Properties of NaxCoO2 /

Polycrysttdline samples of NaiCoOa were prepared using the "Rapid heat-up" method. One set of samples was annealed in flowing O2, while the other set in flowing Argon. X-Ray diffraction measurements indicated a stable phase of Nao.7Co02 mixed with C03O4 for all the samples even though they differed in concentration of Na. Argon annealed samples were insulators, whereas the ones annealed in O2 were metallic. Most of the measurements were performed on the sample Nao.7Co02, because it is the host compound for the superconductor sample Nao.35Co02-H20. Magnetization measurement showed that the magnetic moment decreased with increasing sodium concentration. This is due to the existence of C03O4 in samples with Na^ 0.7. As sodium concentration decreases, the magnetic moment increases due to the increasing concentration of C03O4 and its large magnetic moment. Magnetization measurements showed that the magnetic moment of Nao.7Co02 is field-dependent in low fields eind field-independent in fields higher than 100 G. Resistivity changes with temperature (dp/dT) increased with increasing Na concentration. Also resistivity measurements were performed under different hydrostatic pressures on Nao.7Co02. Two transitions were observed; one at a temperature Ti ~20 K and the other at T2 ^280 K, the transition at Ti has a magnetic origin and the one at T2 is a structiural transition. It was noticed that pressure aJfects resistivity of the sample. At higher pressures resistivity changes faster with temperature. Magnetoresistance measurement showed a small change in the resistivity, especially at lower temperatures. A novel layered superconductor Nao.35Co02H20 was prepared using de-intercalation of Na from the host compound Nao.7Co02. FVom the temperature dependence of the magnetization, the superconducting transition temperature and lower critictil field have been estimated as Tc=4.12 K and Hci=66 G, respectively.

Study on the properties of piezoelectric materials and manganese-based oxide perovskites /

Perovskite type piezoelectric and manganese oxide materials have gained a lot of attention in the field of device engineering. Lead zirconium titananium oxide (PbZri.iTiiOa or PZT) is a piezoelectric material widely used as sensors and actuators. Miniaturization of PZTbased devices will not only perfect many existing products, but also opens doors to new applications. Lanthanum manganese oxides Lai-iAiMnOa (A-divalent alkaline earth such as Sr, Ca or Ba) have been intensively studied for their colossal magnetoresistance (CMR) properties that make them applicable in memory cells, magnetic and pressure sensors. In this study, we fabricate PZT and LSMO(LCMO) heterostructures on SrTiOa substrates and investigate their temperature dependency of resistivity and magnetization as a function of the thickness of LSMO(LCMO) layer. The microstructure of the samples is analysed through TEM. In another set of samples, we study the effect of application of an electric field across the PZT layer that acts as an external pressure on the manganite layer. This verifies the correlation of lattice distortion with transport and magnetic properties of the CMR materials.

Thermodynamic properties and Debye-Waller factor of fee materials

We have calculated the equation of state and the various thermodynamic properties of monatomic fcc crystals by minimizing the Helmholtz free energy derived in the high temperature limit for the quasiharmonic theory, QH, and the lowest-order (cubic and quartic), 'A2, anharmonic terms of the perturbation theory, PT. The total energy in each case is obtained by adding the static energy. The calculation of the thermal properties was carried out for a nearest-neighbour central-force model of the fcc lattice by means of the appropriate thermodynamic relations. We have calculated the lattice constant, the thermal expansion, the coefficient of volume expansion, the specific heat at constant volume and at constant pressure, the isothermal and adiabatic bulk moduli, and the Griineisen parameter, for the rare-gas solids Kr and Xe, and gold. Morse potential and modified Morse potential were each used to represent the atomic interaction for the three fcc materials. For most of the calculated thermodynamic properties from the QH theory, the results for Kr and Xe with the modified Morse potential show an improvement over the results for the Morse potential when compared with the experimental data. However, the results of the 'A 2 equation of state with the modified Morse potential are in good agreement with experiment only in the case of the specific heat at constant volume and at constant pressure. For Au we have calculated the lattice contribution from the QH and 'A 2 PT and the electronic contribution to the thermal properties. The electronic contribution was taken into account by using the free electron model. The results of the thermodynamic properties calculated with the modified Morse potential were similar to those obtained with the Morse potential. U sing the minimized equation of state we also calculated the Mossbauer recoilless fraction for Kr and Xe and the Debye-Waller factor (DWF) for Pb, AI, eu, Ag, and Au. The Mossbauer recoilless fraction was obtained for the above two potentials and Lennard-Jones potential. The L-J potential gives the best agreement with experiment for Kr. No experimental data exists for Xe. At low temperature the calculated DWF results for Pb, AI, and eu show a good agreement with experimental values, but at high temperature the experimental DWF results increase very rapidly. For Ag the computed values were below the expected results at all temperatures. The DWF results of the modified Morse potential for Pb, AI, eu and Ag were slightly better than those of the Morse potential. In the case of Au the calculated values were in poor agreement with experimental results. We have calculated the quasiharmonic phonon dispersion curves for Kr, Xe, eu, Ag, and Au. The calculated and experimental results of the frequencies agree quite well for all the materials except for Au where the longitudinal modes show serious discrepancies with the experimental results. In addition, the two lowest-order anharmonic contributions to the phonon frequency were derived using the Green's function method. The A 2 phonon dispersion curves have been calculated only for eu, and the results were similar to those of the QH dispersion curves. Finally, an expression for the Griineisen parameter "( has been derived from the anharmonic frequencies, and calculated for these materials. The "( results are comparable with those obtained from the thermodynamic definition.