Properties of NaxCoO2 /

Polycrysttdline samples of NaiCoOa were prepared using the "Rapid heat-up" method. One set of samples was annealed in flowing O2, while the other set in flowing Argon. X-Ray diffraction measurements indicated a stable phase of Nao.7Co02 mixed with C03O4 for all the samples even though they differed in concentration of Na. Argon annealed samples were insulators, whereas the ones annealed in O2 were metallic. Most of the measurements were performed on the sample Nao.7Co02, because it is the host compound for the superconductor sample Nao.35Co02-H20. Magnetization measurement showed that the magnetic moment decreased with increasing sodium concentration. This is due to the existence of C03O4 in samples with Na^ 0.7. As sodium concentration decreases, the magnetic moment increases due to the increasing concentration of C03O4 and its large magnetic moment. Magnetization measurements showed that the magnetic moment of Nao.7Co02 is field-dependent in low fields eind field-independent in fields higher than 100 G. Resistivity changes with temperature (dp/dT) increased with increasing Na concentration. Also resistivity measurements were performed under different hydrostatic pressures on Nao.7Co02. Two transitions were observed; one at a temperature Ti ~20 K and the other at T2 ^280 K, the transition at Ti has a magnetic origin and the one at T2 is a structiural transition. It was noticed that pressure aJfects resistivity of the sample. At higher pressures resistivity changes faster with temperature. Magnetoresistance measurement showed a small change in the resistivity, especially at lower temperatures. A novel layered superconductor Nao.35Co02H20 was prepared using de-intercalation of Na from the host compound Nao.7Co02. FVom the temperature dependence of the magnetization, the superconducting transition temperature and lower critictil field have been estimated as Tc=4.12 K and Hci=66 G, respectively.

New Building Blocks for Dual-Property Molecule-Based Magnets

Two classes of compounds have been prepared and characterized as building blocks for chiral magnets and ferromagnetic conductors. In the fIrst project, the organic framework of a pentadentate, (N302) macro cycle has been synthetically modifIed to introduce phenyl substituents into its organic framework and the synthesis of four new [Fe(In(N302)(CN)2] complexes (I) - (IV) is presented. [Molecular diagram availble in pdf] This work represents the fIrst structural and magnetic studies of a family of spin crossover macrocycles that comprise of both structural and stereo-isomers. Magnetic susceptibility and Mossbauer data for the R,R-complex (I) is consistent with both a thermal and a light induced spin crossover transition. The X-ray data supports a change in geometry accompanying the thermal spin transition, from a high spin (HS) 7 -coordinate complex at room temperature to a low spin (LS) 5-coordinate complex at 100 K. The crystal structure ofthe racemic complex (III) reveals a HS, 7-coordinate complex at 200 K that undergoes no signifIcant structural changes on cooling. In contrast, the magnetic - susceptibility and Mossbauer data collected on a powder sample of the racemic complex are consistent with a LS complex. Finally, the meso complex (IV) was prepared and its structure and magnetic properties are consistent with a 5-coordinate LS complex that remains low spin, but undergoes conformational changes on cooling in solution. The chiral [Fe(H)(N302)(CN)2] macro cycle (I), together with its Mn(H) and Fe(H) derivatives have also been exploited as building blocks for the self-assembly of chiral magnets. In the second project, a synthetic route for the preparation of tetrathiafulvalene (TTF) donors covalently attached to a diisopropyl verdazyl radical via a cross conjugated pyridyl linker IS presented. Following this strategy, four new TTF-py- (diisopropyl)verdazyl radicals have been prepared and characterized (V) - (VIII) . [Molecular diagram available in pdf] The first (2:1) charge transfer complex ofa TTF-py-(diisopropyl)verdazyl radical donor and a TCNQ acceptor has been prepared and structurally characterized. The crystal packing shows that the donor and acceptor molecules are organized in a mixed stacking arrangement consistent with its insulating behaviour. EPR and magnetic susceptibility data support intramolecular ferromagnetic interactions between the TTF and the verdazyl radicals and antiferromagnetic interactions between TTF donors within a stack. In an attempt to increase the intramolecular exchange interaction between the two radicals, a TTF-x-(diisopropyl)verdazyl radical (IX) was prepared, where the two radicals are connected ia a conjugated divinylene linker. The neutral radical donors stack in a more favourable head-to-head arrangement but the bulky isopropyl groups prevent the donor radicals from stacking close enough together to facilitate good orbital overlap. [Molecular diagram available in pdf].

Polytypism and Silicon carbide : a solid state nuclear magnetic resonance study

A survey of predominantly industrial silicon carbide has been carried out using Magic Angle Spinning nuclear magnetic resonance (MAS nmr); a solid state technique. Three silicon carbide polytypes were studied; 3C, 6H, and 15R. The 13C and 29 Si MAS nmr spectra of the bulk SiC sample was identified on the basis of silicon (carbon) site type in the d iff ere n t pol Y t Y pes • Out to 5.00 A fro mac en t r a lsi 1 i con (0 r carbon) atom four types of sites were characterized using symmetry based calculations. This method of polytype analysis was also considered, in the prelminary stages, for applications with other polytypic material; CdBr 2 , CdI 2 , and PbI 2 " In an attempt to understand the minor components of silicon carbide, such as its surface, some samples were hydrofluoric acid washed and heated to extreme temperatures. Basically, an HF removable species which absorbs at -110 ppm (Si0 2 ) in the 29 Si MAS nmr spectrum is found in silicon carbide after heating. Other unidentified peaks observed at short recycle delays in some 29 Si MAS nmr spectra are considered to be impurities that may be within the lattice. These components comprise less than 5% of the observable silicon. A Tl study was carried out for 29 Si nuclei in a 3C ii polytype sample, using the Driven Equilibrium Single-Pulse Observation of T1 (DESPOT) technique. It appears as though there are a number of nuclei that have the same chemical shift but different T1 relaxation times. The T1 values range from 30 seconds to 11 minutes. Caution has to be kept when interpreting these results because this is the first time that DESPOT has been used for solid samples and it is not likely in full working order. MAS nmr indicates that the 13C and 29 Si ~sotropic chemical shifts of silicon carbide appear to have a reciprocal type of relationship_ Single crystal nmr analysis of a 6H sample is accordance with this finding when only the resultant isotropic shift is considered. However, single crystal nmr also shows that the actual response of the silicon and carbon nuclear environment to the applied magnetic field at various angles is not at all reciprocal. Such results show that much more single crystal nmr work is required to determine the actual behavior of the local magnetic environment of the SiC nuclei.