Crystal growth, Raman scattering and optical properties of the superconductor Cd2Re2O7(16O, 18O)/

Using the Physical Vapor Transport method, single crystals of Cd2Re207 have been grown, and crystals of dimensions up to 8x6x2 mm have been achieved. X-ray diffraction from a single crystal of Cd2Re207 has showed the crystal growth in the (111) plane. Powder X-ray diffraction measurements were performed on ^^O and ^^O samples, however no difference was observed. Assigning the space group Fd3m to Cd2Re207 at room temperature and using structure factor analysis, the powder X-ray diffraction pattern of the sample was explained through systematic reflection absences. The temperatiure dependence of the resistivity measurement of ^^O has revealed two structural phase transitions at 120 and 200 K, and the superconducting transition at 1.0 K. Using Factor Group Analysis on three different structiures of Cd2Re207, the number of IR and Raman active phonon modes close to the Brillouin zone centre have been determined and the results have been compared to the temperature-dependence of the Raman shifts of ^^O and ^*0 samples. After scaling (via removing Bose-Einstein and Rayleigh scattering factors from the scattered light) all spectra, each spectrum was fitted with a number of Lorentzian peaks. The temperature-dependence of the FWHM and Raman shift of mode Eg, shows the effects of the two structurjil phase transitions above Tc. The absolute reflectance of Cd2Re207 - '^O single crystals in the far-infrared spectral region (7-700 cm~^) has been measured in the superconducting state (0.5 K), right above the superconducting state (1.5 K), and in the normal state (4.2 K). Thermal reflectance of the sample at 0.5 K and 1.5 K indicates a strong absorption feature close to 10 cm~^ in the superconducting state with a reference temperature of 4.2 K. By means of Kramers-Kronig analysis, the absolute reflectance was used to calculate the optical conductivity and dielectric function. The real part of optical conductivity shows five distinct active phonon modes at 44, 200, 300, 375, and 575 cm~' at all temperatures including a Drude-like behavior at low frequencies. The imaginary part of the calculated dielectric function indicates a mode softening of the mode 44 cm~' below Tc.

Specific heat of UPdâ Siâ

The specific heat of single-crystal U Pd2 Si2 has been studied using both the step heating and continious heating methods for the temperature range 2 to 250 K. Successive phase transitions at Tl = 136I< and T2 = 108I< are reported, which are consistent with current publications. The transition at 40K, which was previously reported, has not been detected. Recent published elastic neutron scattering data, magnetic susceptibility and resistivity results suggest that U Pd2 Si2 may be a heavy fermion compound, however, the electronic specific heat coefficient I (= 18.97 ;~), obtained from the specific heat Cv measurements, is smaller than that of the conventional heavy fermion system. The Debye temperature of U Pd2Si2 is found to be 116.55K. The possibility is discussed that the maximum in CIT in the low-temperature range 2 to 4K corresponds to Schottky anomaly induced by localized magnetic impurities .

The Effects of Annealing URu2Si2 on the Resistivity and Meissner Effect

The enigmatic heavy fermion URu2Si2, which is the subject of this thesis, has attracted intensive theoretical and experimental research since 1984 when it was firstly reported by Schlabitz et al. at a conference [1]. The previous bulk property measurements clearly showed that one second order phase transition occurs at the Hidden Order temperature THO ≈ 17.5 K and another second order phase transition, the superconducting transition, occurs at Tc ≈ 1 K. Though twenty eight years have passed, the mechanisms behind these two phase transitions are still not clear to researchers. Perfect crystals do not exist. Different kinds of crystal defects can have considerable effects on the crystalline properties. Some of these defects can be eliminated, and hence the crystalline quality improved, by annealing. Previous publications showed that some bulk properties of URu2Si2 exhibited significant differences between as-grown samples and annealed samples. The present study shows that the annealing of URu2Si2 has some considerable effects on the resistivity and the DC magnetization. The effects of annealing on the resistivity are characterized by examining how the Residual Resistivity Ratio (RRR), the fitting parameters to an expression for the temperature dependence of the resistivity, the temperatures of the local maximum and local minimum of the resistivity at the Hidden Order phase transition and the Hidden Order Transition Width ∆THO change after annealing. The plots of one key fitting parameter, the onset temperature of the Hidden Order transition and ∆THO vs RRR are compared with those of Matsuda et al. [2]. Different media used to mount samples have some impact on how effectively the samples are cooled because the media have different thermal conductivity. The DC magnetization around the superconducting transition is presented for one unannealed sample under fields of 25 Oe and 50 Oe and one annealed sample under fields of 0 Oe and 25 Oe. The DC field dependent magnetization of the annealed Sample1-1 shows a typical field dependence of a Type-II superconductor. The lower critical field Hc1 is relatively high, which may be due to flux pinning by the crystal defects.