Synthesis, Characterisation and Properties of (Ba1-xSrx) (Nd1/2Nb1/2 ) 03 Ceramics for Application as Dielectric Resonators in Microwave Circuits

The (Ba1-x Srx) (Nd1/2, Nb1/2) O3 ceramics have been prepared by the conventional ceramic route for different values of x. Addition of a small amount of CeO2(1 wt%) as a sintering aid increased the density of the samples. The structure and microstructure of the sintered samples are studied by X-ray diffraction and SEM methods. The dielectric properties of the samples are measured in the microwave frequency region as a function of composition. The dielectric constant decreases as x increases. The coefficient of thermal variation of resonant frequency decreases as the Sr content increases and goes to the negative side. The dielectric properties of (Ba1-x Srx) (Nd1/2, Nb1/2) O3 are in the range suitable for application as dielectric resonators in microwave circuits

Ba(Tb1/2Nb1/2)03: A New Ceramic Microwave Dielectric Resonator

A new microwave dielectric resonator Ba(Tb1/2Nb1/2)03 has been prepared and characterized in the microwave frequency region. 1 wt% CeO2 is used as additive to reduce the sintering temperature. The sintered samples were characterized by XRD, SEM and Raman spectroscopic methods. Microwave DR properties such as er, Q factor and temperature-coefficient of resonant frequency (Ti) have been measured using a HP 8510 B Network Analyzer. Cylindrical DRs of Ba(Tb1/2Nbi/2)03 showed high Er (~ 37), high Q (~3,200) and low Tf (~10 ppm /°C) at 4 GHz and hence are useful for practical applications

Microwave dielectric properties of (1-x)CaTi03-xSm(Mg1 /2Ti1/2)03 [0. 1 _

The microwave dielectric properties of (I -x)CaTiO3-xSm(Mg1/2Tit,2)O3(0.1 <-x< 1.0) have been investigated. The system forms a solid solution throughout the entire compositional range. The dielectric constant decreases from 86 to 25 as x varies from 0.1 to 1.0. The Qxf varies non-linearly and increases for composition with x> 0.6. The nonmonotonic variation with composition x is more pronounced in Tt than in er. The microwave dielectric properties indicate the possibility of a phase transformation for x between 0.4 and 0.5

Microwave Dielectric Properties of Ba(Mg1/3Ta(2-2x)/3Wx/3Tix/3) 03 Ceramics

microwave dielectric properties of ceramics based on Ba(Mgv3Ta(2-2x)t3W,t3Tixt3)O3 is investigated as a function of x. The 15 densification as well as dielectric properties deteriorate with increase in the substitution levels of (Ti 1,3W113)333 + at (Ta213)3.33+ site 16 in Ba(Mg113Ta213)03. The rt is approaching zero between x = 0.1 and 0.15 in Ba(Mg it3Ta(2-2,,.)t3W,it3Ti,Tt3)O3 where quality factor is 17 reasonably good (Qu x f = 80,000-90,000 GHz). The Ba(Mg1,3Ta(2_,013W,13Ti,,13)03 with x = 1.0 has e, = 15.4, rf= -25.1 ppm/ 18 "C, Q„ x f = 35,400 GHz

The effect of dopants on the microwave dielectric properties of Ba( Mgo.33Ta0.67)03 ceramics

The effect of dopants with different valencies and ionic radii on the densification, structural ordering, and microwave dielectric properties of Ba(Mg1t3Tazt3)O3 (BMT) is investigated. It is found that dopants such as Sb,05, MnO, ZrO,, WO1, and ZnO improve the microwave dielectric properties of BMT. Addition of trivalent dopants is detrimental to the cation ordering and dielectric properties of BMT. A correlation between the microwave dielectric properties of BMT and ionic radii of the dopant has been established. The variation of the dielectric properties of pure and doped BMT at cryogenic temperatures is also discussed

Preparation, Characterization and Microwave Dielectric Properties of Ba (B1/2Nb1/2)03 [B' = La, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Y, Yb and In] Ceramics

Microwave dielectric resonators (DRs) based on Ba(B1,2Nbi/2)03 [B' = La, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Y, Yb, and In] complex perovskites have been prepared by conventional solid state ceramic route. The dielectric properties (relative permittivity, Er; quality factor, Q; and resonant frequency, rr) of the ceramics have been measured in the frequency range 4-6 GHz using resonance methods. The resonators have relatively high dielectric constant in the range 36-45, high quality factor and small temperature variation of resonant frequency. The dielectric properties are found to depend on the tolerance factor (t), ionic radius (r), and lattice parameter (ap)

The Effect of Glass Additives on the Microwave Dielectric Properties of Ba(Mg 1 /3Ta2/3)03 Ceramics

The effect of glass additives on the densification , phase evolution, microstructure and microwave dielectric properties of Ba(Mg1;3 Ta2i3)03 (BMT) was investigated . Different weight percentages of quenched glass such as B203 , Si02, B203-SiO2, ZnO-B203, 5ZnO-2B2O3, Al203-SiO2, Na20-2B203.10H20, BaO-B203-SiO2, MgO-B203-SiO2, PbO-B203-SiO2 , ZnO-B203-SiO2 and 2MgO-Al203-5SiO2 were added to calcined BMT precursor . The sintering temperature of the glass -added BMT samples were lowered down to 1300 °C compared to solid-state sintering where the temperature was 1650 °C. The formation of high temperature satellite phases such as Ba5Ta4O15 and Ba7Ta6O22 were found to be suppressed by the glass addition . Addition of glass systems such as B203, ZnO-B203, 5ZnO-2B203 and ZnO-B203-SiO2 improved the densification and microwave dielectric properties. Other glasses were found to react with BMT to form low-Q phases which prevented densification . The microwave dielectric properties of undoped BMT with a densification of 93 . 1 % of the theoretical density were Cr = 24 . 8, Tr = 8 ppm/°C and Q„ x f= 80,000 GHz. The BMT doped with 1.0 wt% of B203 has Q„ x f = 124,700GHz, Cr = 24.2, and T f = -1.3 ppm /°C. The unloaded Q factor of 0.2 wt% ZnO-B203-doped BMT was 136,500 GHz while that of 1.0 wt% of 5ZnO-2B203 added ceramic was Q„ x f= 141,800 GHz . The best microwave quality factor was observed for ZnO -B203-SiO2 (ZBS) glass-added ceramics which can act as a perfect liquid-phase medium for the sintering of BMT. The microwave dielectric properties of 0.2wt% ZBS-added BMT dielectric was Q„ x f= 152,800 GHz, F,= 25.5, and Tr = - 1.5 ppm/°C