Page 1. Towards Web 3.0... • Web 1.0 • Web 2.0 • Web 3.0 • Technology hype? • Internet as seen by our kids? Page 2. Random Trivia: Brazil has more Orkut users than citizens Page 3. The war is over. Platforms have won. Applications have lost Page 4. Page 5. Blogosphere • The blogosphere is made up of all blogs and their interconnections Page 6. Social bookmarking Page 7. Page 8. Page 9. Page 10. Page 11. Page 12. Page 13. Page 14. Towards Web 3.0 Page 15. Page 16. Wolfram Alpha Page 17. Page 18. Page 19. Page 20. Page 21. Page 22

CuInS2/In2S3 Cells using a Cost-effective Technique: Significance of Precursor Ratios on Cell Parameters

Thin film solar cells having structure CuInS2/In2S3 were fabricated using chemical spray pyrolysis (CSP) technique over ITO coated glass. Top electrode was silver film (area 0.05 cm2). Cu/In ratio and S/Cu in the precursor solution for CuInS2 were fixed as 1.2 and 5 respectively. In/S ratio in the precursor solution for In2S3 was fixed as 1.2/8. An efficiency of 0.6% (fill factor -37.6%) was obtained. Cu diffusion to the In2S3 layer, which deteriorates junction properties, is inevitable in CuInS2/In2S3 cell. So to decrease this effect and to ensure a Cu-free In2S3 layer at the top of the cell, Cu/In ratio was reduced to 1. Then a remarkable increase in short circuit current density was occurred from 3 mA/cm2 to 14.8 mA/cm2 and an efficiency of 2.13% was achieved. Also when In/S ratio was altered to 1.2/12, the short circuit current density increased to 17.8 mA/cm2 with an improved fill factor of 32% and efficiency remaining as 2%. Thus Cu/In and In/S ratios in the precursor solutions play a crucial role in determining the cell parameters