Activation of Progesterone Receptor by ATP

Progesterone-receptor complex from freshly prepared hen oviduct cytosol acquired the ability to bind to isolated nuclei, DNA-cellulose and ATP-Sepharose when incubated with 5-10 mM ATP at 4°C. The extent of this ATP-dependent activation was higher when compared with heat-activation achieved by warming the progesterone- receptor complex at 23 °C. The transformation of progesterone-receptor complex which occurred in a time-dependent manner was only partially dependent on hormone presence. The ATP effect was selective in causing this transformation whereas ADP, AMP and cAMP failed to show any such effect. The non-hydrolizable analogs of ATP, adenosine 5'-[a,/3-methylene]triphosphate and adenosine 5-[/l,y-imido]triphosphate were also found to be ineffective. Presence of 10 mM sodium molybdate blocked both the ATP and the heat-activation of progesterone-receptor complex. Mn" or Mg` had no detectable effect on the receptor activation but the presence of Ca" increased the extent of ATP-activation slightly. EDTA presence (> 5 mM) decreased the extent of receptor activation by about 40 % and was, therefore, not included in the buffers used for activation studies. Divalent cations were also ineffective when tested in the presence of 1- 5 mM EDTA. The properties of progesterone-receptor complex remained intact under the above conditions when analyzed for steroid-binding specificity and Scatchard analysis. However, the ATP-activated progesterone-receptor complex lost the ability to aggregate when tested on low-salt sucrose gradients. ATP was equally effective in activating the rat-uterine estradiol-receptor complex at 4 "C and influenced the transformation of 4-S receptor form into a 5-S form when analyzed on sucrose gradients containing 0.3 M KCI. The presence of ATP also increased the rate of activation of progesterone-receptor complex at 23 °C. These findings suggest a role for ATP in receptor function and offer a convenient method of studying the process of receptor activation at low temperature and mild assay conditions.

Mechanical Properties of Short-Isora-Fiber-Reinforced Natural Rubber Composites: Effects of Fiber Length, Orientation, and Loading; Alkali Treatment;and Bonding Agent

A series of short-isora-fiber-reinforced natural rubber composites were prepared by the incorporation of fibers of different lengths (6, 10, and 14 mm) at 15 phr loading and at different concentrations (10, 20, 30, and 40 phr) with a 10 mm fiber length. Mixes were also prepared with 10 mm long fibers treated with a 5% NaOH solution. The vulcanization parameters, processability, and stress-strain properties of these composites were analyzed. Properties such as tensile strength, tear strength, and tensile modulus were found to be at maximum for composites containing longitudinally oriented fibers 10 mm in length. Mixes containing fiber loadings of 30 phr with bonding agent (resorcinol-formaldehyde [RF] resin) showed mechanical properties superior to all other composites. Scanning electron microscopy (SEM) studies were carried out to investigate the fiber surface morphology, fiber pullout, and fiber-rubber interface. SEM studies showed that the bonding between the fiber and rubber was improved with treated fibers and with the use of bonding agent.

Long period gratings in multimode optical fibers: application in chemical sensing

We propose and demonstrate a new technique for evanescent wave chemical sensing by writing long period gratings in a bare multimode plastic clad silica fiber. The sensing length of the present sensor is only 10 mm, but is as sensitive as a conventional unclad evanescent wave sensor having about 100 mm sensing length. The minimum measurable concentration of the sensor reported here is 10 nmol/l and the operating range is more than 4 orders of magnitude. Moreover, the detection is carried out in two independent detection configurations viz., bright field detection scheme that detects the core-mode power and dark field detection scheme that detects the cladding mode power. The use of such a double detection scheme definitely enhances the reliability and accuracy of the results. Furthermore, the cladding of the present fiber need not be removed as done in conventional evanescent wave fiber sensors.

Studies on the fracture behaviour of polymer blends with special reference to PP/HDPE and PS/HIPS blends

Investigations on the fracture behaviour of polymer blends is the topic of this thesis. The blends selected are PP/HDPE and PS/HIPS. PP/HDPE blend is chosen due to its commercial importance and PS/HIPS blend is selected to study the transition from brittle fracture to ductile fracture.PP/HDPE blends were prepared at different compositions by melt blending at 180°C and fracture failure process was investigated by conducting notch sensitivity test and tensile test at different strain rates. The effects of two types of modifiers (particulate and elastomer) on the fracture behaviour and notch sensitivity of PP/HDPE blends were studied. The modifiers used are calcium carbonate, a hard particulate filler commonly used in plastics and Ethylene Propylene Diene Monomer (EPDM). They were added in 2%, 4% and 6% by weight of the blends.The study shows that the mechanical properties of PP/HDPE blends can be optimized by selecting proper blend compositions. The selected modifiers are found to alter and improve the fracture behaviour and notch sensitivity of the blends. Particulate fillers like calcium carbonate can be used for making the mechanical behaviour more stable at the various blend compositions. The resistance to notch sensitivity of the blends is found to be marginally lower in the presence of calcium carbonate. The elastomeric modifier EPDM produces a better stability of the mechanical behaviour. A low concentration of EPDM is sufficient to effect such a change. EPDM significantly improves the resistance to notch sensitivity of the blends. The study shows that judicious selection of modifiers can improve the fracture behaviour and notch sensitivity of PP/HDPE blends and help these materials to be used for critical applications.For investigating the transition in fracture behaviour and failure modes, PS/HIPS blends were selected. The blends were prepared by melt mixing followed by injection moulding to prepare the specimens for conducting tensile, impact and flexure tests. These tests were used to simulate the various conditions which promote failure.The tensile behaviour of unnotched and notched PS/HIPS blend samples were evaluated at slow speeds. Tensile strengths and moduli were found to increase at the higher testing speed for all the blend combinations whereas maximum strain at break was found to decrease. For a particular speed of testing, the tensile strength and modulus show only a very slight decrease as HIPS content is increased up to about 40%. However, there is a drastic decrease on increasing the HIPS content thereafter.The maximum strain at break shows only a very slight change up to about 40% HIPS content and thereafter shows a remarkable increase. The notched specimens also follow a comparable trend even though the notch sensitivity is seen high for PS rich blends containing up to 40% HIPS. The notch sensitivity marginally decreases with increase in HIPS content. At the same time, it is found to increase with the increase in strain rate. It is observed that blends containing more than 40% HIPS fail in ductile mode.The impact characteristics of PSIHIPS blends studied were impact strength, the energy absorbed by the test specimen and impact toughness. Remarkable increase in impact strength is observed as HIPS content in the blend exceeds 40%. The energy absorbed by the test specimens and the impact toughness also show a comparable trend.Flexural testing which helps to characterize the load bearing capacity was conducted on PS/HIPS blend samples at the two different testing speeds of 5mmlmin and 10 mm/min. The flexural strength increases with increase in testing speed for all the blend compositions. At both the speeds, remarkable reduction in flexural strength is observed as HIPS content in the blend exceeds 40%. The flexural strain and flexural energy absorbed by the specimens are found to increase with increase in HIPS content. At both the testing speeds, brittle fracture is observed for PS rich blends whereas HIPS rich blends show ductile mode of failure.Photoelastic investigations were conducted on PS/HIPS blend samples to analyze their failure modes. A plane polariscope with a broad source of light was utilized for the study. The coloured isochromatic fringes formed indicate the presence of residual stress concentration in the blend samples. The coverage made by the fringes on the test specimens varies with the blend composition and it shows a reducing trend with the increase in HIPS content. This indicates that the presence of residual stress is a contributing factor leading to brittle fracture in PS rich blends and this tendency gradually falls with increase in HIPS content and leads to their ductile mode of failure.

Long term trends of seasonal and monthly rainfall in different intensity ranges over Indian subcontinent

In general Indian summer monsoon rainfall did not show any significant trend in all Indian summer monsoon rainfall series, however, it was reported that the ISMR is subjected to spatial trends. This paper made an attempt to bring out long term trends of different intensity classes of summer monsoon rainfall in different regions of Indian subcontinent. The long term trend of seasonal and monthly rainfall were also made using the India Meteorological Department gridded daily rainfall data with a spatial resolution of 1° × 1° latitude-longitude grid for the period from 1st January, 1901 to 31st December, 2003. The summer monsoon rainfall shows an increasing trend in southeast, northwest and northeast regions, whereas decreasing trend in the central and west coastal regions. In monthly scale, July rainfall shows decreasing trend over west coastal and central Indian regions and significant increasing trend over northeast region at 0.1% significant level. During the month August, decreasing trend is observed in the west coastal stations at 10% significant level. In most of the stations, mean daily rainfall shows an increasing trend for low and very high intense rainfall. For the moderate rainfall, the trend is different for different regions. In the central and southern regions the trend of moderate and moderately high classes show increasing trend. And for the high and very high intensity classes, the trend is decreasing significantly. In the northeastern regions, above 10 mm/day rainfall shows significantly increasing trend with 0.1% significant level.