Crystal growth, Raman scattering and optical properties of the superconductor Cd2Re2O7(16O, 18O)/

Using the Physical Vapor Transport method, single crystals of Cd2Re207 have been grown, and crystals of dimensions up to 8x6x2 mm have been achieved. X-ray diffraction from a single crystal of Cd2Re207 has showed the crystal growth in the (111) plane. Powder X-ray diffraction measurements were performed on ^^O and ^^O samples, however no difference was observed. Assigning the space group Fd3m to Cd2Re207 at room temperature and using structure factor analysis, the powder X-ray diffraction pattern of the sample was explained through systematic reflection absences. The temperatiure dependence of the resistivity measurement of ^^O has revealed two structural phase transitions at 120 and 200 K, and the superconducting transition at 1.0 K. Using Factor Group Analysis on three different structiures of Cd2Re207, the number of IR and Raman active phonon modes close to the Brillouin zone centre have been determined and the results have been compared to the temperature-dependence of the Raman shifts of ^^O and ^*0 samples. After scaling (via removing Bose-Einstein and Rayleigh scattering factors from the scattered light) all spectra, each spectrum was fitted with a number of Lorentzian peaks. The temperature-dependence of the FWHM and Raman shift of mode Eg, shows the effects of the two structurjil phase transitions above Tc. The absolute reflectance of Cd2Re207 - '^O single crystals in the far-infrared spectral region (7-700 cm~^) has been measured in the superconducting state (0.5 K), right above the superconducting state (1.5 K), and in the normal state (4.2 K). Thermal reflectance of the sample at 0.5 K and 1.5 K indicates a strong absorption feature close to 10 cm~^ in the superconducting state with a reference temperature of 4.2 K. By means of Kramers-Kronig analysis, the absolute reflectance was used to calculate the optical conductivity and dielectric function. The real part of optical conductivity shows five distinct active phonon modes at 44, 200, 300, 375, and 575 cm~' at all temperatures including a Drude-like behavior at low frequencies. The imaginary part of the calculated dielectric function indicates a mode softening of the mode 44 cm~' below Tc.

Crystal growth, characterization and point contact spectroscopy on CuxTiSe₂

Various s e t s of single c rys t a l s and poly c rys t a l s of Cux TiSe2 were grown. X- r ay diffraction and ene rgy dispersive spe c t ros copy r e sul t s verified tha t the c rys t a l s were the cor r e c t compos i t ion and c rys t a l s t ruc tur e . Re s i s t ivi ty me a sur ement s and magne t i c sus c ept ibi l i ty me a sur ement s de t e rmined the supe r conduc t ing t r ans i t ion t empe r a tur e s for the c rys t a l s . The c rys t a l s in each growth had various supe r conduc t ing t r ans i t ion t empe r a tur e s . Also, the me a sur ement s indi c a t ed tha t the c rys t a l s were inhomogeneous. Point cont a c t spe c t ros copy expe r iment s were employed on various single c rys t a l s . Inspe c t ion of the da t a indi c a t ed tha t the ma t e r i a l ha s a single ene rgy gap . A progr am was bui l t ut i l i z ing the Levenbe rg-Ma rqua rdt me thod and theory on point cont a c t spe c t ros copy to de t e rmine the supe r conduc t ing ene rgy gap. Plot s of the supe r conduc t ing ene rgy gap a t various t empe r a tur e s were in di s agr e ement wi th wha t was expe c t ed for a convent iona l supe r conduc tor .

Crystal Growth and Characterization of Li0.9Mo6O17

Purple bronze Li0.9Mo6O17 has attracted researchers for its low dimensionality and corresponding properties. Although it has been studied for nearly two decades, there are still some unsolved puzzles with this unique material. Single crystals of Li0.9Mo6O17 were grown using the temperature gradient flux technique in this research. The crystal growth was optimized by experimenting different conditions and good quality crystals were obtained. X-ray diffraction results have confirmed the right phase of the crystals. Resistivity measurements and magnetic susceptibility measurements were carried out, and anomalous electronic behaviors were found. All of the samples showed the metal-insulator transition near 20K, followed by behavior that differs from sample to sample: either superconducting, metallic or insulating behavior was observed below 2K. Li0.9Mo6O17 was considered as a quasi-one-dimensional crystal and also a superconducting crystal, which implies a dimensional crossover may occur at the metal-insulator transition. A two-band scenario of the Luttinger liquid model was used to fit the resistivity data and excellent results were achieved, suggesting that the Luttinger theory is a very good candidate for the explanation of the anomalous behavior of Li0.9Mo6O17. In addition, the susceptibility measurements showed Curie paramagnetism and some temperature independent paramagnetism at low temperature. The absence of any anomalous magnetic feature near 20K where the resistivity upturn takes place, suggests that a charge density wave mechanism, which has been proposed by some researchers, is not responsible for the unique properties of Li0.9Mo6O17.

An application of cell-cluster theory to a rare gas crystal /|n[by] K. Westera. - 260 St. Catharines [Ont.] : Dept. of Physics, Brock University,

The Lennard-Jones Devonshire 1 (LJD) single particle theory for liquids is extended and applied to the anharmonic solid in a high temperature limit. The exact free energy for the crystal is expressed as a convergent series of terms involving larger and larger sets of contiguous particles called cell-clusters. The motions of all the particles within cell-clusters are correlated to each other and lead to non-trivial integrals of orders 3, 6, 9, ... 3N. For the first time the six dimensional integral has been calculated to high accuracy using a Lennard-Jones (6-12) pair interaction between nearest neighbours only for the f.c.c. lattice. The thermodynamic properties predicted by this model agree well with experimental results for solid Xenon.