Effect of preparation on magnetic properties of Mn-Zn ferrite

Mixed ferrites belonging to the type Mn0.9Zn0.1Fe2O4 have been prepared by the double sintering method and by the chemical co-precipitation for comparing their magnetic properties. Sintered and precipitated ferrites exhibit different characteristics, especially in their magnetic properties like magnetization (Ms), coercive field (Hc) and Curie temperature (Tc). The sintered particles were size reduced in order to compare with the nanosized co-precipitated particles. The effect of grinding has also been studied. Particles have been collected at regular intervals of grinding and their properties have been studied. The increase in the coercive field has been recorded by a hysteresis curve tracer confirming size reduction. X-ray diffraction studies confirmed the structure and consequent size reduction

Synthesis and characterization of γ-Fe2O3—a magnetic tape material

Acicular FeC~O4-2H20 was precipitated from glycerol and starch media. Thermal decomposition of this oxalate in dry and moist nitrogen yielded primarily FeO and Fe 3Oa respectively. Characterization was attempted through DTA, TG, x-ray diffraction, TEM and magnetization studies. It was found that the oxalate can be completely decomposed to FeaO~ in moist nitrogen (PH~o ,"-" 35 torr) at 775 K and then oxidised by dry air to acicular "/-Fe~Oa at 575 K. The resulting material has saturation magnetization (,-,., 70 emu/g), coercive field (N300 Oe) and squareness ratio ( ,~, 0-60-0-65), which values art comparable with those of the commercial samples

Structural, topographical and magnetic evolution of RF-sputtered Fe-Ni alloy based thin films with thermal annealing

Metglas 2826 MB having a nominal composition of Fe40Ni38Mo4B18 is an excellent soft magnetic material and finds application in sensors and memory heads. However, the thin-film forms of Fe40Ni38Mo4B18 are seldom studied, although they are important in micro-electro-mechanical systems/nano-electromechanical systems devices. The stoichiometry of the film plays a vital role in determining the structural and magnetic properties of Fe40Ni38Mo4B18 thin films: retaining the composition in thin films is a challenge. Thin films of 52 nm thickness were fabricated by RF sputtering technique on silicon substrate from a target of nominal composition of Fe40Ni38Mo4B18. The films were annealed at temperatures of 400 °C and 600 °C. The micro-structural studies of films using glancing x-ray diffractometer (GXRD) and transmission electron microscope (TEM) revealed that pristine films are crystalline with (FeNiMo)23B6 phase. Atomic force microscope (AFM) images were subjected to power spectral density analysis to understand the probable surface evolution mechanism during sputtering and annealing. X-ray photoelectron spectroscopy (XPS) was employed to determine the film composition. The sluggish growth of crystallites with annealing is attributed to the presence of molybdenum in the thin film. The observed changes in magnetic properties were correlated with annealing induced structural, compositional and morphological changes