Magnetic and transport properties of (Ba1-xKx)Fe2As2

Single crystals of (Bal - xKx)Fe2As2 were prepared using the Sn flux method. Two heating methods were used to prepare the single crystals: the slow heating and rapid heating methods. It was found that the single crystals grown using the slow heating method were not superconducting due to a significant loss of potassium. When the rapid heating method was used, the single crystals were observed to be superconducting with the desired potassium concentration. The energy dispersive X-ray spectroscopy analysis indicated the presence of multiple phases in the single crystals. Using single crystal X-ray diffraction, the crystal structure of the single crystals was found to be 14/mmm tetragonal at room temperature. The magnetic measurements on the single crystals indicated the presence of multiple phases and magnetic impurities.

Optical properties of organic superconductor K-(BETS)2FeBr4 /

/c-(BETS)2FeBr4 is the first antiferromagnetic organic superconductor with successive antiferromagnetic and superconducting transitions at Ta^=2.5K and Tc=l.lK respectively at ambient pressure. Polarized reflectance measurements were performed on three single crystalsamples of this material using a Briiker IFS66V/S Interferometer, and a Bolometer detector or an MCT detector, at seven temperatures between 4K and 300K, in both the far-infrared and mid-infrared frequency range. After the reflectance results were obtained, the Kramers-Kronig dispersion relation was apphed to determine the optical conductivity of /c-(BETS)2FeBr4 at these seven temperatures. Additionally, the optical conductivity spectra were fitted with a Drude/Lorentz Oscillator model in order to study the evolution of the optical conductivity with temperature along the a-axis and c-axis. The resistivities calculated from the Drude model parameters along the a-axis and c-axis agreed reasonably with previous transport measurements.

Optical properties of organic superconductor K-(BETS)2FeBr4 /

K-(BETS)2FeBr4 is a quasi-2D charge transfer organic metal with interesting electronic and magnetic properties. It undergoes a transition to an antiferromagnetic (AF) state at ambient pressure at the Neel temperature (T^^) = 2.5 K, as well as to a superconducting (SC) state at 1.1 K [1]. The temperature dependence of the electrical resistivity shows a small decrease at T;v indicating the resistivity drops as a result of the onset of the ordering of Fe'*''" spins. A sharp drop in the resistivity at 1.1 K is due to its superconducting transition. The temperature dependence of the susceptibility indicates an antiferromagnetic spin structure with the easy axis parallel to the a-axis. The specific heat at zero-field shows a large peak at about 2.4 K, which corresponds to the antiferromagnetic transition temperature (Tat) and no anomaly is observed around the superconducting transition temperature (1.1 K) demonstrating that the magnetically ordered state is not destroyed by the appearance of another phase transition (the superconducting transition) in the 7r-electron layers [1], [2]. This work presents an investigation of how the low frequency electromagnetic response is affected by the antiferromagnetic and superconducting states, as well as the onset of strong correlation. The location of the easy axis of three samples was determined and polarized thermal reflectance measurements of these «-(BETS)2FeBr4 samples oriented with their vertical axis along the a- and c axes were then carried out using a *He refrigerator cryostat and a Martin-Puplett type polarizing interferometer at various temperatures (T = 0.5 K, 1.4 K. 1.9 K, 2.8 K) above and below the superconducting state and/or antiferromagnetic state. Comparison of the SC state to the normal state along the o- and c-axes indicates a rising thermal reflectance at low frequencies (below 10 cm"' ) which may be a manifestation of the superconducting energy gap. A dip-Hke feature is detected at low frequencies (below 15 cm"') in the thermal reflectance plots which probe the antiferromagnetic state along the two axes, and may be due to the opening of a gap in the excitation spectrum as a result of the antiferromagnetism. In another set of experiments, thermal reflectance measurements carried out along the a- and c-axes at higher temperatures (10 K-80 K) show that the reflectivity decreases with increasing temperature to 60 K (the coherence temperature) above which it increases again. Comparison of the thermal reflectance plots along the a- and c-axes at higher temperatures reveals an anisotropy between these two axes. The Hagen-Rubens thermal reflectance plots corresponding to an average over the ac-plane were calculated using experimental hterature resistivity values. Comparison of the Hagen-Rubens plots with the experimental thermal reflectance along the a- and c-axes indicates that both exhibit the general trend of a decrease in thermal reflectance with increasing frequency, however the calculated Hagen-Rubens thermal reflectance at different temperatures is much lower than the experimental curves.

Electrical properties of some single crystal dodecaborides /|nby Jyoti Burte. -- 260 St. Catharines [Ont. : s. n.],

PreVi011.3 ':i or~ : indicat e('. tk~t ho t~)rE's sed ~-Al B 12 1i~2, ~' a semiconductor. r:Toreove r , the s i mpl.(~ electronic t heory also indi cates that ~ -AIB1 2 should be a semico nductor, since thf're is one nonbonding e 'Le ctrofl per AlB12- uni t. JPor these reasons, we decided to measure t he electrical n ropert i ~ s of ~ -AlB1 2 single crystal s . Singl e crystal s of¥- AIB 12 ab ou t 1 x 1 r1n1 . size were grown from a copper mel t at 12500 C. The melt technique coupled. 1,vi th slow cooling vilas used because of i ts advantages such as : siTYInle set- up of the expe rimon t ; only e ;l.sil y available c hemi cals are required and it i s a c omparatively strair::bt forvvard y,le t hod still yielding crystal s big enouGh for OtU' purpose . Copper rms used as a solvent , i nst8ad of previOl.wly used aluminum , because it allows c.l.'ystal growth at hig he r t emneratures. HovlGver, the cry s tals of ] -AlB12 shm'red very hi gh res i s t ance a t r oom temperature . From our neasureJ'lents we conclude that the r esistivity of j3- Al B12 is, at least, given as ~ = 4. x 107 oblD .em •• Those results are inc ons i s t ent wi 'uh the ones .. reported by IIiss Khin fo r bot- pressed j3-AlB12 g i ven a s = 7600 ohm . em . or I e s s . ' Since tbe hot pressing was done at about 800 - ' 9000C i n ~ rap hi te moul ds 1,7i th 97% AlB12- p oVJder, vie thi nk there is pas s ib i 1 i ty th a.t lower borides or borot] carbide are , being formed, ':.Jhich are k11 own to be good semiconductors . v7e tried to ro-pe r-AlB12 by addi'J,'?: agents s uch as l:Ig , IG.-InO 4. ' HgS04 , KI12PO 4·' etc. to t he melt .. However , all these re age 11 t eel either reduced the yield and size of t lJe crystals or r;ave crystals of high r esis'can ce again. We think tba t molten copper keeps t he i mpurities off . There is also a pos s i bil i ty t hc:!,t these doping agents get oxidi~::;ed at '1 250°C • Hence, we co ~ clud e that J -AIB12 has v~ ry high r es i stance at r oom temperature . This was a l s o C011 - fi rmed by checki ng the siYlgle and. polycrystals of .~-AIB12 from Norton Co., Ontario and Cooper Nletallurgical Association. Boron carbide has been reported to be a semiconductor with ~ - 0.3 to 0.8 ohm . cm. for hotpres sed s araples. Boron carbide b e inq: struct urally related to ¥-AIB12 , we de cided to study the electrical prone rties of it~ Single crystals. These crystals were cut from a Single melt grovvn crystal a t Norton Co., Ontario. The resistivity of th," se crystal s was measured by the Van der Pam-v' s ~ nethod, which \vas very c onvenient fo r our crystal sha-pp.s. Some of the crystals showed resistivity ~ == 0.50 ob,Tn.cr] . i n agreement with the previously reported results . However , a few crystals showed lower resistivity e.g . 0 .13 and 0.20 ohm.cra • • The Hall mobility could .not be measured and th8reiore i s lower than 0 .16 em 2 v - 1 sec -1 • This is in agreement \vith t he re1)orted Hall mobility for pyrolytic boron . _ 2 -1 -1 carbide as 0.13 cm v sec • We also studied the orientation of the boron carbide crystals by the Jjaue-method. The inclination of c-axis with res pect to x-ray be81Il was det ermined . This was found to be 100 t o 20° f or normal resistivity sarnples (0.5 ohm . cm.) and 27 - 30° for t he lower r esistivity samples (0.1 ~5 to 0.20 ohm.cm .). This indica tes the possibility that th.e r es if.1tivity of B13C3 i s orientation dependent.

Some electrical properties of semi-conductor crystals / |nPhyu Phyu Khin. -- 260 St. Catharines, Ont. : [s. n.],

SiC and AtB 12 have been prepared and their resistivities and Hall voltages measured. The resistivities and Hall voltages were measured by the Van der Pauw's method, using spring loaded tungsten contacts. In this method, the major requirement is to have samples of plane parallel surfaces of arbitrary shape with four small contacts at the circumference. Similar measurements were made with a number of SiC crystals obtained from the Norton Research Corporation (Canada)-Ltd., Carolina Aluminum Co., Exolon Co. and Carborundum Co. It was found that resistivity, carrier concentration and mobility of ions depend on the type of impurity. AtB 12 was prepared from the melt containing At and B in the ratio of 4:1. They formed amber-colour pseudo tetragonal crystals. As the crystals obtained were small for electrical measurements, hot pressed lumps have been used to measure their resistivity.

Magnetic and high pressure studies in the YPd5B3C3 system

The macroscopic properties of the superconducting phase in the multiphase compound YPd5B3 C.3 have been investigated. The onset of superconductivity was observed at 22.6 K, zero resistance at 21.2 K, the lower critical field Hel at 5 K was determined to be Hel (5) rv 310 Gauss and the compound was found to be an extreme type-II superconductor with the upper critical field in excess of 55000 Gauss at 15 K. From the upper and lower critical field values obtained, several important parameters of the superconducting state were determined at T = 15 K. The Ginzburg-Landau paramater was determined to be ~ > 9 corresponding to a coherence length ~ rv 80A and magnetic penetration depth of 800A. In addition measurements of the superconducting transition temperature Te(P) under purely hydrostatically applied pressure have been carried out. Te(P) of YPd5B3 C.3 decreases linearly with dTe/dP rv -8.814 X 10-5 J

Polytypism and Silicon carbide : a solid state nuclear magnetic resonance study

A survey of predominantly industrial silicon carbide has been carried out using Magic Angle Spinning nuclear magnetic resonance (MAS nmr); a solid state technique. Three silicon carbide polytypes were studied; 3C, 6H, and 15R. The 13C and 29 Si MAS nmr spectra of the bulk SiC sample was identified on the basis of silicon (carbon) site type in the d iff ere n t pol Y t Y pes • Out to 5.00 A fro mac en t r a lsi 1 i con (0 r carbon) atom four types of sites were characterized using symmetry based calculations. This method of polytype analysis was also considered, in the prelminary stages, for applications with other polytypic material; CdBr 2 , CdI 2 , and PbI 2 " In an attempt to understand the minor components of silicon carbide, such as its surface, some samples were hydrofluoric acid washed and heated to extreme temperatures. Basically, an HF removable species which absorbs at -110 ppm (Si0 2 ) in the 29 Si MAS nmr spectrum is found in silicon carbide after heating. Other unidentified peaks observed at short recycle delays in some 29 Si MAS nmr spectra are considered to be impurities that may be within the lattice. These components comprise less than 5% of the observable silicon. A Tl study was carried out for 29 Si nuclei in a 3C ii polytype sample, using the Driven Equilibrium Single-Pulse Observation of T1 (DESPOT) technique. It appears as though there are a number of nuclei that have the same chemical shift but different T1 relaxation times. The T1 values range from 30 seconds to 11 minutes. Caution has to be kept when interpreting these results because this is the first time that DESPOT has been used for solid samples and it is not likely in full working order. MAS nmr indicates that the 13C and 29 Si ~sotropic chemical shifts of silicon carbide appear to have a reciprocal type of relationship_ Single crystal nmr analysis of a 6H sample is accordance with this finding when only the resultant isotropic shift is considered. However, single crystal nmr also shows that the actual response of the silicon and carbon nuclear environment to the applied magnetic field at various angles is not at all reciprocal. Such results show that much more single crystal nmr work is required to determine the actual behavior of the local magnetic environment of the SiC nuclei.

The effects of moisture, cation concentration, temperature, density and composition of soils on their electrical resistivity

The effects. of moisture, cation concentration, dens ity , temper~ t ure and grai n si ze on the electrical resistivity of so il s are examined using laboratory prepared soils. An i nexpen si ve method for preparing soils of different compositions was developed by mixing various size fractions i n the laboratory. Moisture and cation c oncentration are related to soil resistivity by powe r functions, whereas soil resistiv ity and temperature, density, Yo gravel, sand , sil t, and clay are related by exponential functions . A total of 1066 cases (8528 data) from all the experiments were used in a step-wise multiple linear r egression to determine the effect of each variable on soil resistivity. Six variables out of the eight variables studied account for 92.57/. of the total variance in so il resistivity with a correlation coefficient of 0.96. The other two variables (silt and gravel) did not increase the · variance. Moisture content was found to be - the most important Yo clay. variable- affecting s oil res istivi ty followed by These two variables account for 90.81Yo of the total variance in soil resistivity with a correlation ~oefficient ·.of 0 . 95. Based on these results an equation to ' ~~ed{ ct soil r esist ivi ty using moisture and Yo clay is developed . To t est the predicted equation, resistivity measurements were made on natural soils both in s i tu a nd i n the laboratory. The data show that field and laboratory measurements are comparable. The predicted regression line c losely coinciqes with resistivity data from area A and area B soils ~clayey and silty~clayey sands). Resistivity data and the predicted regression line in the case of c layey soils (clays> 40%) do not coincide, especially a t l ess than 15% moisture. The regression equation overestimates the resistivity of so i l s from area C and underestimates for area D soils. Laboratory prepared high clay soils give similar trends. The deviations are probably caused by heterogeneous distribution of mo i sture and difference in the type o f cl ays present in these soils.

Calculation of the magnetic field penetration depth for high-Tc cuprate superconductors based on the Interlayer Pair Tunneling model /

In this work, the magnetic field penetration depth for high-Tc cuprate superconductors is calculated using a recent Interlayer Pair Tunneling (ILPT) model proposed by Chakravarty, Sudb0, Anderson, and Strong [1] to explain high temperature superconductivity. This model involves a "hopping" of Cooper pairs between layers of the unit cell which acts to amplify the pairing mechanism within the planes themselves. Recent work has shown that this model can account reasonably well for the isotope effect and the dependence of Tc on nonmagnetic in-plane impurities [2] , as well as the Knight shift curves [3] and the presence of a magnetic peak in the neutron scattering intensity [4]. In the latter case, Yin et al. emphasize that the pair tunneling must be the dominant pairing mechanism in the high-Tc cuprates in order to capture the features found in experiments. The goal of this work is to determine whether or not the ILPT model can account for the experimental observations of the magnetic field penetration depth in YBa2Cu307_a7. Calculations are performed in the weak and strong coupling limits, and the efi"ects of both small and large strengths of interlayer pair tunneling are investigated. Furthermore, as a follow up to the penetration depth calculations, both the neutron scattering intensity and the Knight shift are calculated within the ILPT formalism. The aim is to determine if the ILPT model can yield results consistent with experiments performed for these properties. The results for all three thermodynamic properties considered are not consistent with the notion that the interlayer pair tunneling must be the dominate pairing mechanism in these high-Tc cuprate superconductors. Instead, it is found that reasonable agreement with experiments is obtained for small strengths of pair tunneling, and that large pair tunneling yields results which do not resemble those of the experiments.

Far infrared reflectance and optical properties of organic superconductor (TMTSF)2ClO4 /

Polarized reflectance measurements of the quasi I-D charge-transfer salt (TMTSFh CI04 were carried out using a Martin-Puplett-type polarizing interferometer and a 3He refrigerator cryostat, at several temperatures between 0.45 K and 26 K, in the far infrared, in the 10 to 70 cm- 1 frequency range. Bis-tetramethyl-tetraselena-fulvalene perchlorate crystals, grown electrochemically and supplied by K. Behnia, of dimensions 2 to 4 by 0.4 by 0.2 mm, were assembled on a flat surface to form a mosaic of 1.5 by 3 mm. The needle shaped crystals were positioned parallel to each other along their long axis, which is the stacking direction of the planar TMTSF cations, exposing the ab plane face (parallel to which the sheets of CI04 anions are positioned). Reflectance measurements were performed with radiation polarized along the stacking direction in the sample. Measurements were carried out following either a fast (15-20 K per minute) or slow (0.1 K per minute) cooling of the sample. Slow cooling permits the anions to order near 24 K, and the sample is expected to be superconducting below 1.2 K, while fast cooling yields an insulating state at low temperatures. Upon the slow cooling the reflectance shows dependence with temperature and exhibits the 28 cm- 1 feature reported previously [1]. Thermoreflectance for both the 'slow' and 'fast' cooling of the sample calculated relative to the 26 K reflectance data indicates that the reflectance is temperature dependent, for the slow cooling case only. A low frequency edge in the absolute reflectance is assigned an electronic origin given its strong temperature dependence in the relaxed state. We attribute the peak in the absolute reflectance near 30 cm-1 to a phonon coupled to the electronic background. Both the low frequency edge and the 30 cm-1 feature are noted te shift towards higher frequcncy, upon cntering the superconducting state, by an amount of the order of the expected superconducting energy gap. Kramers-Kronig analysis was carried out to determine the optical conductivity for the slowly cooled sample from the measured reflectance. In order to do so the low frequency data was extrapolated to zero frequency using a Hagen-Ru bens behaviour, and the high frequency data was extended with the data of Cao et al. [2], and Kikuchi et al. [3]. The real part of the optical conductivity exhibits an asymmetric peak at 35 cm-1, and its background at lower frequencies seems to be losing spectral weight with lowering of the temperature, leading us to presume that a narrow peak is forming at even lower frequencies.

Electronic and magnetic properties of LaV1-xO3 /

A series of LaVi^xOs compounds (x=0.00, 0.02, 0.04, 0.06, 0.08) were prepeired using the standard solid reaction. The samples were chareicterized by X-ray diffraction (XRD), fourprobe resistivity, smd magnetic susceptibility studies. Powder X-ray diffraction analysis indicated the formation of a single-phase sample with a orthorhombic structure which was first found in GdFeOs (space group Pnma) . The Unit Cell program was used for calculating lattice peirameters from XFID data. The XRD spectnim could be indexed on a cubic lattice with Og = 2ap ~ (7.8578 to 7.9414 A). The lattice parameter was observed to increase as the Vanadium vacancy increased. Four-probe resistivity measurements exhibited semiconductor behavior for all sajnples from room temperature down to 19K. The resistivity of samples increased with increasing Vanadium vacancy. The resistivity of samples demonstrated activated conduction with an activation energy of approximately 0.2 eV. The activation energy increased with increasing lattice parameter. Field cool magnetic susceptibility measurements were performed with field of 500 G from 300 K to 5 K. These measurements indicated the presence of an antiferromagnetic transition at about 140 K. The data was fitted above Neel temperature to Ciurie-Weiss law yielding a negative parameignetic Curie temperature. This implies that antiferromagnetic ordering is present.

Crystal growth, Raman scattering and optical properties of the superconductor Cd2Re2O7(16O, 18O)/

Using the Physical Vapor Transport method, single crystals of Cd2Re207 have been grown, and crystals of dimensions up to 8x6x2 mm have been achieved. X-ray diffraction from a single crystal of Cd2Re207 has showed the crystal growth in the (111) plane. Powder X-ray diffraction measurements were performed on ^^O and ^^O samples, however no difference was observed. Assigning the space group Fd3m to Cd2Re207 at room temperature and using structure factor analysis, the powder X-ray diffraction pattern of the sample was explained through systematic reflection absences. The temperatiure dependence of the resistivity measurement of ^^O has revealed two structural phase transitions at 120 and 200 K, and the superconducting transition at 1.0 K. Using Factor Group Analysis on three different structiures of Cd2Re207, the number of IR and Raman active phonon modes close to the Brillouin zone centre have been determined and the results have been compared to the temperature-dependence of the Raman shifts of ^^O and ^*0 samples. After scaling (via removing Bose-Einstein and Rayleigh scattering factors from the scattered light) all spectra, each spectrum was fitted with a number of Lorentzian peaks. The temperature-dependence of the FWHM and Raman shift of mode Eg, shows the effects of the two structurjil phase transitions above Tc. The absolute reflectance of Cd2Re207 - '^O single crystals in the far-infrared spectral region (7-700 cm~^) has been measured in the superconducting state (0.5 K), right above the superconducting state (1.5 K), and in the normal state (4.2 K). Thermal reflectance of the sample at 0.5 K and 1.5 K indicates a strong absorption feature close to 10 cm~^ in the superconducting state with a reference temperature of 4.2 K. By means of Kramers-Kronig analysis, the absolute reflectance was used to calculate the optical conductivity and dielectric function. The real part of optical conductivity shows five distinct active phonon modes at 44, 200, 300, 375, and 575 cm~' at all temperatures including a Drude-like behavior at low frequencies. The imaginary part of the calculated dielectric function indicates a mode softening of the mode 44 cm~' below Tc.

Study on the properties of piezoelectric materials and manganese-based oxide perovskites /

Perovskite type piezoelectric and manganese oxide materials have gained a lot of attention in the field of device engineering. Lead zirconium titananium oxide (PbZri.iTiiOa or PZT) is a piezoelectric material widely used as sensors and actuators. Miniaturization of PZTbased devices will not only perfect many existing products, but also opens doors to new applications. Lanthanum manganese oxides Lai-iAiMnOa (A-divalent alkaline earth such as Sr, Ca or Ba) have been intensively studied for their colossal magnetoresistance (CMR) properties that make them applicable in memory cells, magnetic and pressure sensors. In this study, we fabricate PZT and LSMO(LCMO) heterostructures on SrTiOa substrates and investigate their temperature dependency of resistivity and magnetization as a function of the thickness of LSMO(LCMO) layer. The microstructure of the samples is analysed through TEM. In another set of samples, we study the effect of application of an electric field across the PZT layer that acts as an external pressure on the manganite layer. This verifies the correlation of lattice distortion with transport and magnetic properties of the CMR materials.

Properties of NaxCoO2 /

Polycrysttdline samples of NaiCoOa were prepared using the "Rapid heat-up" method. One set of samples was annealed in flowing O2, while the other set in flowing Argon. X-Ray diffraction measurements indicated a stable phase of Nao.7Co02 mixed with C03O4 for all the samples even though they differed in concentration of Na. Argon annealed samples were insulators, whereas the ones annealed in O2 were metallic. Most of the measurements were performed on the sample Nao.7Co02, because it is the host compound for the superconductor sample Nao.35Co02-H20. Magnetization measurement showed that the magnetic moment decreased with increasing sodium concentration. This is due to the existence of C03O4 in samples with Na^ 0.7. As sodium concentration decreases, the magnetic moment increases due to the increasing concentration of C03O4 and its large magnetic moment. Magnetization measurements showed that the magnetic moment of Nao.7Co02 is field-dependent in low fields eind field-independent in fields higher than 100 G. Resistivity changes with temperature (dp/dT) increased with increasing Na concentration. Also resistivity measurements were performed under different hydrostatic pressures on Nao.7Co02. Two transitions were observed; one at a temperature Ti ~20 K and the other at T2 ^280 K, the transition at Ti has a magnetic origin and the one at T2 is a structiural transition. It was noticed that pressure aJfects resistivity of the sample. At higher pressures resistivity changes faster with temperature. Magnetoresistance measurement showed a small change in the resistivity, especially at lower temperatures. A novel layered superconductor Nao.35Co02H20 was prepared using de-intercalation of Na from the host compound Nao.7Co02. FVom the temperature dependence of the magnetization, the superconducting transition temperature and lower critictil field have been estimated as Tc=4.12 K and Hci=66 G, respectively.

Far-infrared optical properties of the heavy fermion superconductor UB[E13]

Temperature dependent resistivity, p, magnetic susceptibility, X, and far-infrared reflectance measurements were made on the low Tc superconductor UBe13. Two variants of UBe13 have been proposed, named 'L'- (for low Tc ) and 'H'-type (for high Tc ). Low temperature resistivity measurements confirmed that our sample was of H-type and that the transition temperature was at 0.9 K. This was further confirmed with the observation of this transition in the AC-susceptibility. Low temperature reflectance measurements showed a decrease in the reflectivity as the temperature is lowered from 300 to 10 K, which is in qualitative agreement with the increasing resistivity in this temperature range as temperature is lowered. No dramatic change in the reflectivity was observed between 10 and 0.75 K. A further decrease of the reflectance was observed for the temperature of 0.5 K. The calculated optical conductivity shows a broad minimum near 80 cm-1 below 45 K. Above 45 K the conductivity is relatively featureless. As the temperature is lowered, the optical conductivity decreases. The frequency dependent scattering rate was found to be flat for temperatures between 300 and 45 K. The development of a peak, at around 70 cm-1 was found for temperatures of 45 K and below. This peak has been associated with the energy at which the transition to a coherent state occurs from single impurity scattering in other heavy fermion systems. The frequency dependent mass enhancement coefficient was found to increase at low frequencies as the frequency decreases. Its' magnitude as frequency approaches zero also increased as the temperature decreased.