A study on mitigating the effect of sulphates in lime stabilised Cochin marine clays

Soft clays known for their high compressibility, low stiffness and low shear strength are always associated with large settlement. In place soil treatment using calcium-based stabilizers like lime and cement is a feasible solution to readdress strength deficiencies and problematic shrink/swell behaviour of unstable subgrade soils. Out of these, lime has been proved unambiguously as the most effective and economical stabilising agent for marine clays. Lime stabilisation creates long-term chemical changes in unstable clay soils to create strong, but flexible, permanent structural layers in foundations and other pavement systems. Even though calcium-based stabilizers can improve engineering properties of soft clays, problems can arise when they are used in soils rich in sulphates. It is possible for marine clays to be enriched with sulphates, either by nature or due to the discharge of nearby industrial wastes containing sulphates. The presence of sulphates is reported to adversely affect the cation exchange and pozzolanic reactions of cement and lime treated soil systems. The anions of sulphates may combine with the available calcium and alumina, and form insoluble ettringite in the soil system. Literature on sulphate attack in lime treated marine clays reports that formation of ettringite in lime-sodium sulphate-clay system is capable of adversely affecting the engineering behavior of marine clays. Only very few studies have been conducted on soft marine clays found along the coastal belt of Kerala and that too, is limited to Cochin marine clays. The studies conducted also have the limitation that the strength behaviour of lime stabilised clay was investigated only for one year. Practically no data pertaining to long term adverse effects likely to be brought about by sulphates on the strength and compressibility characteristics of Cochin marine clays is available. The overriding goal of this investigation was thus to examine the effectiveness of lime stabilisation in Cochin marine clays under varying sulphate contents. The study aims to reveal the changes brought about by varying sulphate contents on both physical and engineering properties of these clays stabilised by lime and the results for various curing periods up to two years is presented in this thesis. Quite often the load causing an unacceptable settlement may be less than the load required to cause shear failure and therefore attempt has been made in this research to highlight sulphate induced changes in both the compressibility and strength characteristics of lime treated Cochin marine clays. The study also aimed at comparing the available IS methods for sulphate quantification and has attempted to determine the threshold level of sulphate likely make these clays vulnerable by lime stabilisation. Clays used in this study were obtained from two different sites in Kochi and contained sulphate in two different concentrations viz., 0.5% and 0.1%. Two different lime percentages were tried out, 3% and 6%. Sulphate content was varied from 1% to 4% by addition of reagent grade sodium sulphate. The long term influence of naturally present sulphate is also investigated. X-ray diffraction studies and SEM studies have been undertaken to understand how the soil-lime reactions are affected in the presence of sodium sulphate. Natural sulphate content of 0.1% did not seem to have influenced normal soil lime reactions but 0.5% sulphate could induce significant changes adversely in both compressibility and strength behaviour of lime treated clays after long duration. Compressibility is seen to increase drastically with increasing sulphate content suggesting formation of ettringite on curing for longer periods. Increase in compression index and decrease in bond strength with curing period underlined the adverse effects induced in lime treated marine clays by the presence of sulphates. Presence of sulphate in concentrations ranging from 0.5 % to 4% is capable of adversely affecting the strength of lime treated marine clays. Considerable decrease is observed with increasing concentrations of sulphate. Ettringite formation due to domination of sodium ions in the system was confirmed in mineralogical studies made. Barium chloride and barium hydroxide is capable of bringing about beneficial changes both in compressibility and strength characteristics of lime treated Cochin marine clays in the presence of varying concentrations of sulphate and is strongly influenced by curing time. Clay containing sodium sulphate has increased strength values when either of barium compounds was used with lime ascompared with specimens treated with lime only. Barium hydroxide is observed to remarkably increase the strength as compared to barium chloride,when used in conjunction with lime to counteract the effect of sulphate.

Synthesis, Characterization and Applications of Modified TiO2 Systems

This thesis is divided in to 9 chapters and deals with the modification of TiO2 for various applications include photocatalysis, thermal reaction, photovoltaics and non-linear optics. Chapter 1 involves a brief introduction of the topic of study. An introduction to the applications of modified titania systems in various fields are discussed concisely. Scope and objectives of the present work are also discussed in this chapter. Chapter 2 explains the strategy adopted for the synthesis of metal, nonmetal co-doped TiO2 systems. Hydrothermal technique was employed for the preparation of the co-doped TiO2 system, where Ti[OCH(CH3)2]4, urea and metal nitrates were used as the sources for TiO2, N and metals respectively. In all the co-doped systems, urea to Ti[OCH(CH3)2]4 was taken in a 1:1 molar ratio and varied the concentration of metals. Five different co-doped catalytic systems and for each catalysts, three versions were prepared by varying the concentration of metals. A brief explanation of physico-chemical techniques used for the characterization of the material was also presented in this chapter. This includes X-ray Diffraction (XRD), Raman Spectroscopy, FTIR analysis, Thermo Gravimetric Analysis, Energy Dispersive X-ray Analysis (EDX), Scanning Electron Microscopy(SEM), UV-Visible Diffuse Reflectance Spectroscopy (UV-Vis DRS), Transmission Electron Microscopy (TEM), BET Surface Area Measurements and X-ray Photoelectron Spectroscopy (XPS). Chapter 3 contains the results and discussion of characterization techniques used for analyzing the prepared systems. Characterization is an inevitable part of materials research. Determination of physico-chemical properties of the prepared materials using suitable characterization techniques is very crucial to find its exact field of application. It is clear from the XRD pattern that photocatalytically active anatase phase dominates in the calcined samples with peaks at 2θ values around 25.4°, 38°, 48.1°, 55.2° and 62.7° corresponding to (101), (004), (200), (211) and (204) crystal planes (JCPDS 21-1272) respectively. But in the case of Pr-N-Ti sample, a new peak was observed at 2θ = 30.8° corresponding to the (121) plane of the polymorph brookite. There are no visible peaks corresponding to dopants, which may be due to their low concentration or it is an indication of the better dispersion of impurities in the TiO2. Crystallite size of the sample was calculated from Scherrer equation byusing full width at half maximum (FWHM) of the (101) peak of the anatase phase. Crystallite size of all the co-doped TiO2 was found to be lower than that of bare TiO2 which indicates that the doping of metal ions having higher ionic radius into the lattice of TiO2 causes some lattice distortion which suppress the growth of TiO2 nanoparticles. The structural identity of the prepared system obtained from XRD pattern is further confirmed by Raman spectra measurements. Anatase has six Raman active modes. Band gap of the co-doped system was calculated using Kubelka-Munk equation and that was found to be lower than pure TiO2. Stability of the prepared systems was understood from thermo gravimetric analysis. FT-IR was performed to understand the functional groups as well as to study the surface changes occurred during modification. EDX was used to determine the impurities present in the system. The EDX spectra of all the co-doped samples show signals directly related to the dopants. Spectra of all the co-doped systems contain O and Ti as the main components with low concentrations of doped elements. Morphologies of the prepared systems were obtained from SEM and TEM analysis. Average particle size of the systems was drawn from histogram data. Electronic structures of the samples were identified perfectly from XPS measurements. Chapter 4 describes the photocatalytic degradation of herbicides Atrazine and Metolachlor using metal, non-metal co-doped titania systems. The percentage of degradation was analyzed by HPLC technique. Parameters such as effect of different catalysts, effect of time, effect of catalysts amount and reusability studies were discussed. Chapter 5 deals with the photo-oxidation of some anthracene derivatives by co-doped catalytic systems. These anthracene derivatives come underthe category of polycyclic aromatic hydrocarbons (PAH). Due to the presence of stable benzene rings, most of the PAH show strong inhibition towards biological degradation and the common methods employed for their removal. According to environmental protection agency, most of the PAH are highly toxic in nature. TiO2 photochemistry has been extensively investigated as a method for the catalytic conversion of such organic compounds, highlighting the potential of thereof in the green chemistry. There are actually two methods for the removal of pollutants from the ecosystem. Complete mineralization is the one way to remove pollutants. Conversion of toxic compounds to another compound having toxicity less than the initial starting compound is the second way. Here in this chapter, we are concentrating on the second aspect. The catalysts used were Gd(1wt%)-N-Ti, Pd(1wt%)-N-Ti and Ag(1wt%)-N-Ti. Here we were very successfully converted all the PAH to anthraquinone, a compound having diverse applications in industrial as well as medical fields. Substitution of 10th position of desired PAH by phenyl ring reduces the feasibility of photo reaction and produced 9-hydroxy 9-phenyl anthrone (9H9PA) as an intermediate species. The products were separated and purified by column chromatography using 70:30 hexane/DCM mixtures as the mobile phase and the resultant products were characterized thoroughly by 1H NMR, IR spectroscopy and GCMS analysis. Chapter 6 elucidates the heterogeneous Suzuki coupling reaction by Cu/Pd bimetallic supported on TiO2. Sol-Gel followed by impregnation method was adopted for the synthesis of Cu/Pd-TiO2. The prepared system was characterized by XRD, TG-DTG, SEM, EDX, BET Surface area and XPS. The product was separated and purified by column chromatography using hexane as the mobile phase. Maximum isolated yield of biphenyl of around72% was obtained in DMF using Cu(2wt%)-Pd(4wt%)-Ti as the catalyst. In this reaction, effective solvent, base and catalyst were found to be DMF, K2CO3 and Cu(2wt%)-Pd(4wt%)-Ti respectively. Chapter 7 gives an idea about the photovoltaic (PV) applications of TiO2 based thin films. Due to energy crisis, the whole world is looking for a new sustainable energy source. Harnessing solar energy is one of the most promising ways to tackle this issue. The present dominant photovoltaic (PV) technologies are based on inorganic materials. But the high material, low power conversion efficiency and manufacturing cost limits its popularization. A lot of research has been conducted towards the development of low-cost PV technologies, of which organic photovoltaic (OPV) devices are one of the promising. Here two TiO2 thin films having different thickness were prepared by spin coating technique. The prepared films were characterized by XRD, AFM and conductivity measurements. The thickness of the films was measured by Stylus Profiler. This chapter mainly concentrated on the fabrication of an inverted hetero junction solar cell using conducting polymer MEH-PPV as photo active layer. Here TiO2 was used as the electron transport layer. Thin films of MEH-PPV were also prepared using spin coating technique. Two fullerene derivatives such as PCBM and ICBA were introduced into the device in order to improve the power conversion efficiency. Effective charge transfer between the conducting polymer and ICBA were understood from fluorescence quenching studies. The fabricated Inverted hetero junction exhibited maximum power conversion efficiency of 0.22% with ICBA as the acceptor molecule. Chapter 8 narrates the third order order nonlinear optical properties of bare and noble metal modified TiO2 thin films. Thin films were fabricatedby spray pyrolysis technique. Sol-Gel derived Ti[OCH(CH3)2]4 in CH3CH2OH/CH3COOH was used as the precursor for TiO2. The precursors used for Au, Ag and Pd were the aqueous solutions of HAuCl4, AgNO3 and Pd(NO3)2 respectively. The prepared films were characterized by XRD, SEM and EDX. The nonlinear optical properties of the prepared materials were investigated by Z-Scan technique comprising of Nd-YAG laser (532 nm,7 ns and10 Hz). The non-linear coefficients were obtained by fitting the experimental Z-Scan plot with the theoretical plots. Nonlinear absorption is a phenomenon defined as a nonlinear change (increase or decrease) in absorption with increasing of intensity. This can be mainly divided into two types: saturable absorption (SA) and reverse saturable absorption (RSA). Depending on the pump intensity and on the absorption cross- section at the excitation wavelength, most molecules show non- linear absorption. With increasing intensity, if the excited states show saturation owing to their long lifetimes, the transmission will show SA characteristics. Here absorption decreases with increase of intensity. If, however, the excited state has strong absorption compared with that of the ground state, the transmission will show RSA characteristics. Here in our work most of the materials show SA behavior and some materials exhibited RSA behavior. Both these properties purely depend on the nature of the materials and alignment of energy states within them. Both these SA and RSA have got immense applications in electronic devices. The important results obtained from various studies are presented in chapter 9.