Synthesis, Characterisation and Properties of (Ba1-xSrx) (Nd1/2Nb1/2 ) 03 Ceramics for Application as Dielectric Resonators in Microwave Circuits

The (Ba1-x Srx) (Nd1/2, Nb1/2) O3 ceramics have been prepared by the conventional ceramic route for different values of x. Addition of a small amount of CeO2(1 wt%) as a sintering aid increased the density of the samples. The structure and microstructure of the sintered samples are studied by X-ray diffraction and SEM methods. The dielectric properties of the samples are measured in the microwave frequency region as a function of composition. The dielectric constant decreases as x increases. The coefficient of thermal variation of resonant frequency decreases as the Sr content increases and goes to the negative side. The dielectric properties of (Ba1-x Srx) (Nd1/2, Nb1/2) O3 are in the range suitable for application as dielectric resonators in microwave circuits

Preparation and Microwave Characterisation of Ba2-xSrx Ti9 O20 Cermics

Ceramics of composition BaO-Ln2O3-STiO2 have been prepared with four elements (Ln=La,Pr,Nd.Sm) by a conventional solid state ceramic preparation route and the dielectric properties measured in the microwave frequency range

High Permittivity and Low Ceramics in the Bao-SrO-Nb2O5 System

A new group of compounds with composition (Ba5-xSrx) Nb4015, having high permittivity and low loss have been prepared and characterized in the microwave frequency region . X-ray diffraction studies showed that monophase compound existed for all values of x from 0 to 5. Microwave dielectric properties such as and c f showed smooth variation with x , while the unloaded quality factor (Qu) showed remarkable improvement with x

Preparation, Characterization and Dilectric Properties of Ceramics in the BaO-Nd2O3-TiO2 System

The dielectric ceramics BaNd2Ti3Oto, BaNd2Ti4O12 and BaNd2Ti5O14 have been prepared by Conventional solid state ceramic route. The sintered ceramic samples have been characterized by X-ray diffraction and Scanning Electron Microscopy (SEM). The dielectric properties in the microwave frequency range have been measured using conventional microwave dielectric resonator methods. The BaNd2Ti1O10, BaN2Ti4O12 and BaNd2Ti5O14 have dielectric constants (Er) ~ 60, 84 and 77 respectively. They have relatively high quality factors

Tailoring the Microwave Dielectric Properties of BaRE2Ti4012 and BaRE2Ti5014 Ceramics by Compositional Variations

Ceramic dielectric resonators in the BaO-RE2O3-TiO2 (RE = rare earth) system have been prepared by the conventional solid state ceramic route. The dielectric properties have been tailored by substitution of different rare earth oxides and by bismuth oxide addition. The dielectric constants increased with Bi addition whereas the 0 decreased. The temperature coefficient of the resonant frequency improved with bismuth addition

Microwave Characterisation of BaCe2Ti5O15 and Ba5Nb4O15 Ceramic Dielectric Resonators Using Whispering Gallery Mode Method

A microwave dielectric ceramic resonator based on BaCe2Ti5O15 and Ba5Nb4O15 have been prepared by conventional solid state ceramic route. The dielectric resonators (DRs) have high dielectric constant 32 and 40 for BaCe2Ti5O15 and Ba5Nb4O15, respectively. The whispering gallery mode (WGM) technique was employed for the accurate determination of the dielectric properties in the microwave frequency range. The BaCe2Ti5O15 and Ba5Nb4O15 have quality factors (Q X F) of 30,600 and 53,000 respectively. The quality factor is found to depend on the azimuthal mode numbers. The temperature coefficient of resonant frequency (Tr) of BaCe2Ti5O15 and Ba5Nb4O15 have been measured accurately using different resonant modes and are + 41 and + 78 ppm/K, respectively

Synthesis,Characterization and Properties of [REI_xREX]TiNb06 Dielectric Ceramics

Dielectric ceramics based on solid solution phases of [RE1_x= REr]TiNb06, where REI_s = Nd, Pr, Sm and RE' = Dy, Gd and Y, were prepared by the conventional solid-state ceramic route for values of x. The ceramic samples are characterized by X-ray diffraction and microwave methods. Ceramics based on RE (Pr, Nd and Sm) belonging to aeschynite group shows positive value of Tf and those based on RE (Gd, Dy and Y) belonging to euxenite group show negative value of r f. The solid solution phases between the aeschynite and the euxenite group shows intermediate dielectric constant and r f values. The results indicate the possibility of tailoring the dielectric properties by varying the composition of the solid solution phases. The range of solid solubility of euxenite in aeschenite and aeschenite in euxenite are different for different rare earth ions

Microwave Dielectric Properties of RETiTaO6 (RE = La, Ce,Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Y, Er, Yb, Al, and In) Ceramics

Microwave dielectric ceramics based on RETiTaO6 (RE = La, Cc, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Y, Er, Yb, Al, and In) were prepared using a conventional solid-state ceramic route. The structure and microstructure of the samples were analyzed using x-ray diffraction and scanning electron microscopy techniques. The sintered samples were characterized in the microwave frequency region. The ceramics based on Ce, Pr, Nd, Sm, Eu, Gd, Tb, and Dy, which crystallize in orthorhombic aeschynite structure, had a relatively high dielectric constant and positive T f while those based on Ho, Er, and Yb, with orthorhombic euxenite structure, had a low dielectric constant and negative Tf. The RETiTaO6 ceramics had a high-quality factor. The dielectric constant and unit cell volume of the ceramics increased with an increase in ionic radius of the rare-earth ions, but density decreased with it. The value of Tf increased with an increase in RE ionic radii, and a change in the sign of Tf occurred when the ionic radius was between 0.90 and 0.92 A. The results indicated that the boundary of the aeschynite to euxenite morphotropic phase change lay between DyTiTaO6 and HoTiTaO6. Low-loss ceramics like ErTiTaO6 (Er = 20.6, Qxf = 85,500), EuTiTaO6 (Er = 41.3, Qxf = 59,500), and YTiTaO6 (Er = 22.1, Q„xf = 51,400) are potential candidates for dielectric resonator applications

Synthesis, Characterization and Properties of Ca5A2TiO12 (A=Nb, Ta) Ceramic Dielectric Materials for Applications in Microwave Telecommunication Systems

Microwave ceramic dielectric materials Ca5Nb2TiO12 and Ca5Ta2TiO12 have been prepared by a conventional solid-state ceramic process. The structure was studied by X-ray diffraction and the dielectric properties were characterized at microwave frequencies. The ceramics posses a relatively high dielectric constant, very low dielectric loss (Q5 x f > 30000GHz) and small temperature variation of resonant frequency. These materials are potential candidates for dielectric resonator applications in microwave integrated circuits. [DOI: 10. 1 143/JJAP.41.3834]

Tailoring the Microwave Dielectric Properties of GdTiNb 1 _-xTa,O6 and Sm 1 _X Y,TiTa06 Ceramics

Microwave dielectric ceramics based on GdTiNb,-,.Ta,O6 and Sml _.,Y,TiTa06 have been prepared by conventional solid state method . The GdTiTaO6 and SmTiTaO6 have aeschenite structure with positive rr and GdTiNbO6 and YTiTaO6 have euxenite structure with negative rr. The rr of the ceramics has been tuned by preparing solid solution phases between the aeschynites and euxenites for a possible zero rr material . It is observed that GdTiNbt_YTa.,O6 undergoes a phase transition from aeschynite to euxenite when x=0.75 and in Sml-,YxTiTa06 for x= 0.73. The microwave dielectric properties change abruptly near the transition region . The rr value approaches zero near the phase transition region while the samples have poor sinterability and poor quality factor . The unloaded quality factor, dielectric constant and the sign of rr of the solid solution phases are found to depend on the average ionic radius of the rare earth ion in RE ,-5RE',TiTaO6. The boundary of the euxenite-aeschynite phase transition occurs at an average ( RE) ionic radius of 0.915 A in Sm,_, Y,.TiTaO6 solid solution phases

Microwave Dielectric Properties of BaO -2CeO2-nTiO2 Ceramics

The BaO-2CeO2-nTiO2 ceramics with n = 3, 4 and 5 have been prepared with CeO2 as starting material . The ceramics have been characterized using scanning electron microscopy , X-ray diffraction , Raman and X-ray photoelectron spectroscopy techniques. The microwave dielectric properties have been measured using standard dielectric resonator techniques . BaO-2CeO2-3TiO2 (123), BaO-2CeO2-4TiO2 ( 124) and BaO-2CeO2-5TiO2 ( 125) ceramics showed dielectric constants of 38, 27 and 32, respectively . All the ceramics showed fairly good unloaded Q - factors . 124 and 125 compounds exhibited low tf values, while 123 showed a high rf value

Preparation, Characterization and Microwave Dielectric Properties of Ba (B1/2Nb1/2)03 [B' = La, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Y, Yb and In] Ceramics

Microwave dielectric resonators (DRs) based on Ba(B1,2Nbi/2)03 [B' = La, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Y, Yb, and In] complex perovskites have been prepared by conventional solid state ceramic route. The dielectric properties (relative permittivity, Er; quality factor, Q; and resonant frequency, rr) of the ceramics have been measured in the frequency range 4-6 GHz using resonance methods. The resonators have relatively high dielectric constant in the range 36-45, high quality factor and small temperature variation of resonant frequency. The dielectric properties are found to depend on the tolerance factor (t), ionic radius (r), and lattice parameter (ap)

The Effect of Glass Additives on the Microwave Dielectric Properties of Ba(Mg 1 /3Ta2/3)03 Ceramics

The effect of glass additives on the densification , phase evolution, microstructure and microwave dielectric properties of Ba(Mg1;3 Ta2i3)03 (BMT) was investigated . Different weight percentages of quenched glass such as B203 , Si02, B203-SiO2, ZnO-B203, 5ZnO-2B2O3, Al203-SiO2, Na20-2B203.10H20, BaO-B203-SiO2, MgO-B203-SiO2, PbO-B203-SiO2 , ZnO-B203-SiO2 and 2MgO-Al203-5SiO2 were added to calcined BMT precursor . The sintering temperature of the glass -added BMT samples were lowered down to 1300 °C compared to solid-state sintering where the temperature was 1650 °C. The formation of high temperature satellite phases such as Ba5Ta4O15 and Ba7Ta6O22 were found to be suppressed by the glass addition . Addition of glass systems such as B203, ZnO-B203, 5ZnO-2B203 and ZnO-B203-SiO2 improved the densification and microwave dielectric properties. Other glasses were found to react with BMT to form low-Q phases which prevented densification . The microwave dielectric properties of undoped BMT with a densification of 93 . 1 % of the theoretical density were Cr = 24 . 8, Tr = 8 ppm/°C and Q„ x f= 80,000 GHz. The BMT doped with 1.0 wt% of B203 has Q„ x f = 124,700GHz, Cr = 24.2, and T f = -1.3 ppm /°C. The unloaded Q factor of 0.2 wt% ZnO-B203-doped BMT was 136,500 GHz while that of 1.0 wt% of 5ZnO-2B203 added ceramic was Q„ x f= 141,800 GHz . The best microwave quality factor was observed for ZnO -B203-SiO2 (ZBS) glass-added ceramics which can act as a perfect liquid-phase medium for the sintering of BMT. The microwave dielectric properties of 0.2wt% ZBS-added BMT dielectric was Q„ x f= 152,800 GHz, F,= 25.5, and Tr = - 1.5 ppm/°C

Development and Analysis of a Drum-Shaped Compact Microstrip Antenna

The thesis is the outcome of the experimental and theoretical investigations on a new compact drum-shaped microstrip antenna. A new compact antenna suitable for personal communication system(PCS), Global position System(GPS) and array applications is developed and analysed. The generalised cavity model and spatial fourier transform technique are suitably modified for the analysis of the antenna. The predicted results are compared with experimental results and excellent agreement is observed. The experimental work done by the author in related fields are incorporated as three appendices in this thesis. A single feed dual frequency microstrip antenne is presented in appendix A.Appendix B describes a new broadband dual frequeny microstrip antenna. The bandwidth enhancement effect of microstrip antennas through dielectric resonator loading is demonstarted in Appendix C.