Infrared spectroscopy of Mg-doped SrRuO3 thin films /

The reflectance of thin films of magnesium doped SrRu03(Mg-SR0) produced by pulsed laser deposition on SrTiOa (100) substrates has been measured at room temperature between 100 and 7500 cm~^. The films were chosen to have wide range of thickness, stoichiometry and electrical properties. As the films were very thin (less than 300 nm), and some were insulating the reflectance data shows structures due to both the film and the substrate. Hence, the data was analyzed using Kramers-Kronig constrained variational fitting (VDF) method to extract the real optical conductivity of the Mg-SRO films. Although the VDF technique is flexible enough to fit all features of the reflectance spectra, it seems that VDF could not eliminate the substrate's contribution from fllm conductivity results. Also the comparison of the two different programs implementing VDF fltting shows that this technique has a uniqueness problem. The optical properties are discussed in light of the measured structural and transport properties of the fllms which vary with preparation conditions and can be correlated with differences in stoichiometry. This investigation was aimed at checking the VDF technique and also getting answer to the question whether Mg^"*" substitutes in to Ru or Sr site. Analysis of our data suggests that Mg^+ goes to Ru site.

Composition analysis of high-Tc superconducting thin films by quantitative x-ray fluorescence

A method is presented for determining the composition of thin films containing the elements Bi, Sr, Br, Cu, and Ca. Quantitative x-ray fluorescence (XRF) consisting of radioactive sources (secondary foil excitor 241Am-Mo source and 55Pe source), a Si(Li) detector, and a multichannel analyzer were employed. The XRF system was calibrated by using sol gel thin films of known element composition and also by sputtered thin films analyzed by the conventional Rutherford Back Scattering (RBS). The XRF system has been used to assist and optimize the sputter target composition required to produce high-Tc BiSrCaCuO films with the desired metal composition.

Preparation of SrMgx-Ru1-xO3 thin films by pulsed laser deposition /

SrMg^Rui-iOa thin films were made by using pulsed laser deposition on SrTiOa (100) substrates in either O2 or Ar atmosphere. The thin films were characterized by x-ray diffraction, energy dispersive x-ray microanalysis, dc resistivity measurement, and dc magnetization measurement. The effect of Mg doping was observed. As soon as the amount of Mg increased in SrMg-cRui-iOa thin films, the magnetization decreased, and the resistivity increased. It had little effect on the Curie temperature (transition temperature). The magnetization states of SrMgiRui-iOa thin films, for x < 0.15, are similar to SrRuOs films. X-ray diffraction results for SrMga-Rui-iOa thin films made in oxygen showed that the films are epitaxial. The thin films could not be well made in Ar atmosphere during laser ablation as there was no clear peak of SrMg^Rui-iOa in x-ray diffraction results. Substrate temperatures had an effect on the resistivity of the films. The residual resistivity ratios were increased by increasing substrate temperature. It was observed that the thickness of thin films are another factor for film quality: Thin films were epitaxial, but thicker films were not epitaxial.

The Influence of Sex on the Relationship Between Arterial Mechanical Properties and Cardiovagal Baroreflex Sensitivity

Cardiovagal baroreflex sensitivity (cvBRS) demonstrates a strong relationship with arterial mechanical properties. Both cvBRS and arterial mechanics differ by sex such that males demonstrate greater cvBRS, yet lower large artery elasticity than females. Whether the relationship between cvBRS and arterial mechanics is similar in males and females remains unexamined. As a result, it is unclear whether arterial mechanics contribute to sex differences in cvBRS. This study investigated the cross-sectional relationship between cvBRS and arterial mechanical properties of the common carotid, carotid sinus and aortic arch (AA) in 36 (18 females) young, healthy normotensives. The cvBRS-arterial mechanics relationship did not reach statistical significance and did not differ by sex. Both cvBRS and AA distensibility were greater in females than males. Sex differences in cvBRS were eliminated after controlling for AA distensibility. These findings suggest that in this sample, AA elasticity may contribute to the greater cvBRS in females than males.