Selective N-monomethylation of aniline over Zn1-xNixFe2O4 (x=0, 0.2, 0.5, 0.8 and 1) type systems

The reaction of aniline with methanol was carried out over Zn1-xNixFe2O4 (x= 0, 0.2, 0.5, 0.8 and 1) type systems in a fixed-bed down-flow reactor. It was observed that systems possessing low ``x'' values are highly selective and active for mono N-alkylation of aniline leading to N-methyl aniline. Selectivity for N-methyl aniline over ZnFe2O4 was more than 99% under the optimized reaction conditions. Even at methanol to aniline molar ratio of 2, the yield of N-methyl aniline was nearly 55.5%, whereas its yield exceeded 67% at the molar ratio of 7. The Lewis acid sites of the catalysts are mainly responsible for the good catalytic performance. Cation distribution in the spinel lattice influences their acido-basic properties, and hence, these factors have been considered as helpful to evaluate the activity and stability of the systems.

Selective N-monomethylation of aniline using Zn1-x CoxFe2O4( x=0, 0.2, 0.5, 0.8 and 1.0)type systems

A series of ferrites having the general formula Zn1-xCoxFe2O4 (x=0, 0.2, 0.5, 0.8 and 1.0)were prepared by soft chemical route. The materials were characterized by adopting various physico-chemical methods. The reaction of aniline with methanol was studied in a fixed-bed reactor system as a potential source for the production of various methyl anilines. It was observed that systems possessing low ‘ x’ values are highly selective and active for N-monoalkylation of aniline leading to N-methylaniline. Reaction parameters were properly varied to optimize the reaction conditions for obtaining N-methylaniline selectively and in better yield. Among the systems Zn0.8Co0.2Fe2O4 is remarkable due to its very high activity and excellent stability. Under the optimized conditions N-methylaniline selectivity exceeded 98%. Even at a methanol to aniline molar ratio of 2, the yield of N-methylaniline was nearly 50%, whereas its yield exceeded 71% at the molar ratio of 5. ZnFe2O4, though executed better conversion than Zn0.8Co0.2Fe2O4 in the initial period of the run, deactivates quickly as the reaction proceeds. The Lewis acidity of the catalysts is mainly responsible for the good performance. Cation distribution in the spinel lattice influences their acido-basic properties and, hence, these factors have been considered as helpful parameters to evaluate the activity of the systems.

Selective alkylation of aniline to N-methyl aniline using chromium manganese ferrospinels

Various compositions of chromium manganese ferrospinels were tested as catalysts for the vapour phase alkylation of aniline with methanol. The samples were prepared by room temperature co-precipitation technique and characterized by various physico-chemical methods. The acidity–basicity determination revealed that the samples possess greater amount of basic sites than acidic sites. All the ferrite samples proved to be selective and active for N-monoalkylation of aniline leading to N-methyl aniline; Cr0.6Mn0.4Fe2O4, Cr0.8Mn0.2Fe2O4 and CrFe2O4 exhibited cent percent selectivity for N-methyl aniline. Neither C-alkylated products nor any other side products were detected for all catalyst samples. The catalytic activity of the samples studied in this reaction is related to their acid–base properties and also on the cation distribution. Under the optimized reaction conditions all the systems showed constant activity for a long duration.

Catalysis By Ferrites And Cobaltites For The Alkylation And Oxidation Of Organic Compounds

Catalysis is a very important process from an industrial point of view since the production of most industrially important chemicals involves catalysis.Solid acid catalysts are appealing since the nature of acid sites is known and their chemical behavior in acid catalyzed reactions can be rationalized by means of existing theories and models. Mixed oxides crystallizing in spinel structure are of special interest because the spinel lattice imparts extra stability to the catalyst under various reaction conditions so that theses systems have sustained activities for longer periods. The thesis entitled" Catalysis By Ferrites And Cobaltites For The Alkylation And Oxidation Of Organic Compounds " presents the preparation ,characterization ,and activity studies of the prepared spinels were modified by incorporating other ions and by changing the stoichiometry.The prepared spinels exhibiting better catalytic activity towards the studied reactions with good product selectivity.Acid-base properties and cation distribution of the spinels were found to control the catalytic activity.

Impact of zinc substitution on the structural and magnetic properties of chemically derived nanosized manganese zinc mixed ferrites

Mn1-xZnxFe2O4 nanoparticles (x=0-1) were synthesized by wet chemical co-precipitation techniques. X-ray diffraction, transmission electron microscopy and high-resolution transmission electron microscopy were effectively utilized to investigate the different structural parameters. The elemental analysis was conducted using energy-dispersive spectrum and inductively coupled plasma analysis. The magnetic properties such as magnetization and coercivity were measured using vibrating sample magnetometer. The observed magnetization values of the nanoparticles were found to be lower compared to the bulk counterpart. The magnetization showed a gradual decrease with zinc substitution except for a small increase from x=0.2 to 0.3. The Curie temperature was found to be enhanced in the case of ferrites in the nanoregime. The variation in lattice constant, reduced magnetization values, variation of magnetization with zinc substitution, the presence of a net magnetic moment for the zinc ferrite and the enhancement in Curie temperature in Mn1-xZnxFe2O4 all provide evidence to the existence of a metastable cation distribution together with possible surface effects at the nanoregime.

On the magnetic properties of ultra-Þne zinc ferrites

Zinc ferrite belongs to the class of normal spinels where it is assumed to have a cation distribution of Zn2`(Fe3`)2(O2~)4, and it is purported to be showing zero net magnetisation. However, there have been recent reports suggesting that zinc ferrite exhibits anomaly in its magnetisation. Zinc ferrite samples have been prepared by two di¤erent routes and have been analysed using low energy ion scattering, Mo¬ ssbauer spectroscopy and magnetic measurements. The results indicate that zinc occupies octahedral sites, contrary to the earlier belief that zinc occupies only the tetrahedral sites in a normal spinel. The amount of zinc on the B site increases with decrease in particle size. The LEIS results together with the Mo¬ ssbauer results and the magnetic measurements lead to the conclusion that zinc occupies the B site and the magnetisation exhibited by ultraÞne particles of zinc is due to short range ordering