The effect of matrix toughening on the properties of glass reinforced composites and the effect of fillers on the properties of commercial epoxy resin were also investigated. The blends were characterized by thermo gravimetric analysis, differential scanning calorimetry, dynamic mechanical analysis, scanning electron microscopy and mechanical property measurements. Among the thermoset blends, substantial toughening was observed in the case of epoxy phenolic novolacs especially epoxy para cresol novolac (ECN). In the case of elastomer blending , the toughest blends were obtained in the case of maleic anhydride grafted NBR. Among functional elastomers the best results were obtained with CTBN. Studies on filled and glass reinforced composites employing modified epoxy as matrix revealed an overall improvement in mechanical properties

A Novel Accelerator Combination for the Low Temperature Curing of Silica-Filled NBR Compounds

Zinc salts of ethyl, isopropyl, and butyl xanthates were prepared in the laboratory. The effect of these xanthates in combination with zinc diethyldithiocarbamate (ZDC) on the vulcanization of silica-filled NBR compounds has been studied at different temperatures. The cure times of these compounds were compared with that of NBR compounds containing tetramethylthiuram disulphide/dibenzthiazyl disulphide. The rubber compounds with the xanthates and ZDC were cured at various temperatures from 60 to 150°C. The sheets were molded and properties such as tensile strength, tear strength, crosslink density, elongation at break, compression set, abrasion resistance, flex resistance, heat buildup, etc. were evaluated. The properties showed that zinc salt of xanthate/ZDC combination has a positive synergistic effect on the cure rate and mechanical properties of NBR compounds.

Synergism of Xanthate/Dithiocarbamate Accelerator in Carbon Black Filled NR Compounds

Zinc salts of ethyl, isopropyl and butyl xanthates were prepared in the laboratory. The effect of these xanthates with zinc diethyldithiocarbamate (ZDC) on the vulcanization of HAF filled NR compound has been studied at different temperatures. The rubber compounds with the three xanthate accelerators and ZDC were cured at various temperatures from 60°C to 150°C. The sheets were moulded and properties such as tensile strength , tear strength , cross-link density, elongation -at-break, compression set, heat build up, abrasion resistance, flex resistance , etc. were evaluated . The properties showed that zinc xanthate/ZDC accelerator combination has a positive synergistic effect on the mechanical properties of NR compounds. The curing of HAF filled NR compound containing zinc xanthate /ZDC is slightly slower than the curing of the corresponding gum compounds . It is observed that, by gradually increasing the amount of the accelerator, the cure time of black filled NR compound can be made equal to that of the gum compou

Use of Amine Terminated Liquid Natural Rubber as a Plasticiser in Filled NR andNBR Compounds

Amine Terminated Liquid Natural Rubber (ATNR) was used as a plasticiser in filled NR and NBR compounds replacing oil/DOP. The scorch time and cure time were found to be lowered when ATNR was used as the plasticiser. ATNR was found to improve the mechanical properties like tensile strength, tear strength and modulus of the vulcanizates . The ageing resistance of the vulcanizates containing ATNR was superior compared to the vulcanizates containing oil/DOP.

Studies on Conductive Silicone Rubber Compounds

ABSTRACT: The electrical conductivity of silicone rubber vulcanizates containing carbon blacks [e.g., acetylene black, lamp black, and ISAF (N-234) black] were investigated. The change in electrical conductivity with varying amounts of carbon blacks and the temperature dependence was measured. The mechanical properties like tensile strength, tear strength, elongation at break, hardness, etc., of the vulcanizates were determined. A comparative study of the electrical conductivity of the composites revealed that the electrical conductivity of the composites made with acetylene black was higher than that of the composites made of other blacks.

Studies on the Dipping Characteristics of RVNRL and NRLatex Compounds

ABSTRACT: The dipping characteristics of radiation-vulcanized natural rubber latex and natural rubber latex compounds were investigated with a lab-model semiautomatic dipping machine. The effect of the variation of the speed of immersion and withdrawal, dwell time, compound viscosity, and concentration of coagulant on the thickness of the latex deposit was investigated. The results of the study show that the deposit thickness depends on the withdrawal speed of the former, the concentration of the coagulant, dwell times, and the viscosity of the latex compounds

Rubber Seed Oil: A Multipurpose Additive in NR and SBR Compounds

ABSTRACT: Rubber seed oil was used as a multipurpose ingredient in natural rubber (NR) and styrene butadiene rubber (SBR) compounds. The study shows that the oil, when substituted for conventional plasticiser, imparts excellent mechanical properties to NR and SBR vulcanizates. Further, it also improves aging resistance, reduces cure time, increases abrasion resistance and flex resistance, and reduces blooming.

A Study on the Use of Castor Oil as Plasticizer in Natural Rubber Compounds

Mechanical properties and thermal degradation of natural rubber compounds containing castor oil were studied to evaluate its suitability as plasticizer. Naphthenic oil was used as a reference plasticizer. The cure time was marginally lower in the case of castor oil mixes, probably due to the presence offree fatty acids in it. The tear strength and modulus were better in the case of mixes containing castor oil, while most of the other mechanical properties were comparable to the mixes containing naphthenic oil. The heat build up and compression set were higher than that of the naphthenic oil mixes. Thermal studies showed an increase of 8 °C in the temperature of initiation of degradation and an increase of 6 °C in the temperature at which the peak rate of degradation occurred. The peak rate of degradation was comparable to that of the reference compound

A Study on the Use of Coconut Oil as Plasticiser in Natural Rubber Compounds

Mechanical properties and thermal degradation characteristics of natural rubber compounds captaining coconut oil were compared with that of a control compound containing naphthenic oil. Cure time was marginally lower in the case of coconut oil mixes, probably due to the presence of free fatty acids. Tensile strength , tear strength, resilience and abrasion resistance were better than the naphthenic oil-based compounds . Compression set and hardness were marginally inferior The coconut oil mixes had a crosslink density comparable to that of the reference compound. Thermal studies showed that the temperature of initiation of degradation was increased by 10°C and the temperature at which the peak rate of degradation occured was increased by 7°C. The peak rate of degradation was compa rable to the control compound.

Rheological Characteristics of Short Nylon -6 Fiber Reinforced Styrene Butadiene Rubber Containing Epoxy Resin as Bonding Agent

The rheological characteristics of short Nylon-6 fiber-reinforced Styrene Butadiene rubber (SBR) in the presence of epoxy resin-based bonding agent were studied with respect to the effect of shear rate, fiber concentration , and temperature on shear viscosity and die swell using a capillary rheonzeter. All the composites containing bonding agent showed a pseudoplastic nature, which decreased with increasing temperature. Shear viscosity was increased in the presence of fibers. The temperature sensitivity of the SBR matrices was reduced on introduction of fibers. The temperature sensitivity of the melts was found to be lower at higher shear rates. Die swell was reduced in the presence of fibers. Relative viscosity of the composites increased with shear rate. In the presence of epoxy resin bonding agent the temperature sensitivity of the mixes increased. Die swell was larger in the presence of bonding agent.